Medium-temperature colored glaze, medium-temperature colored glaze ceramic product and preparation method of medium-temperature colored glaze ceramic product
The invention discloses medium-temperature colored glaze, a medium-temperature colored glaze ceramic product and a preparation method of the medium-temperature colored glaze ceramic product. The medium-temperature colored glaze comprises basic glaze slip and reflective glaze slip which are sequentially applied to the surface of a ceramic body from inside to outside. The basic glaze slip comprises the following components in parts by weight: 15-20 parts of quartz, 5-8 parts of potassium feldspar, 5-8 parts of albite, 2-5 parts of calcium oxide, 5-8 parts of celsian, 12-15 parts of kaolin, 6-10 parts of borax, 3-6 parts of sodium silicate and 2-4 parts of zinc sulfate. The reflective glaze slip comprises the following components in parts by weight: 15-20 parts of quartz, 5-8 parts of aluminum oxide, 6-9 parts of titanium dioxide, 5-8 parts of zirconium oxide, 12-15 parts of kaolin, 6-10 parts of borax, 3-6 parts of sodium silicate and 2-4 parts of zinc sulfate. According to the medium-temperature colored glaze, the medium-temperature colored glaze ceramic product and the preparation method of the medium-temperature colored glaze ceramic product, the method is simple and high in efficiency, and the prepared ceramic is high in wear resistance and glossiness.
本发明公开了一种中温色釉、中温色釉陶瓷制品及其制备方法，所述中温色釉包括用于由内到外依次施加在陶瓷坯体表面的基础釉浆和反光釉浆。基础釉浆包括以下重量份的组分：石英15‑20份，钾长石5‑8份，钠长石5‑8份，氧化钙2‑5份，钡长石5‑8份，高岭土12‑15份，硼砂6‑10份，硅酸钠3‑6份和硫酸锌2‑4份。反光釉浆包括以下重量份的组分：石英15‑20份，氧化铝5‑8份，二氧化钛6‑9份，氧化锆5‑8份，高岭土12‑15份，硼砂6‑10份，硅酸钠3‑6份和硫酸锌2‑4份。本发明的中温色釉、中温色釉陶瓷制品及其制备方法，其方法简单、效率高，制得的陶瓷耐磨性高，光泽度高。
Medium-temperature colored glaze, medium-temperature colored glaze ceramic product and preparation method of medium-temperature colored glaze ceramic product
The invention discloses medium-temperature colored glaze, a medium-temperature colored glaze ceramic product and a preparation method of the medium-temperature colored glaze ceramic product. The medium-temperature colored glaze comprises basic glaze slip and reflective glaze slip which are sequentially applied to the surface of a ceramic body from inside to outside. The basic glaze slip comprises the following components in parts by weight: 15-20 parts of quartz, 5-8 parts of potassium feldspar, 5-8 parts of albite, 2-5 parts of calcium oxide, 5-8 parts of celsian, 12-15 parts of kaolin, 6-10 parts of borax, 3-6 parts of sodium silicate and 2-4 parts of zinc sulfate. The reflective glaze slip comprises the following components in parts by weight: 15-20 parts of quartz, 5-8 parts of aluminum oxide, 6-9 parts of titanium dioxide, 5-8 parts of zirconium oxide, 12-15 parts of kaolin, 6-10 parts of borax, 3-6 parts of sodium silicate and 2-4 parts of zinc sulfate. According to the medium-temperature colored glaze, the medium-temperature colored glaze ceramic product and the preparation method of the medium-temperature colored glaze ceramic product, the method is simple and high in efficiency, and the prepared ceramic is high in wear resistance and glossiness.
本发明公开了一种中温色釉、中温色釉陶瓷制品及其制备方法，所述中温色釉包括用于由内到外依次施加在陶瓷坯体表面的基础釉浆和反光釉浆。基础釉浆包括以下重量份的组分：石英15‑20份，钾长石5‑8份，钠长石5‑8份，氧化钙2‑5份，钡长石5‑8份，高岭土12‑15份，硼砂6‑10份，硅酸钠3‑6份和硫酸锌2‑4份。反光釉浆包括以下重量份的组分：石英15‑20份，氧化铝5‑8份，二氧化钛6‑9份，氧化锆5‑8份，高岭土12‑15份，硼砂6‑10份，硅酸钠3‑6份和硫酸锌2‑4份。本发明的中温色釉、中温色釉陶瓷制品及其制备方法，其方法简单、效率高，制得的陶瓷耐磨性高，光泽度高。
Medium-temperature colored glaze, medium-temperature colored glaze ceramic product and preparation method of medium-temperature colored glaze ceramic product
一种中温色釉、中温色釉陶瓷制品及其制备方法
LIN JIANHUA (author) / HUANG QIAOYING (author) / LIN CHENLU (author)
2023-04-18
Patent
Electronic Resource
Chinese
Glaze used for medium-temperature ceramic product and ceramic preparation method applying glaze