Preparation method of inorganic stone with granite-like patterns
The invention discloses a preparation method of inorganic stone with granite-like patterns, which comprises the following steps: adding 330-340 parts by mass of white crystal sand, 95-105 parts by mass of white cement, 8-12 parts by mass of metakaolin, 600-700 parts by mass of calcium powder, 0.1-0.2 part by mass of water-retaining agent, 6-8 parts by mass of modified polycarboxylate superplasticizer, 8-12 parts by mass of styrene-butadiene emulsion, 20-25 parts by mass of water and 0.5-2 parts by mass of inorganic pigment into a stirrer, and uniformly stirring to obtain a mixed material; adding the mixed material into a disc machine, uniformly mixing, crushing, and adding into an air seal machine to obtain a pre-product; and uniformly dispersing the pre-product into a mold, demolding, maintaining for 25-30 days, sawing, polishing, processing and detecting to obtain the inorganic stone with the granite-like patterns, the modified polycarboxylate superplasticizer is prepared from the following raw materials: diethyl allyloxy silane and carbon nanofibers. The inorganic stone with the granite-like patterns obtained through the preparation method is high in bending strength, high in compressive strength and high in falling ball impact strength, and the dot-shaped patterns are clear, remarkable and stable in effect.
本发明公开了一种花纹类似花岗岩状无机石的制备方法，其包括以下步骤：按质量份，将330～340份白晶砂、95～105份白水泥、8～12份偏高领土、600～700份钙粉、0.1～0.2份保水剂、6～8份改性聚羧酸减水剂、8～12份丁苯乳液、20～25份水、0.5～2份无机颜料加入搅拌机中，搅拌均匀，得到混合物料；将所述混合物料加入圆盘机中，混料均匀，破碎后加入关风器，得到预产物；将所述预产物均匀分散到模具内后脱模，然后养护25～30天，然后进行锯切、抛光、加工和检测，得到所述花纹类似花岗岩状无机石；所述改性聚羧酸减水剂的制备原料包括二乙基烯丙氧基硅烷和碳纳米纤维。本发明提供的制备方法得到的花纹类似花岗岩状无机石抗弯强度高、抗压强度大、落球冲击强度高，且点状花纹效果清晰显著和稳定。
Preparation method of inorganic stone with granite-like patterns
The invention discloses a preparation method of inorganic stone with granite-like patterns, which comprises the following steps: adding 330-340 parts by mass of white crystal sand, 95-105 parts by mass of white cement, 8-12 parts by mass of metakaolin, 600-700 parts by mass of calcium powder, 0.1-0.2 part by mass of water-retaining agent, 6-8 parts by mass of modified polycarboxylate superplasticizer, 8-12 parts by mass of styrene-butadiene emulsion, 20-25 parts by mass of water and 0.5-2 parts by mass of inorganic pigment into a stirrer, and uniformly stirring to obtain a mixed material; adding the mixed material into a disc machine, uniformly mixing, crushing, and adding into an air seal machine to obtain a pre-product; and uniformly dispersing the pre-product into a mold, demolding, maintaining for 25-30 days, sawing, polishing, processing and detecting to obtain the inorganic stone with the granite-like patterns, the modified polycarboxylate superplasticizer is prepared from the following raw materials: diethyl allyloxy silane and carbon nanofibers. The inorganic stone with the granite-like patterns obtained through the preparation method is high in bending strength, high in compressive strength and high in falling ball impact strength, and the dot-shaped patterns are clear, remarkable and stable in effect.
本发明公开了一种花纹类似花岗岩状无机石的制备方法，其包括以下步骤：按质量份，将330～340份白晶砂、95～105份白水泥、8～12份偏高领土、600～700份钙粉、0.1～0.2份保水剂、6～8份改性聚羧酸减水剂、8～12份丁苯乳液、20～25份水、0.5～2份无机颜料加入搅拌机中，搅拌均匀，得到混合物料；将所述混合物料加入圆盘机中，混料均匀，破碎后加入关风器，得到预产物；将所述预产物均匀分散到模具内后脱模，然后养护25～30天，然后进行锯切、抛光、加工和检测，得到所述花纹类似花岗岩状无机石；所述改性聚羧酸减水剂的制备原料包括二乙基烯丙氧基硅烷和碳纳米纤维。本发明提供的制备方法得到的花纹类似花岗岩状无机石抗弯强度高、抗压强度大、落球冲击强度高，且点状花纹效果清晰显著和稳定。
Preparation method of inorganic stone with granite-like patterns
一种花纹类似花岗岩状无机石的制备方法
FENG WEIRONG (author) / YANG DEZHI (author) / HUANG JINMING (author)
2024-03-01
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| Wiley | 2008
Preparation method of inorganic external stone-like coating
| European Patent Office | 2021
Granite stone powder mortar and preparation method thereof
| European Patent Office | 2024
Concrete based on granite stone powder and preparation method thereof
| European Patent Office | 2022