BENEFICIATION METHOD OF COLEMANITE ORE AGGREGATE AND CONCRETE STRUCTURE
PROBLEM TO BE SOLVED: To provide a method of beneficiation of a colemanite ore aggregate capable of being solidified by normal Portland cement from natural colemanite ore raw stone.SOLUTION: A natural colemanite ore raw stone having BOquality of about 45% and a maximum dimension of about 200 mm is used (Step 1). The natural colemanite ore raw stone is dried (Step 2). For example, the ore is dried at a temperature of 100°C for about 1 hour by a rotary kiln type drier. In this case, aggregate having a grain size of 5 mm or less crushed by drying may be removed (Step 2-2). The colemanite ore in a dry state is impregnated or watered to be a wet state (Step 3). Then surface is dried and the colemanite ore is rough-crushed (Step 4). The grain size is adjusted by slightly crushing the ore by stirring or compression. The colemanite aggregate is screened (Step 5). Fine powder with a grain size of 0.15 mm or less is removed to obtain a coarse aggregate and a fine aggregate. Concrete is formed by using the colemanite aggregate with removing unnecessary objects.SELECTED DRAWING: Figure 4
【課題】天然産コレマナイト鉱原石から普通ポルトランドセメントで固めることが可能なコレマナイト鉱骨材を選鉱する方法を提供する。【解決手段】B2O3品位が45%程度、最大寸法200mm程度の天然コレマナイト鉱原石を用いる（ステップ１）。天然コレマナイト鉱原石を乾燥させる（ステップ２）。例えば、ロータリーキルン型乾燥機により、温度100℃で1時間程度、乾燥させる。このとき、乾燥により破砕された粒度5mm以下の集塊を取り除いても良い（ステップ２−２）。乾燥状態のコレマナイト鉱を水に浸漬させるか散水して湿潤状態にする（ステップ３）。次いで、表乾させ、コレマナイト鉱を粗破砕する（ステップ４）。撹拌または圧縮により軽く破砕することで粒度調整する。コレマナイト骨材を篩分けする（ステップ５）。0.15mm以下の微粉を取り除き、粗骨材、細骨材を得る。不要物を取り除いたコレマナイト骨材を用いて、コンクリートを形成する。【選択図】図４
BENEFICIATION METHOD OF COLEMANITE ORE AGGREGATE AND CONCRETE STRUCTURE
PROBLEM TO BE SOLVED: To provide a method of beneficiation of a colemanite ore aggregate capable of being solidified by normal Portland cement from natural colemanite ore raw stone.SOLUTION: A natural colemanite ore raw stone having BOquality of about 45% and a maximum dimension of about 200 mm is used (Step 1). The natural colemanite ore raw stone is dried (Step 2). For example, the ore is dried at a temperature of 100°C for about 1 hour by a rotary kiln type drier. In this case, aggregate having a grain size of 5 mm or less crushed by drying may be removed (Step 2-2). The colemanite ore in a dry state is impregnated or watered to be a wet state (Step 3). Then surface is dried and the colemanite ore is rough-crushed (Step 4). The grain size is adjusted by slightly crushing the ore by stirring or compression. The colemanite aggregate is screened (Step 5). Fine powder with a grain size of 0.15 mm or less is removed to obtain a coarse aggregate and a fine aggregate. Concrete is formed by using the colemanite aggregate with removing unnecessary objects.SELECTED DRAWING: Figure 4
【課題】天然産コレマナイト鉱原石から普通ポルトランドセメントで固めることが可能なコレマナイト鉱骨材を選鉱する方法を提供する。【解決手段】B2O3品位が45%程度、最大寸法200mm程度の天然コレマナイト鉱原石を用いる（ステップ１）。天然コレマナイト鉱原石を乾燥させる（ステップ２）。例えば、ロータリーキルン型乾燥機により、温度100℃で1時間程度、乾燥させる。このとき、乾燥により破砕された粒度5mm以下の集塊を取り除いても良い（ステップ２−２）。乾燥状態のコレマナイト鉱を水に浸漬させるか散水して湿潤状態にする（ステップ３）。次いで、表乾させ、コレマナイト鉱を粗破砕する（ステップ４）。撹拌または圧縮により軽く破砕することで粒度調整する。コレマナイト骨材を篩分けする（ステップ５）。0.15mm以下の微粉を取り除き、粗骨材、細骨材を得る。不要物を取り除いたコレマナイト骨材を用いて、コンクリートを形成する。【選択図】図４
BENEFICIATION METHOD OF COLEMANITE ORE AGGREGATE AND CONCRETE STRUCTURE
コレマナイト鉱骨材の選鉱方法およびコンクリート構造物
MARU AKIO (author) / OBATA KUNIHIKO (author)
2016-06-20
Patent
Electronic Resource
Japanese