CURING METHOD FOR CEMENT CONCRETE
PROBLEM TO BE SOLVED: To provide a curing method for cement concrete that does not require a large-scale facility, allows prompt curing work, is highly effective in suppressing dry shrinkage resulting from water evaporation, allows a dense cement concrete hardened body to be produced, and suppresses dry shrinkage even under a low-temperature environment by adding a heat insulation effect, thereby constructing a high-quality cement concrete structure with which high strength is developed.SOLUTION: A curing method for cement concrete is for curing a coated cement concrete hardened body made in the following steps: casting cement concrete in a concrete mold; curing the cement concrete and removing the mold; coating a surface of the cement concrete hardened body with a foam polyurethane resin of an expansion ratio between 1.2 to 8 at 150 to 1,500 g/m, the foam polyurethane resin being made of diene-based polyol, a foaming agent, solution A containing catalyst, and solution B containing diisocyanate, thus forming a foamed hardened coat on the surface of the cement concrete hardened body. Furthermore, the foamed hardened coat is removed when the curing process is completed.SELECTED DRAWING: None
【課題】大掛かりな設備が不要で、迅速に養生作業ができ、水分の蒸発による乾燥収縮を抑える効果が高く、緻密なセメントコンクリート硬化体を調製でき、断熱効果を付与することで、低温環境下でも乾燥収縮を抑え、強度発現性の良好な高品質なセメントコンクリート構造物を構築することができる養生方法を提供する。【解決手段】セメントコンクリートを型枠内に打設し、硬化後に脱型したセメントコンクリート硬化体表面に、ジエン系ポリオールと、発泡剤と、触媒を含有するＡ液と、ジイソシアネートを含有するＢ液とを原料として得られる、発泡倍率1.2〜８倍の発泡ポリウレタン樹脂を150〜1,500g/m2被覆して、セメントコンクリート硬化体表面に発泡硬化皮膜を形成して被覆セメントコンクリート硬化体とし、それを養生するセメントコンクリートの養生方法であり、さらに、養生終了時、形成した発泡硬化皮膜を剥がすセメントコンクリートの養生方法である。【選択図】なし
CURING METHOD FOR CEMENT CONCRETE
PROBLEM TO BE SOLVED: To provide a curing method for cement concrete that does not require a large-scale facility, allows prompt curing work, is highly effective in suppressing dry shrinkage resulting from water evaporation, allows a dense cement concrete hardened body to be produced, and suppresses dry shrinkage even under a low-temperature environment by adding a heat insulation effect, thereby constructing a high-quality cement concrete structure with which high strength is developed.SOLUTION: A curing method for cement concrete is for curing a coated cement concrete hardened body made in the following steps: casting cement concrete in a concrete mold; curing the cement concrete and removing the mold; coating a surface of the cement concrete hardened body with a foam polyurethane resin of an expansion ratio between 1.2 to 8 at 150 to 1,500 g/m, the foam polyurethane resin being made of diene-based polyol, a foaming agent, solution A containing catalyst, and solution B containing diisocyanate, thus forming a foamed hardened coat on the surface of the cement concrete hardened body. Furthermore, the foamed hardened coat is removed when the curing process is completed.SELECTED DRAWING: None
【課題】大掛かりな設備が不要で、迅速に養生作業ができ、水分の蒸発による乾燥収縮を抑える効果が高く、緻密なセメントコンクリート硬化体を調製でき、断熱効果を付与することで、低温環境下でも乾燥収縮を抑え、強度発現性の良好な高品質なセメントコンクリート構造物を構築することができる養生方法を提供する。【解決手段】セメントコンクリートを型枠内に打設し、硬化後に脱型したセメントコンクリート硬化体表面に、ジエン系ポリオールと、発泡剤と、触媒を含有するＡ液と、ジイソシアネートを含有するＢ液とを原料として得られる、発泡倍率1.2〜８倍の発泡ポリウレタン樹脂を150〜1,500g/m2被覆して、セメントコンクリート硬化体表面に発泡硬化皮膜を形成して被覆セメントコンクリート硬化体とし、それを養生するセメントコンクリートの養生方法であり、さらに、養生終了時、形成した発泡硬化皮膜を剥がすセメントコンクリートの養生方法である。【選択図】なし
CURING METHOD FOR CEMENT CONCRETE
セメントコンクリートの養生方法
ARAKI AKITOSHI (author) / MATSUMOTO MASAO (author) / NAGASAKI HIRONORI (author) / IWASAKI MASAHIRO (author) / TANAKA TORU (author) / ASANO HITOSHI (author) / SEKINE ICHIRO (author) / NAKAMURA GENKI (author) / HARA NAOHIRO (author)
2016-05-26
Patent
Electronic Resource
Japanese
Curing of Portland cement concrete
| Engineering Index Backfile | 1929
Curing Compounds for Portland Cement Concrete
| NTIS | 1968
Curing of Portland cement concrete -- V
| Engineering Index Backfile | 1933
White cement-based concrete curing method, white cement-based concrete member and application
| European Patent Office | 2024
| European Patent Office | 2019