SPRAY CONCRETE AND MANUFACTURING METHOD THEREFOR
To provide a spray concrete excellent in quick setting property or initial strength development property, good in consistency of concrete and good in pump forcibly feeding during spray even when a liquid quick setting agent is used, and a manufacturing method therefor.SOLUTION: There is provided spray concrete manufactured by combining concrete containing sodium aluminate, lime, one or more kind of retardant selected from tartaric acid, gluconic acid and heptonic acid or salt thereof, in which the content of the sodium aluminate is 0.6 to 3.0 pts.mass based on 100 pts.mass of cement in concrete, the content of the lime is 0.2 to 4.0 pts.mass based on 100 pts.mass of the cement in the concrete, and the content of the retardant is 0.04 to 0.15 pts.mass based on 100 pts.mass of the cement in the concrete, and a liquid quick setting agent containing aluminum sulfate as an active ingredient.SELECTED DRAWING: None
【課題】液体急結剤を用いても、急結性や初期強度発現性が優れるとともに、コンクリートのコンシステンシーが良好で吹付時のポンプ圧送が良好である吹付コンクリート及びその製造方法を提供する。【解決手段】アルミン酸ナトリウムと、石灰と、酒石酸、グルコン酸及びへプトン酸又はその塩から選ばれる１種以上の遅延剤とを含有するコンクリートであって、該アルミン酸ナトリウムの含有量がコンクリート中のセメント１００質量部に対して０．６〜３．０質量部であり、該石灰の含有量がコンクリート中のセメント１００質量部に対して０．２〜４．０質量部であり、かつ該遅延剤の含有量がコンクリート中のセメント１００質量部に対して０．０４〜０．１５質量部であるコンクリートと、硫酸アルミニウムを有効成分とする液体急結剤とを組み合わせてなることを特徴とする吹付コンクリート。【選択図】なし
SPRAY CONCRETE AND MANUFACTURING METHOD THEREFOR
To provide a spray concrete excellent in quick setting property or initial strength development property, good in consistency of concrete and good in pump forcibly feeding during spray even when a liquid quick setting agent is used, and a manufacturing method therefor.SOLUTION: There is provided spray concrete manufactured by combining concrete containing sodium aluminate, lime, one or more kind of retardant selected from tartaric acid, gluconic acid and heptonic acid or salt thereof, in which the content of the sodium aluminate is 0.6 to 3.0 pts.mass based on 100 pts.mass of cement in concrete, the content of the lime is 0.2 to 4.0 pts.mass based on 100 pts.mass of the cement in the concrete, and the content of the retardant is 0.04 to 0.15 pts.mass based on 100 pts.mass of the cement in the concrete, and a liquid quick setting agent containing aluminum sulfate as an active ingredient.SELECTED DRAWING: None
【課題】液体急結剤を用いても、急結性や初期強度発現性が優れるとともに、コンクリートのコンシステンシーが良好で吹付時のポンプ圧送が良好である吹付コンクリート及びその製造方法を提供する。【解決手段】アルミン酸ナトリウムと、石灰と、酒石酸、グルコン酸及びへプトン酸又はその塩から選ばれる１種以上の遅延剤とを含有するコンクリートであって、該アルミン酸ナトリウムの含有量がコンクリート中のセメント１００質量部に対して０．６〜３．０質量部であり、該石灰の含有量がコンクリート中のセメント１００質量部に対して０．２〜４．０質量部であり、かつ該遅延剤の含有量がコンクリート中のセメント１００質量部に対して０．０４〜０．１５質量部であるコンクリートと、硫酸アルミニウムを有効成分とする液体急結剤とを組み合わせてなることを特徴とする吹付コンクリート。【選択図】なし
SPRAY CONCRETE AND MANUFACTURING METHOD THEREFOR
吹付コンクリート及びその製造方法