Unfired pouring corundum spinel sliding plate brick and preparation method thereof
The invention relates to a sliding plate unfired cast corundum spinel sliding plate brick and a preparation method thereof, and the sliding plate unfired cast corundum spinel sliding plate brick comprises the following components by weight: 50%-80% of sintered corundum, 5%-25% of magnesium aluminate spinel, 8%-11% of fused corundum, 3%-5% of fused spinel, 5%-10% of activated alumina micro powder, and 5%-10% of pure calcium aluminate cement. According to the preparation method, the finished product is prepared through the steps of weighing, mixing and forming, and the finished product is prepared from the following components in percentage by weight: 1-3% of a medium-temperature sintering agent, 1-3% of a polycarboxylate superplasticizer and 0.05-0.15% of explosion-proof fibers. According to the invention, the components of the product are mainly adjusted, the preparation period of the product is shortened and adjusted, the preparation process is reduced, green production without firing and oil immersion is realized, and the requirements of low-carbon and environment-friendly modern production are met.
本发明涉及一种滑板不烧浇注刚玉尖晶石质滑板砖及其制备方法，其中不烧浇注刚玉尖晶石质滑板砖，包括以下重量百分比的组分：烧结刚玉50％～80％、镁铝尖晶石5％～25％、电熔刚玉8％～11％、电熔尖晶石3％～5％、活性氧化铝微粉5％～10％、纯铝酸钙水泥5％～10％，中温烧结剂1％～3％、聚羧酸减水剂1％～3％、防爆纤维0.05％～0.15％，另外制备方法中，通过称量、混合和成型步骤制备该成品。本发明主要是对产品组分进行调整，同时缩短和调整了产品制备周期，减少制备工序，无烧成、无油浸的绿色化生产，符合低碳环保的现代化生产需求。
Unfired pouring corundum spinel sliding plate brick and preparation method thereof
The invention relates to a sliding plate unfired cast corundum spinel sliding plate brick and a preparation method thereof, and the sliding plate unfired cast corundum spinel sliding plate brick comprises the following components by weight: 50%-80% of sintered corundum, 5%-25% of magnesium aluminate spinel, 8%-11% of fused corundum, 3%-5% of fused spinel, 5%-10% of activated alumina micro powder, and 5%-10% of pure calcium aluminate cement. According to the preparation method, the finished product is prepared through the steps of weighing, mixing and forming, and the finished product is prepared from the following components in percentage by weight: 1-3% of a medium-temperature sintering agent, 1-3% of a polycarboxylate superplasticizer and 0.05-0.15% of explosion-proof fibers. According to the invention, the components of the product are mainly adjusted, the preparation period of the product is shortened and adjusted, the preparation process is reduced, green production without firing and oil immersion is realized, and the requirements of low-carbon and environment-friendly modern production are met.
本发明涉及一种滑板不烧浇注刚玉尖晶石质滑板砖及其制备方法，其中不烧浇注刚玉尖晶石质滑板砖，包括以下重量百分比的组分：烧结刚玉50％～80％、镁铝尖晶石5％～25％、电熔刚玉8％～11％、电熔尖晶石3％～5％、活性氧化铝微粉5％～10％、纯铝酸钙水泥5％～10％，中温烧结剂1％～3％、聚羧酸减水剂1％～3％、防爆纤维0.05％～0.15％，另外制备方法中，通过称量、混合和成型步骤制备该成品。本发明主要是对产品组分进行调整，同时缩短和调整了产品制备周期，减少制备工序，无烧成、无油浸的绿色化生产，符合低碳环保的现代化生产需求。
Unfired pouring corundum spinel sliding plate brick and preparation method thereof
一种不烧浇注刚玉尖晶石质滑板砖及其制备方法
LI YUZHANG (author) / LI HAOWEI (author) / LI WEIJIE (author) / XIAO QINGHAI (author)
2024-08-23
Patent
Electronic Resource
Chinese
Unfired magnesia-alumina spinel brick and preparation process thereof
| European Patent Office | 2023
Ternary composite self-repairing unfired sliding plate brick and preparation method thereof
| European Patent Office | 2022
Low-thermal-conductivity unfired magnesia-alumina spinel brick and preparation method thereof
| European Patent Office | 2024
UNFIRED BRICK REFRACTORY AND METHOD FOR PRODUCING UNFIRED BRICK REFRACTORY
| European Patent Office | 2018
Magnesium-spinel sliding plate brick and preparation method thereof
| European Patent Office | 2020