Stone damage repair construction method
The invention provides a stone damage repairing construction method. Comprising the following steps that 1, the stone surface and stone damage gaps are cleaned; 2, broken stone in the broken stone is taken and ground into powder; 3, a damage repairing material is prepared, and stone powder, epoxy resin and a curing agent are blended into a colloidal repairing material; step 4, pressing the colloidal repair material into the gap by using a batch knife or a scraper; 5, the strength of the repaired stone is gradually enhanced after the gelatinous repairing material is hardened; and 6, after the strength of the stone damage repairing material is proper, the filled gap and the periphery are polished. According to the stone damage repairing method, epoxy resin is adopted as a main component, and a stone damage repairing material with a curing agent mixed in the epoxy resin is used for solving the technical problems of repairing strength, color similarity, shrinkage depression and attractive effect in the stone crack and damage repairing process.
本发明提供一种石材破损修复施工方法。包括以下步骤，步骤1、清洁石材表面和石材破损缝隙处；步骤2、取破损石材中碎石研磨成粉；步骤3、制备破损修复材料，石材粉末和环氧树脂、固化剂调和成胶状修复材料；步骤4、使用批刀或刮刀将胶状修复材料按压到缝隙中；步骤5、修补后的石材，等待胶状修补材料硬化，强度逐渐增强；步骤6、等石材破损修补材料强度合适后，将填充好的缝隙及周围进行打磨。在石材破损修复方法中，采用环氧树脂为主成分，在环氧树脂中混合固化剂的一种石材破损修复材料，用以解决石材裂缝及破损的修补过程中修补强度、颜色相似度、收缩凹陷、美观效果的技术问题。
Stone damage repair construction method
The invention provides a stone damage repairing construction method. Comprising the following steps that 1, the stone surface and stone damage gaps are cleaned; 2, broken stone in the broken stone is taken and ground into powder; 3, a damage repairing material is prepared, and stone powder, epoxy resin and a curing agent are blended into a colloidal repairing material; step 4, pressing the colloidal repair material into the gap by using a batch knife or a scraper; 5, the strength of the repaired stone is gradually enhanced after the gelatinous repairing material is hardened; and 6, after the strength of the stone damage repairing material is proper, the filled gap and the periphery are polished. According to the stone damage repairing method, epoxy resin is adopted as a main component, and a stone damage repairing material with a curing agent mixed in the epoxy resin is used for solving the technical problems of repairing strength, color similarity, shrinkage depression and attractive effect in the stone crack and damage repairing process.
本发明提供一种石材破损修复施工方法。包括以下步骤，步骤1、清洁石材表面和石材破损缝隙处；步骤2、取破损石材中碎石研磨成粉；步骤3、制备破损修复材料，石材粉末和环氧树脂、固化剂调和成胶状修复材料；步骤4、使用批刀或刮刀将胶状修复材料按压到缝隙中；步骤5、修补后的石材，等待胶状修补材料硬化，强度逐渐增强；步骤6、等石材破损修补材料强度合适后，将填充好的缝隙及周围进行打磨。在石材破损修复方法中，采用环氧树脂为主成分，在环氧树脂中混合固化剂的一种石材破损修复材料，用以解决石材裂缝及破损的修补过程中修补强度、颜色相似度、收缩凹陷、美观效果的技术问题。
Stone damage repair construction method
一种石材破损修复施工方法
HE ZHILI (author) / NING LIYAN (author) / CHEN YONGCHANG (author) / ZHANG SHENG (author) / SHAO XIANGYU (author) / WU QIFEI (author) / CHEN JIANYONG (author) / GUO YAOLONG (author) / MA CHI (author) / CHEN CHANGYUAN (author)
2024-01-30
Patent
Electronic Resource
Chinese
| European Patent Office | 2015
British Library Online Contents | 2002