Metal flash glazed tile and preparation method thereof
The invention discloses a metal flashing glazed tile and a preparation method thereof. The preparation method comprises the following steps: A, preparing a green body layer; b, applying ground coat on the surface of the green body layer to obtain a ground coat layer; the ground glaze is prepared from the following raw materials in parts by mass: 6 to 10 parts of kaolin, 2 to 8 parts of aluminum oxide, 35 to 42 parts of nepheline, 2 to 10 parts of albite, 18 to 25 parts of calcium strontium barium frit and 18 to 22 parts of zirconium silicate; c, applying metal flash glaze to the surface of the ground glaze layer to obtain a metal flash glaze layer; and D, after drying, firing in a kiln to obtain the metal flashing glazed tile. According to the metal glittering glazed tile and the preparation method thereof, the formula structures of the ground glaze layer and the metal glittering glaze layer in the glazed tile are matched with each other, so that a strong metal glittering effect can be shown on the surface of the glazed tile; the technical problems that the metal texture of flashing spots is not strong, the distribution of the flashing spots is not uniform and not fine and the like in the existing flashing glaze can be effectively solved.
本发明公开了一种金属闪光釉面砖及其制备方法，包括以下步骤：A、准备坯体层；B、将底釉布施于所述坯体层的表面，得到底釉层；按照质量份数，所述底釉包括以下原料：高岭土6～10份、氧化铝2～8份、霞石35～42份、钠长石2～10份、钙锶钡熔块18～25份和硅酸锆18～22份；C、将金属闪光釉布施于所述底釉层的表面，得到金属闪光釉层；D、烘干后入窑烧制，得到金属闪光釉面砖。本方案提出的一种金属闪光釉面砖及其制备方法，釉面砖中底釉层和金属闪光釉层的配方结构相互匹配，有利于在瓷砖表面呈现出强烈的金属闪光效果，能有效解决现有闪光釉存在的闪光点金属质感不强、闪光点分布不均匀且不细腻等的技术问题。
Metal flash glazed tile and preparation method thereof
The invention discloses a metal flashing glazed tile and a preparation method thereof. The preparation method comprises the following steps: A, preparing a green body layer; b, applying ground coat on the surface of the green body layer to obtain a ground coat layer; the ground glaze is prepared from the following raw materials in parts by mass: 6 to 10 parts of kaolin, 2 to 8 parts of aluminum oxide, 35 to 42 parts of nepheline, 2 to 10 parts of albite, 18 to 25 parts of calcium strontium barium frit and 18 to 22 parts of zirconium silicate; c, applying metal flash glaze to the surface of the ground glaze layer to obtain a metal flash glaze layer; and D, after drying, firing in a kiln to obtain the metal flashing glazed tile. According to the metal glittering glazed tile and the preparation method thereof, the formula structures of the ground glaze layer and the metal glittering glaze layer in the glazed tile are matched with each other, so that a strong metal glittering effect can be shown on the surface of the glazed tile; the technical problems that the metal texture of flashing spots is not strong, the distribution of the flashing spots is not uniform and not fine and the like in the existing flashing glaze can be effectively solved.
本发明公开了一种金属闪光釉面砖及其制备方法，包括以下步骤：A、准备坯体层；B、将底釉布施于所述坯体层的表面，得到底釉层；按照质量份数，所述底釉包括以下原料：高岭土6～10份、氧化铝2～8份、霞石35～42份、钠长石2～10份、钙锶钡熔块18～25份和硅酸锆18～22份；C、将金属闪光釉布施于所述底釉层的表面，得到金属闪光釉层；D、烘干后入窑烧制，得到金属闪光釉面砖。本方案提出的一种金属闪光釉面砖及其制备方法，釉面砖中底釉层和金属闪光釉层的配方结构相互匹配，有利于在瓷砖表面呈现出强烈的金属闪光效果，能有效解决现有闪光釉存在的闪光点金属质感不强、闪光点分布不均匀且不细腻等的技术问题。
Metal flash glazed tile and preparation method thereof
一种金属闪光釉面砖及其制备方法
LUO QIANG (author) / ZHONG BAOMIN (author) / LI FENG (author) / GU WENCAN (author) / XIONG XUNWANG (author) / XU YU (author) / YANG XIAN (author) / YANG YUTAO (author) / ZHA WUHUA (author) / LI SUBO (author)
2024-05-14
Patent
Electronic Resource
Chinese
Metal decorative glazed marble tile and preparation method thereof
| European Patent Office | 2022
| European Patent Office | 2023