METHOD FOR PRODUCING PORTLAND CEMENT FOR CONTROLLING DRYING SHRINKAGE STRAIN
To provide a method for producing a Portland cement for controlling drying shrinkage strain of a cement hardened body by adjusting a particle size distribution of the Portland cement to a specified range.SOLUTION: Drying shrinkage strain of a cement hardened body is controlled by, in a grinding step in a process for producing a Portland cement: adjusting a Blaine's specific surface area of the cement within a range of 3,000-3,600 cm-/g; and adjusting a distribution constant, when particle size distribution is regressed by a Rosin-Rammler distribution expression, to a specified range. Preferably, the distribution constant n, when the range of 5-90 μm of the particle size distribution curve of the cement is regressed by a Rosin-Rammler distribution expression, is adjusted within the range of 1.000-1.117, for example, the drying shrinkage strain (ε) after 28 day of a storage term is made equal to or lower than 580×10.SELECTED DRAWING: Figure 1
【課題】ポルトランドセメントの粒度分布を特定の範囲に調整することによって、セメント硬化体の乾燥収縮ひずみを制御するポルトランドセメントの製造方法を提供する。【解決手段】ポルトランドセメント製造工程の粉砕工程において、セメントのブレーン比表面積を３０００〜３６００ｃｍ２/ｇの範囲に調整し、かつ粒度分布をRosin−Rammler分布式で回帰したときの均等数を所定範囲に調整することによって、セメント硬化体の乾燥収縮ひずみを制御することを特徴とし、好ましくは、セメントの粒度分布曲線の５〜９０μｍの範囲をRosin−Rammler分布式で回帰したときの均等数ｎを１.０００〜１.１１７の範囲に調整し、例えば、保存期間２８日の乾燥収縮ひずみ(ε２８)を５８０×１０−６以下にするポルトランドセメントの製造方法。【選択図】図１
METHOD FOR PRODUCING PORTLAND CEMENT FOR CONTROLLING DRYING SHRINKAGE STRAIN
To provide a method for producing a Portland cement for controlling drying shrinkage strain of a cement hardened body by adjusting a particle size distribution of the Portland cement to a specified range.SOLUTION: Drying shrinkage strain of a cement hardened body is controlled by, in a grinding step in a process for producing a Portland cement: adjusting a Blaine's specific surface area of the cement within a range of 3,000-3,600 cm-/g; and adjusting a distribution constant, when particle size distribution is regressed by a Rosin-Rammler distribution expression, to a specified range. Preferably, the distribution constant n, when the range of 5-90 μm of the particle size distribution curve of the cement is regressed by a Rosin-Rammler distribution expression, is adjusted within the range of 1.000-1.117, for example, the drying shrinkage strain (ε) after 28 day of a storage term is made equal to or lower than 580×10.SELECTED DRAWING: Figure 1
【課題】ポルトランドセメントの粒度分布を特定の範囲に調整することによって、セメント硬化体の乾燥収縮ひずみを制御するポルトランドセメントの製造方法を提供する。【解決手段】ポルトランドセメント製造工程の粉砕工程において、セメントのブレーン比表面積を３０００〜３６００ｃｍ２/ｇの範囲に調整し、かつ粒度分布をRosin−Rammler分布式で回帰したときの均等数を所定範囲に調整することによって、セメント硬化体の乾燥収縮ひずみを制御することを特徴とし、好ましくは、セメントの粒度分布曲線の５〜９０μｍの範囲をRosin−Rammler分布式で回帰したときの均等数ｎを１.０００〜１.１１７の範囲に調整し、例えば、保存期間２８日の乾燥収縮ひずみ(ε２８)を５８０×１０−６以下にするポルトランドセメントの製造方法。【選択図】図１
METHOD FOR PRODUCING PORTLAND CEMENT FOR CONTROLLING DRYING SHRINKAGE STRAIN
乾燥収縮ひずみを制御するポルトランドセメントの製造方法
HARADA TAKUMI (author) / KADOTA HIROSHI (author)
2018-11-01
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
Drying shrinkage of ordinary portland cement pastes
| Tema Archive | 1989
An updated look at drying shrinkage of Portland and blended Portland cement concretes
| Online Contents | 2006
Effects of Superplasticising Admixtures on Drying Shrinkage of Portland Cement Mortars
| British Library Conference Proceedings | 1995
Analysis of drying shrinkage data for portland cement mortar and concrete
| Engineering Index Backfile | 1967