SURFACE-TREATED MOLDED HEAT INSULATOR AND METHOD FOR PRODUCING THE SAME
PROBLEM TO BE SOLVED: To provide a long-life molded heat insulator at a low cost, which could be suppressed from deterioration and powdering.SOLUTION: Provided is a method for producing a surface-treated molded heat insulator, comprising: an immersion step where at least one surface of a molded heat insulator, having a fiber felt interlaced with carbon fibers and a protective carbon layer comprising a carbonaceous material which coats surfaces of the carbon fibers in the fiber felt, is immersed in a solution of a surface coating agent comprising a synthetic resin which is carbonized by a heat treatment and a solvent which dissolves the synthetic resin to add the surface coating agent-containing solution to the molded heat insulator; and a heat treatment step where, after the immersion step, the molded heat insulator is heat treated at 1500 to 2500°C under an inert atmosphere to form a surface coating layer by carbonizing the synthetic resin.SELECTED DRAWING: Figure 1
【課題】劣化や粉化を抑制し得た長寿命な成形断熱材を低コストで提供する。【解決手段】炭素繊維を交絡させた繊維フェルトと前記繊維フェルトの炭素繊維表面を被覆する炭素質からなる保護炭素層とを有する成形断熱材の少なくとも一つの表面を、熱処理により炭素化する合成樹脂と前記合成樹脂を溶解する溶媒とからなる表面被覆剤溶液に浸漬して、成形断熱材に前記表面被覆剤溶液を添加する浸漬ステップと、前記浸漬ステップ後、成形断熱材を不活性雰囲気下1500〜2500℃で熱処理し、前記合成樹脂を炭素化させて、表面被覆層を形成する熱処理ステップと、を有する表面処理された成形断熱材の製造方法。【選択図】図1
SURFACE-TREATED MOLDED HEAT INSULATOR AND METHOD FOR PRODUCING THE SAME
PROBLEM TO BE SOLVED: To provide a long-life molded heat insulator at a low cost, which could be suppressed from deterioration and powdering.SOLUTION: Provided is a method for producing a surface-treated molded heat insulator, comprising: an immersion step where at least one surface of a molded heat insulator, having a fiber felt interlaced with carbon fibers and a protective carbon layer comprising a carbonaceous material which coats surfaces of the carbon fibers in the fiber felt, is immersed in a solution of a surface coating agent comprising a synthetic resin which is carbonized by a heat treatment and a solvent which dissolves the synthetic resin to add the surface coating agent-containing solution to the molded heat insulator; and a heat treatment step where, after the immersion step, the molded heat insulator is heat treated at 1500 to 2500°C under an inert atmosphere to form a surface coating layer by carbonizing the synthetic resin.SELECTED DRAWING: Figure 1
【課題】劣化や粉化を抑制し得た長寿命な成形断熱材を低コストで提供する。【解決手段】炭素繊維を交絡させた繊維フェルトと前記繊維フェルトの炭素繊維表面を被覆する炭素質からなる保護炭素層とを有する成形断熱材の少なくとも一つの表面を、熱処理により炭素化する合成樹脂と前記合成樹脂を溶解する溶媒とからなる表面被覆剤溶液に浸漬して、成形断熱材に前記表面被覆剤溶液を添加する浸漬ステップと、前記浸漬ステップ後、成形断熱材を不活性雰囲気下1500〜2500℃で熱処理し、前記合成樹脂を炭素化させて、表面被覆層を形成する熱処理ステップと、を有する表面処理された成形断熱材の製造方法。【選択図】図1
SURFACE-TREATED MOLDED HEAT INSULATOR AND METHOD FOR PRODUCING THE SAME
表面処理された成形断熱材及びその製造方法
MIZUNO JUNYA (author) / SOGABE TOSHIAKI (author)
2017-03-23
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
D04H
Herstellen von flächigem Textilgut, z.B. aus Fasern oder fadenförmigem Material
,
MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL
/
D06M
Behandeln von Fasern, Fäden, Garnen, Textilgut, Federn oder aus solchen Materialien hergestelltem Fasergut, soweit nicht anderweitig in Klasse D06 vorgesehen
,
TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
/
F16L
PIPES
,
Rohre
MOLDED HEAT INSULATING MATERIAL AND METHOD FOR PRODUCING THE SAME
European Patent Office | 2018
|