Preparation method of nano purple gold glaze
The invention belongs to the technical field of porcelain glaze, and particularly relates to a preparation method of nano purple gold glaze, which comprises the following steps: (1) preparing glaze: mixing silver oxide, zinc oxide, silicon oxide, aluminum oxide, calcium oxide, potassium oxide and copper oxide in proportion, adding water and a dispersing agent, and uniformly stirring to form uniform slurry; (2) glaze coating: coating the slurry on the surface of a ceramic body by spraying, dipping or brushing to form a uniform glaze layer with the thickness of 0.1-0.2 mm; (3) firing the glaze: putting the ceramic green body coated with the glaze into a high-temperature furnace, and firing, so that the glaze is molten and is combined with the green body to form purple gold glaze; according to the method, the ceramic glaze with purple golden luster can be prepared by utilizing the nanoscale oxide and a digital control system, the quality and the stability of the glaze are improved, the firing temperature and the energy consumption are reduced, and the color and the glossiness of the glaze are increased.
本发明属于瓷釉技术领域，具体涉及一种纳米紫金釉的制作方法，包括包括以下步骤：(1)配制釉料：将氧化银、氧化锌、氧化硅、氧化铝、氧化钙、氧化钾、氧化铜按比例混合，并加入水和分散剂，搅拌均匀，形成均匀的浆料；(2)涂覆釉料：将浆料通过喷涂或浸渍或刷涂涂覆在陶瓷坯体的表面，形成一层均匀的釉层，厚度为0.1‑0.2㎜；(3)烧制釉料：将涂覆釉料的陶瓷坯体放入高温炉中，进行烧制，使釉料熔融并与坯体结合，形成紫金釉；该方法能够利用纳米级氧化物和数字控制系统制作出具有紫金色光泽的陶瓷釉料，提高釉料的质量和稳定性，降低烧制温度和能耗，增加釉料的色彩和光泽度。
Preparation method of nano purple gold glaze
The invention belongs to the technical field of porcelain glaze, and particularly relates to a preparation method of nano purple gold glaze, which comprises the following steps: (1) preparing glaze: mixing silver oxide, zinc oxide, silicon oxide, aluminum oxide, calcium oxide, potassium oxide and copper oxide in proportion, adding water and a dispersing agent, and uniformly stirring to form uniform slurry; (2) glaze coating: coating the slurry on the surface of a ceramic body by spraying, dipping or brushing to form a uniform glaze layer with the thickness of 0.1-0.2 mm; (3) firing the glaze: putting the ceramic green body coated with the glaze into a high-temperature furnace, and firing, so that the glaze is molten and is combined with the green body to form purple gold glaze; according to the method, the ceramic glaze with purple golden luster can be prepared by utilizing the nanoscale oxide and a digital control system, the quality and the stability of the glaze are improved, the firing temperature and the energy consumption are reduced, and the color and the glossiness of the glaze are increased.
本发明属于瓷釉技术领域，具体涉及一种纳米紫金釉的制作方法，包括包括以下步骤：(1)配制釉料：将氧化银、氧化锌、氧化硅、氧化铝、氧化钙、氧化钾、氧化铜按比例混合，并加入水和分散剂，搅拌均匀，形成均匀的浆料；(2)涂覆釉料：将浆料通过喷涂或浸渍或刷涂涂覆在陶瓷坯体的表面，形成一层均匀的釉层，厚度为0.1‑0.2㎜；(3)烧制釉料：将涂覆釉料的陶瓷坯体放入高温炉中，进行烧制，使釉料熔融并与坯体结合，形成紫金釉；该方法能够利用纳米级氧化物和数字控制系统制作出具有紫金色光泽的陶瓷釉料，提高釉料的质量和稳定性，降低烧制温度和能耗，增加釉料的色彩和光泽度。
Preparation method of nano purple gold glaze
一种纳米紫金釉的制作方法
LI LIANGDONG (author)
2024-05-28
Patent
Electronic Resource
Chinese
Ru-kiln purple gold glaze and preparation method thereof
| European Patent Office | 2024
Purple blue glaze for manufacturing Jun pottery and preparation method of purple blue glaze
| European Patent Office | 2021
Preparation method and application of purple-bronze ceramic art glaze
| European Patent Office | 2015
Preparation method of high-hardness gem-like diamond purple-light glaze
| European Patent Office | 2020