Preparation method of ceramic glaze
The invention discloses a preparation method of a ceramic glaze. The preparation method comprises the following steps: step 1, preparing the ceramic glaze from the following raw materials: 60 parts of calcite, 15 parts of zinc oxide, 2 parts of aluminum oxide, 10 parts of barium carbonate, 20 parts of kaolin and 12 parts of albite; the raw materials are crushed and mixed; step 2, adding deionized water into the crushed mixture, wherein the ratio of the mixture to the deionized water is 1: 4; 3, after the mixture and the deionized water are fully mixed, stirring is conducted; and step 4, pouring into a ball mill, carrying out ball milling for 10-20 minutes, pouring out, and sieving.
本发明公开了一种陶瓷釉料制备方法，包括以下步骤：步骤一，陶瓷釉料包括以下原料：60份方解石、15份氧化锌、2份氧化铝、10份碳酸钡、20份高岭土和12份钠长石；将以上原料粉碎后混合；步骤二，将粉碎后的混合物加入去离子水，混合物与去离子水的比例为1：4；步骤三，待混合物与去离子水充分混合后进行搅拌；步骤四，倒入球磨机进行10‑20min球磨，倒出后过筛。
Preparation method of ceramic glaze
The invention discloses a preparation method of a ceramic glaze. The preparation method comprises the following steps: step 1, preparing the ceramic glaze from the following raw materials: 60 parts of calcite, 15 parts of zinc oxide, 2 parts of aluminum oxide, 10 parts of barium carbonate, 20 parts of kaolin and 12 parts of albite; the raw materials are crushed and mixed; step 2, adding deionized water into the crushed mixture, wherein the ratio of the mixture to the deionized water is 1: 4; 3, after the mixture and the deionized water are fully mixed, stirring is conducted; and step 4, pouring into a ball mill, carrying out ball milling for 10-20 minutes, pouring out, and sieving.
本发明公开了一种陶瓷釉料制备方法，包括以下步骤：步骤一，陶瓷釉料包括以下原料：60份方解石、15份氧化锌、2份氧化铝、10份碳酸钡、20份高岭土和12份钠长石；将以上原料粉碎后混合；步骤二，将粉碎后的混合物加入去离子水，混合物与去离子水的比例为1：4；步骤三，待混合物与去离子水充分混合后进行搅拌；步骤四，倒入球磨机进行10‑20min球磨，倒出后过筛。
Preparation method of ceramic glaze
一种陶瓷釉料制备方法
ZHANG LINYUE (author) / CAI XILAI (author)
2023-03-21
Patent
Electronic Resource
Chinese
| European Patent Office | 2022
| European Patent Office | 2024
Ceramic glaze prepared from waste concrete powder and preparation method of ceramic glaze
| European Patent Office | 2015