Rapid soil curing agent and preparation method thereof
The invention discloses a rapid soil curing agent and a preparation method thereof. The rapid soil curing agent comprises a slag mixture, an alkali activator, a surfactant, anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite, modified rosin resin and cement clinker. The cement comprises the following components in percentage by mass: 20-30% of a slag mixture, 2-4% of an alkali activator, 1-3% of a surfactant, 5-10% of anhydrite, 5-10% of glycerol, 6-12% of sodium sulfate, 3-9% of aluminum sulfate, 6-12% of fluorite, 3-5% of modified rosin resin and the balance of cement clinker, the preparation method comprises the following steps: firstly, putting anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite and modified rosin resin into a stirrer, and uniformly stirring and mixing; the invention has the following beneficial effects: by using the slag mixture, raw materials can be saved, and the natural environment can be protected; by adding anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite, modified rosin resin and cement clinker, the strength of the solidified soil can be further improved, and the anti-permeability and anti-freezing performance can be improved.
本发明公开了一种土壤快速固化剂以及制备方法，包括矿渣混合物、碱性激发剂、表面活性剂、硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂、水泥熟料，其组份按质量百分比计为：矿渣混合物20‑30％、碱性激发剂2‑4％、表面活性剂1‑3％、硬石膏5‑10％、丙三醇5‑10％、硫酸钠6‑12％、硫酸铝3‑9％、氟石6‑12％、改型松香树脂3‑5％、余量为水泥熟料；所述制备方法如下：先将硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂置于搅拌器内，搅拌混合均匀；本发明的有益效果是：矿渣混合物的使用，有助于节约原材料，保护自然环境；硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂、水泥熟料的加入有助于进一步提高所固化的土壤强度，还有助于提高抗渗、抗冻性能。
Rapid soil curing agent and preparation method thereof
The invention discloses a rapid soil curing agent and a preparation method thereof. The rapid soil curing agent comprises a slag mixture, an alkali activator, a surfactant, anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite, modified rosin resin and cement clinker. The cement comprises the following components in percentage by mass: 20-30% of a slag mixture, 2-4% of an alkali activator, 1-3% of a surfactant, 5-10% of anhydrite, 5-10% of glycerol, 6-12% of sodium sulfate, 3-9% of aluminum sulfate, 6-12% of fluorite, 3-5% of modified rosin resin and the balance of cement clinker, the preparation method comprises the following steps: firstly, putting anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite and modified rosin resin into a stirrer, and uniformly stirring and mixing; the invention has the following beneficial effects: by using the slag mixture, raw materials can be saved, and the natural environment can be protected; by adding anhydrite, glycerol, sodium sulfate, aluminum sulfate, fluorite, modified rosin resin and cement clinker, the strength of the solidified soil can be further improved, and the anti-permeability and anti-freezing performance can be improved.
本发明公开了一种土壤快速固化剂以及制备方法，包括矿渣混合物、碱性激发剂、表面活性剂、硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂、水泥熟料，其组份按质量百分比计为：矿渣混合物20‑30％、碱性激发剂2‑4％、表面活性剂1‑3％、硬石膏5‑10％、丙三醇5‑10％、硫酸钠6‑12％、硫酸铝3‑9％、氟石6‑12％、改型松香树脂3‑5％、余量为水泥熟料；所述制备方法如下：先将硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂置于搅拌器内，搅拌混合均匀；本发明的有益效果是：矿渣混合物的使用，有助于节约原材料，保护自然环境；硬石膏、丙三醇、硫酸钠、硫酸铝、氟石、改型松香树脂、水泥熟料的加入有助于进一步提高所固化的土壤强度，还有助于提高抗渗、抗冻性能。
Rapid soil curing agent and preparation method thereof
一种土壤快速固化剂以及制备方法
JIAN ENLAI (author)
2024-02-09
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2024
High-humic-acid soil curing agent and preparation method thereof
| European Patent Office | 2021
Desulfurization ash-based soil curing agent and preparation method thereof
| European Patent Office | 2022
Curing agent for fluid stabilized soil and preparation method of curing agent
| European Patent Office | 2024
Modularization-building-foundation-soil rapid chemical curing agent and application thereof
| European Patent Office | 2016