Ceramic raw material iron red glaze and preparation method thereof
The invention provides a ceramic raw material iron red glaze and a preparation method thereof, and belongs to the technical field of inorganic material preparation. The raw material of the ceramic raw material iron red glaze comprises the following components in parts by weight: 15.5-17.5 parts of potassium feldspar, 22.5-23.5 parts of albite, 7-8 parts of white kaolin in the Panxi region, 14-18 parts of quartz, 6-7 parts of calcite, 10-12 parts of calcined talc, 10-12 parts of bone meal and 14-16 parts of vanadium titano-magnetite. The bone meal is prepared from the following components in percentage by mass: 0.85 percent to 2.35 percent of SiO2, 0.36 percent to 0.74 percent of Al2O3, 44.56 percent to 46.75 percent of CaO, 0.76 percent to 1.50 percent of MgO, 0.03 percent to 0.12 percent of K2O, 0.53 percent to 0.86 percent of Na2O, 0.12 percent to 0.14 percent of Fe2O3, 0.03 percent to 0.05 percent of TiO2, 36.76 percent to 48.79 percent of P2O5 and the balance of inevitable impurities. The iron red glaze provided by the invention is bright and flexible in glaze color and rich in change, yellow filiform flow lines are also inserted into flakes of fire red, and the iron red glaze is bright and colorful, so that the whole utensil has the treasure, noble and solemn texture, is mainly used for tea ceremony utensils such as tea bowls and cups, and can also be used for life utensils such as bowls, dishes, toys and inkstones.
本发明提供了一种陶瓷生料铁红釉及其制备方法，属于无机材料制备技术领域。该陶瓷生料铁红釉，其原料包括以下重量份的组分：钾长石15.5～17.5份，钠长石22.5～23.5份，攀西地区白色高岭土7～8份，石英14～18份，方解石6～7份，烧滑石10～12份，骨粉10～12份，钒钛磁铁矿14～16份；所述骨粉按照质量百分比包括：SiO2:0.85～2.35％、Al2O3:0.36～0.74％、CaO:44.56～46.75％、MgO:0.76～1.50％、K2O:0.03～0.12％、Na2O:0.53～0.86％、Fe2O3:0.12～0.14％、TiO2:0.03～0.05％、P2O5:36.76～48.79％，余量为不可避免的杂质。本发明提供的铁红釉釉色鲜艳灵动，富于变化，成片的火红色中还穿插黄色的丝状流纹，绚丽多彩，使整个器皿具有珍奇、高贵和庄重的质感，主要用于茶碗、杯等茶道用具，同时也可用于钵、盘子、玩具、砚等生活用具。
Ceramic raw material iron red glaze and preparation method thereof
The invention provides a ceramic raw material iron red glaze and a preparation method thereof, and belongs to the technical field of inorganic material preparation. The raw material of the ceramic raw material iron red glaze comprises the following components in parts by weight: 15.5-17.5 parts of potassium feldspar, 22.5-23.5 parts of albite, 7-8 parts of white kaolin in the Panxi region, 14-18 parts of quartz, 6-7 parts of calcite, 10-12 parts of calcined talc, 10-12 parts of bone meal and 14-16 parts of vanadium titano-magnetite. The bone meal is prepared from the following components in percentage by mass: 0.85 percent to 2.35 percent of SiO2, 0.36 percent to 0.74 percent of Al2O3, 44.56 percent to 46.75 percent of CaO, 0.76 percent to 1.50 percent of MgO, 0.03 percent to 0.12 percent of K2O, 0.53 percent to 0.86 percent of Na2O, 0.12 percent to 0.14 percent of Fe2O3, 0.03 percent to 0.05 percent of TiO2, 36.76 percent to 48.79 percent of P2O5 and the balance of inevitable impurities. The iron red glaze provided by the invention is bright and flexible in glaze color and rich in change, yellow filiform flow lines are also inserted into flakes of fire red, and the iron red glaze is bright and colorful, so that the whole utensil has the treasure, noble and solemn texture, is mainly used for tea ceremony utensils such as tea bowls and cups, and can also be used for life utensils such as bowls, dishes, toys and inkstones.
本发明提供了一种陶瓷生料铁红釉及其制备方法，属于无机材料制备技术领域。该陶瓷生料铁红釉，其原料包括以下重量份的组分：钾长石15.5～17.5份，钠长石22.5～23.5份，攀西地区白色高岭土7～8份，石英14～18份，方解石6～7份，烧滑石10～12份，骨粉10～12份，钒钛磁铁矿14～16份；所述骨粉按照质量百分比包括：SiO2:0.85～2.35％、Al2O3:0.36～0.74％、CaO:44.56～46.75％、MgO:0.76～1.50％、K2O:0.03～0.12％、Na2O:0.53～0.86％、Fe2O3:0.12～0.14％、TiO2:0.03～0.05％、P2O5:36.76～48.79％，余量为不可避免的杂质。本发明提供的铁红釉釉色鲜艳灵动，富于变化，成片的火红色中还穿插黄色的丝状流纹，绚丽多彩，使整个器皿具有珍奇、高贵和庄重的质感，主要用于茶碗、杯等茶道用具，同时也可用于钵、盘子、玩具、砚等生活用具。
Ceramic raw material iron red glaze and preparation method thereof
陶瓷生料铁红釉及其制备方法
CHEN DONGLI (author) / WU LIAOXING (author) / MA HONGQIANG (author)
2024-10-15
Patent
Electronic Resource
Chinese
Ceramic metal glaze material and preparation method thereof
| European Patent Office | 2016
Ceramic iron glaze material as well as preparation method and application thereof
| European Patent Office | 2015
Ceramic tile glaze raw material and preparation method thereof
| European Patent Office | 2021
| European Patent Office | 2022
Glaze material of jade glaze, ceramic tile and preparation method of ceramic tile
| European Patent Office | 2023