The invention discloses a preparation method of a foamed ceramic plate with insert decoration, which comprises the following steps: step 1, preparation of base material components: preparing the following base materials in parts by weight: 30-50 parts of tantalum-niobium tailings, 30-50 parts of lithium tailings, 5-10 parts of ceramic waste residue, 1-5 parts of magnesia soil, 2.5-5 parts of kaolin, 5-10 parts of potassium feldspar powder, 0.1-2 parts of silicon carbide and 0.3-1 part of tripolyphosphate; mixing by adopting a ball milling mode, and controlling the fineness of the combined materials and the raw materials to be 0.5-2% of 250-mesh screen residues; the method not only has the characteristics of low cost and high efficiency, but also has a unique product appearance effect and a good application prospect, and meets the requirements of the market on the appearance effect of stone products; the particles and the foamed ceramic are added to form a composite material for toughening, so that the crack propagation resistance of the foamed ceramic is improved, the brittleness and breakage rate of the foamed ceramic are reduced, and the breakage phenomenon of the foamed ceramic in the use process is improved.
本发明公开了一种具有镶嵌物装饰的发泡陶瓷板制备方法，包括以下步骤：步骤一：基料组分准备，按重量份数准备以下基料：钽铌尾矿30‑50份、锂尾矿30‑50份、陶瓷废渣5‑10份、镁质土1‑5份、高岭土2.5‑5份、钾长石粉5‑10份、碳化硅0.1‑2份、三聚磷酸盐0.3‑1份；采用球磨方式混合，将组合物料及原料细度制备控制至250目筛余0.5‑2％；本发明不仅具有低成本、高效率的特点，而且产品外观效果独特，具有良好的应用前景，满足了市场对于石材制品外观效果的需求；通过添加颗粒物与发泡陶瓷形成复合材料进行增韧，提高发泡陶瓷对裂纹扩展的抗力，降低发泡陶瓷的脆性和破损率，改善发泡陶瓷在使用过程中破损的现象。
Preparation method of foamed ceramic plate with insert decoration
The invention discloses a preparation method of a foamed ceramic plate with insert decoration, which comprises the following steps: step 1, preparation of base material components: preparing the following base materials in parts by weight: 30-50 parts of tantalum-niobium tailings, 30-50 parts of lithium tailings, 5-10 parts of ceramic waste residue, 1-5 parts of magnesia soil, 2.5-5 parts of kaolin, 5-10 parts of potassium feldspar powder, 0.1-2 parts of silicon carbide and 0.3-1 part of tripolyphosphate; mixing by adopting a ball milling mode, and controlling the fineness of the combined materials and the raw materials to be 0.5-2% of 250-mesh screen residues; the method not only has the characteristics of low cost and high efficiency, but also has a unique product appearance effect and a good application prospect, and meets the requirements of the market on the appearance effect of stone products; the particles and the foamed ceramic are added to form a composite material for toughening, so that the crack propagation resistance of the foamed ceramic is improved, the brittleness and breakage rate of the foamed ceramic are reduced, and the breakage phenomenon of the foamed ceramic in the use process is improved.
本发明公开了一种具有镶嵌物装饰的发泡陶瓷板制备方法，包括以下步骤：步骤一：基料组分准备，按重量份数准备以下基料：钽铌尾矿30‑50份、锂尾矿30‑50份、陶瓷废渣5‑10份、镁质土1‑5份、高岭土2.5‑5份、钾长石粉5‑10份、碳化硅0.1‑2份、三聚磷酸盐0.3‑1份；采用球磨方式混合，将组合物料及原料细度制备控制至250目筛余0.5‑2％；本发明不仅具有低成本、高效率的特点，而且产品外观效果独特，具有良好的应用前景，满足了市场对于石材制品外观效果的需求；通过添加颗粒物与发泡陶瓷形成复合材料进行增韧，提高发泡陶瓷对裂纹扩展的抗力，降低发泡陶瓷的脆性和破损率，改善发泡陶瓷在使用过程中破损的现象。
Preparation method of foamed ceramic plate with insert decoration
一种具有镶嵌物装饰的发泡陶瓷板制备方法
PENG YEQING (author) / HU XIAOQIANG (author) / ZHOU HUA (author) / SUN YAN (author)
2024-10-11
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Preparation method of Yellow River sediment foamed ceramic insulation board with glaze decoration
| European Patent Office | 2021
| European Patent Office | 2020