High-gloss, high-transparency and high-whiteness jade porcelain thin-body glaze and preparation method thereof
The invention relates to the technical field of glaze, and particularly discloses jade porcelain thin-body high-gloss high-transparency high-whiteness glaze which comprises the following raw materials in parts by weight: 45-55% of feldspar, 15-25% of quartz, 5-15% of modified calcined talc, 5-15% of calcite, 4-8% of zinc oxide, 5-10% of Suzhou clay, 3-10% of modified hydroxyapatite and 5-15% of barium carbonate. According to the invention, the jade porcelain product with high transparency, high whiteness and high glossiness can be prepared according to process control and firing temperature and atmosphere requirements; the glaze is suitable for a high-whiteness green body and is also suitable for a common green body, and the glossiness of a glaze surface is very high; the glaze material is prepared by a special process of modifying calcined talc and modified hydroxyapatite, and the calcined talc and the hydroxyapatite are blended and matched, so that the transparency, the glossiness and the whiteness of the product can be harmoniously improved, and the use efficiency of the product is optimized.
本发明涉及釉料技术领域，具体公开了玉瓷薄胎高光泽高透明高白度釉料，包括以下重量份原料：长石45～55％，石英15～25％，改性烧滑石5～15％，方解石5～15％，氧化锌4～8％，苏州土5～10％，改性羟基磷灰石3～10％，碳酸钡5～15％。本发明按照工艺控制及其烧成温度，气氛要求，可制成高透明、高白度、高光泽度的玉瓷制品；本研究釉料适用于高白度坯体，也适用于一般坯体，釉面光泽度很高；在釉料配制中通过改性烧滑石、改性羟基磷灰石的特殊工艺制成，采用二者调和协配，能够使产品的透明度、光泽度、白度协调改进，优化产品的使用效率。
High-gloss, high-transparency and high-whiteness jade porcelain thin-body glaze and preparation method thereof
The invention relates to the technical field of glaze, and particularly discloses jade porcelain thin-body high-gloss high-transparency high-whiteness glaze which comprises the following raw materials in parts by weight: 45-55% of feldspar, 15-25% of quartz, 5-15% of modified calcined talc, 5-15% of calcite, 4-8% of zinc oxide, 5-10% of Suzhou clay, 3-10% of modified hydroxyapatite and 5-15% of barium carbonate. According to the invention, the jade porcelain product with high transparency, high whiteness and high glossiness can be prepared according to process control and firing temperature and atmosphere requirements; the glaze is suitable for a high-whiteness green body and is also suitable for a common green body, and the glossiness of a glaze surface is very high; the glaze material is prepared by a special process of modifying calcined talc and modified hydroxyapatite, and the calcined talc and the hydroxyapatite are blended and matched, so that the transparency, the glossiness and the whiteness of the product can be harmoniously improved, and the use efficiency of the product is optimized.
本发明涉及釉料技术领域，具体公开了玉瓷薄胎高光泽高透明高白度釉料，包括以下重量份原料：长石45～55％，石英15～25％，改性烧滑石5～15％，方解石5～15％，氧化锌4～8％，苏州土5～10％，改性羟基磷灰石3～10％，碳酸钡5～15％。本发明按照工艺控制及其烧成温度，气氛要求，可制成高透明、高白度、高光泽度的玉瓷制品；本研究釉料适用于高白度坯体，也适用于一般坯体，釉面光泽度很高；在釉料配制中通过改性烧滑石、改性羟基磷灰石的特殊工艺制成，采用二者调和协配，能够使产品的透明度、光泽度、白度协调改进，优化产品的使用效率。
High-gloss, high-transparency and high-whiteness jade porcelain thin-body glaze and preparation method thereof
玉瓷薄胎高光泽高透明高白度釉料及其制备方法
ZHANG MENGYA (author) / SHI ZHANJIE (author)
2024-03-15
Patent
Electronic Resource
Chinese
| European Patent Office | 2024
| European Patent Office | 2022
Preparation method of jade glaze daily porcelain with high thermal stability and high strength
| European Patent Office | 2020
High-gloss domestic ceramic glaze and preparation method thereof
| European Patent Office | 2020
Eggshell glaze, high-whiteness glazed tile and preparation method thereof
| European Patent Office | 2024