METHOD FOR PRESSURIZATION STEAM-AGING OF STEEL SLAG
PROBLEM TO BE SOLVED: To provide an aging method for steel slag capable of stably reducing expansibility of a pressurization steam aging treated steel slag while maintaining crushed product particle size regardless of characteristic or composition of the steel slag.SOLUTION: There is provided a method for conducting aging by pressure vapor by injecting a steel slag crushed to 40 mm or less into a pressure vessel, including reducing vapor pressure in the pressure vessel to 0.14 to 0.27 MPa by diffusing vapor after a first aging by adding pressure to 0.29 to 0.98 MPa by saturation vapor pressure and holding for 1 to 5 hours, and reducing pressure in the pressure vessel to ambient pressure after a second aging by holding at temperature the above mentioned pressure is balanced for 0.5 to 3 hours.
【課題】製鋼スラグの性状や組成によらず、加圧蒸気でエージング処理した製鋼スラグの膨張性を、破砕した製品粒度を保持したまま、安定して低減することができる製鋼スラグのエージング方法を提案する。【解決手段】４０ｍｍ以下に破砕した製鋼スラグを圧力容器内に装入し、加圧蒸気でエージングを施す方法において、飽和蒸気圧で０．２９〜０．９８ＭＰａに加圧して１〜５ｈｒ保持する一次エージングした後、蒸気を放散して圧力容器内の蒸気圧を０．１４〜０．２７ＭＰａに減圧し、上記蒸気圧に平衡する温度で０．５〜３ｈｒ保持する二次エージングした後、圧力容器内の圧力を大気圧まで減圧することを特徴とする製鋼スラグの加圧蒸気エージング方法。【選択図】なし
METHOD FOR PRESSURIZATION STEAM-AGING OF STEEL SLAG
PROBLEM TO BE SOLVED: To provide an aging method for steel slag capable of stably reducing expansibility of a pressurization steam aging treated steel slag while maintaining crushed product particle size regardless of characteristic or composition of the steel slag.SOLUTION: There is provided a method for conducting aging by pressure vapor by injecting a steel slag crushed to 40 mm or less into a pressure vessel, including reducing vapor pressure in the pressure vessel to 0.14 to 0.27 MPa by diffusing vapor after a first aging by adding pressure to 0.29 to 0.98 MPa by saturation vapor pressure and holding for 1 to 5 hours, and reducing pressure in the pressure vessel to ambient pressure after a second aging by holding at temperature the above mentioned pressure is balanced for 0.5 to 3 hours.
【課題】製鋼スラグの性状や組成によらず、加圧蒸気でエージング処理した製鋼スラグの膨張性を、破砕した製品粒度を保持したまま、安定して低減することができる製鋼スラグのエージング方法を提案する。【解決手段】４０ｍｍ以下に破砕した製鋼スラグを圧力容器内に装入し、加圧蒸気でエージングを施す方法において、飽和蒸気圧で０．２９〜０．９８ＭＰａに加圧して１〜５ｈｒ保持する一次エージングした後、蒸気を放散して圧力容器内の蒸気圧を０．１４〜０．２７ＭＰａに減圧し、上記蒸気圧に平衡する温度で０．５〜３ｈｒ保持する二次エージングした後、圧力容器内の圧力を大気圧まで減圧することを特徴とする製鋼スラグの加圧蒸気エージング方法。【選択図】なし
METHOD FOR PRESSURIZATION STEAM-AGING OF STEEL SLAG
製鋼スラグの加圧蒸気エージング方法
ICHIKAWA KOICHI (author)
2015-11-05
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
B09B
DISPOSAL OF SOLID WASTE
,
Beseitigung von festem Abfall
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE