MOLDED POROUS ARTICLE, METHOD FOR PRODUCTION THEREOF, CATALYST CARRIER, AND CATALYST
The present invention aims at providing a porous molded product comprising magnesium and aluminum which is satisfactory in both of a specific surface area and mechanical properties, can be suitably used as filters, drying agents, adsorbents, purifying agents, deodorants, carriers for catalysts, etc., includes a large amount of micropores, and has a large specific surface area and a high strength, as well as a process for producing the porous molded product. The porous molded product of the present invention comprises at least magnesium and aluminum, and having a magnesium content of 10 to 50% by weight in terms of a magnesium atom, an aluminum content of 5 to 35% by weight in terms of an aluminum atom, a pore volume of 0.01 to 0.5 cm 3 /g, an average pore diameter of not more than 300 Å and an average collapse strength of not less than 3 kg, and can be produced by molding hydrotalcite comprising at least magnesium and aluminum and then calcining the resulting molded product at a temperature of 500 to 1500°C.
MOLDED POROUS ARTICLE, METHOD FOR PRODUCTION THEREOF, CATALYST CARRIER, AND CATALYST
The present invention aims at providing a porous molded product comprising magnesium and aluminum which is satisfactory in both of a specific surface area and mechanical properties, can be suitably used as filters, drying agents, adsorbents, purifying agents, deodorants, carriers for catalysts, etc., includes a large amount of micropores, and has a large specific surface area and a high strength, as well as a process for producing the porous molded product. The porous molded product of the present invention comprises at least magnesium and aluminum, and having a magnesium content of 10 to 50% by weight in terms of a magnesium atom, an aluminum content of 5 to 35% by weight in terms of an aluminum atom, a pore volume of 0.01 to 0.5 cm 3 /g, an average pore diameter of not more than 300 Å and an average collapse strength of not less than 3 kg, and can be produced by molding hydrotalcite comprising at least magnesium and aluminum and then calcining the resulting molded product at a temperature of 500 to 1500°C.
MOLDED POROUS ARTICLE, METHOD FOR PRODUCTION THEREOF, CATALYST CARRIER, AND CATALYST
PORÖSER FORMARTIKEL, VERFAHREN ZU SEINER HERSTELLUNG, KATALYSATORTRÄGER UND KATALYSATOR
ARTICLE POREUX MOULÉ, SON PROCÉDÉ DE FABRICATION, SUPPORT DE CATALYSEUR ET CATALYSEUR
TAKAHASHI SHINJI (author) / KOBAYASHI NAOYA (author)
2018-10-17
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
/
B01J
Chemische oder physikalische Verfahren, z.B. Katalyse oder Kolloidchemie
,
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY
/
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
Porous molded product and process for producing the same, carrier for catalysts, and catalyst
| European Patent Office | 2016
Porous ceramics catalyst carrier possessing two-dimensional nanopores and preparation method thereof
| European Patent Office | 2015