Cosmetic ceramic massage head formula and preparation process thereof
The invention discloses a cosmetic ceramic massage head formula and a preparation process thereof, the cosmetic ceramic massage head formula is prepared from the following raw materials in parts by weight: 92.6% of aluminum oxide fine powder, 1.4% of fused quartz powder, 1.9% of kaolin, 2.6% of calcium carbonate and 1.5% of graphene, and the preparation process comprises the following specific steps: preparing ceramic slurry; injecting into a mold to prepare a blank, correcting the blank, blow-drying, and respectively putting into a low-temperature furnace, a degreasing furnace and a high-temperature furnace to finish preparation; after vibration polishing, soaking and cleaning to obtain a finished product; according to the cosmetic ceramic massage head formula and the preparation process thereof, the cosmetic ceramic massage head is high in impact strength and good in anti-tearing effect, by the adoption of the preparation process, serious deformation along with temperature changes and bursting in the high-temperature sintering process are not prone to occurring in the preparation process, and therefore the stability and plumpness of a product are effectively improved, and the service life of the product is prolonged. The surface strength and the abrasive resistance of the product are improved, so that the service life of the cosmetic ceramic massage head is prolonged.
本发明公开了一种化妆品陶瓷按摩头配方及其制备工艺，包括如下重量份数原料：三氧化二铝细粉92.6%、熔融石英粉1.4%、高岭土1.9%、碳酸钙2.6%以及石墨烯1.5%，其具体步骤包括如下：制成陶瓷泥浆；注入模具中制成毛坯、修正毛坯后吹干、分别置入低温炉、脱脂炉以及高温炉完成制备；震荡抛光后浸泡清洗制得成品；该一种化妆品陶瓷按摩头配方及其制备工艺，其抗冲击强度高，抗撕裂效果好，且采用上述制备工艺，其制备过程中不容易随着温度高低的变化产生严重的形变以及高温烧结过程中炸裂，从而有效地提升产品的导稳性能以及产品的饱满度，提升产品表面强度以及耐磨强度，以此提升该化妆品陶瓷按摩头的使用寿命。
Cosmetic ceramic massage head formula and preparation process thereof
The invention discloses a cosmetic ceramic massage head formula and a preparation process thereof, the cosmetic ceramic massage head formula is prepared from the following raw materials in parts by weight: 92.6% of aluminum oxide fine powder, 1.4% of fused quartz powder, 1.9% of kaolin, 2.6% of calcium carbonate and 1.5% of graphene, and the preparation process comprises the following specific steps: preparing ceramic slurry; injecting into a mold to prepare a blank, correcting the blank, blow-drying, and respectively putting into a low-temperature furnace, a degreasing furnace and a high-temperature furnace to finish preparation; after vibration polishing, soaking and cleaning to obtain a finished product; according to the cosmetic ceramic massage head formula and the preparation process thereof, the cosmetic ceramic massage head is high in impact strength and good in anti-tearing effect, by the adoption of the preparation process, serious deformation along with temperature changes and bursting in the high-temperature sintering process are not prone to occurring in the preparation process, and therefore the stability and plumpness of a product are effectively improved, and the service life of the product is prolonged. The surface strength and the abrasive resistance of the product are improved, so that the service life of the cosmetic ceramic massage head is prolonged.
本发明公开了一种化妆品陶瓷按摩头配方及其制备工艺，包括如下重量份数原料：三氧化二铝细粉92.6%、熔融石英粉1.4%、高岭土1.9%、碳酸钙2.6%以及石墨烯1.5%，其具体步骤包括如下：制成陶瓷泥浆；注入模具中制成毛坯、修正毛坯后吹干、分别置入低温炉、脱脂炉以及高温炉完成制备；震荡抛光后浸泡清洗制得成品；该一种化妆品陶瓷按摩头配方及其制备工艺，其抗冲击强度高，抗撕裂效果好，且采用上述制备工艺，其制备过程中不容易随着温度高低的变化产生严重的形变以及高温烧结过程中炸裂，从而有效地提升产品的导稳性能以及产品的饱满度，提升产品表面强度以及耐磨强度，以此提升该化妆品陶瓷按摩头的使用寿命。
Cosmetic ceramic massage head formula and preparation process thereof
一种化妆品陶瓷按摩头配方及其制备工艺
CAI GUOXIANG (author)
2024-04-30
Patent
Electronic Resource
Chinese
| European Patent Office | 2022