CEMENT COMPOSITION AND HARDENING BODY THEREOF
To provide a cement composition in which the generation of cracks is suppressed and a hardening body with excellent durability can be obtained, and the hardening body thereof.SOLUTION: The present invention relates to a cement composition that includes cement, cellulose nanofiber, and water, and has a mass ratio of water to the cement of 0.4 or less. Portland cement is preferable as the cement. It is preferable that the portland cement is high early strength portland cement, and the mass ratio of fine aggregate to the high early strength portland cement is 2.0 or less. It is preferable that the unit quantity of cellulose nanofiber in the cement composition is 0.1 kg/mor more and 15 kg/mor less. In a hardening body of the cement composition of the present invention, the rate of split tensile strength of 91 days of material age by atmospheric curing relative to the split tensile strength of 91 days of material age by underwater curing measured in accordance with JIS-A-1113(2006) is 0.90 or more and 1.10 or less.SELECTED DRAWING: None
【課題】ひび割れの発生が抑制され、耐久性に優れる硬化体を得ることができるセメント組成物及びその硬化体を提供する。【解決手段】本発明は、セメントと、セルロースナノファイバーと、水とを含有し、セメントに対する水の質量比が０．４以下であるセメント組成物である。セメントとしては、ポルトランドセメントが好ましい。ポルトランドセメントが早強ポルトランドセメントであり、早強ポルトランドセメントに対する細骨材の質量比が２．０以下であることが好ましい。当該セメント組成物のセルロースナノファイバーの単位量としては、０．１ｋｇ／ｍ３以上１５ｋｇ／ｍ３以下が好ましい。また、本発明は、水中養生による材齢９１日のＪＩＳ−Ａ−１１１３（２００６）に準拠して測定される割裂引張強度に対する気中養生による材齢９１日の上記割裂引張強度の割合が、０．９０以上１．１０以下である当該セメント組成物の硬化体である。【選択図】なし
CEMENT COMPOSITION AND HARDENING BODY THEREOF
To provide a cement composition in which the generation of cracks is suppressed and a hardening body with excellent durability can be obtained, and the hardening body thereof.SOLUTION: The present invention relates to a cement composition that includes cement, cellulose nanofiber, and water, and has a mass ratio of water to the cement of 0.4 or less. Portland cement is preferable as the cement. It is preferable that the portland cement is high early strength portland cement, and the mass ratio of fine aggregate to the high early strength portland cement is 2.0 or less. It is preferable that the unit quantity of cellulose nanofiber in the cement composition is 0.1 kg/mor more and 15 kg/mor less. In a hardening body of the cement composition of the present invention, the rate of split tensile strength of 91 days of material age by atmospheric curing relative to the split tensile strength of 91 days of material age by underwater curing measured in accordance with JIS-A-1113(2006) is 0.90 or more and 1.10 or less.SELECTED DRAWING: None
【課題】ひび割れの発生が抑制され、耐久性に優れる硬化体を得ることができるセメント組成物及びその硬化体を提供する。【解決手段】本発明は、セメントと、セルロースナノファイバーと、水とを含有し、セメントに対する水の質量比が０．４以下であるセメント組成物である。セメントとしては、ポルトランドセメントが好ましい。ポルトランドセメントが早強ポルトランドセメントであり、早強ポルトランドセメントに対する細骨材の質量比が２．０以下であることが好ましい。当該セメント組成物のセルロースナノファイバーの単位量としては、０．１ｋｇ／ｍ３以上１５ｋｇ／ｍ３以下が好ましい。また、本発明は、水中養生による材齢９１日のＪＩＳ−Ａ−１１１３（２００６）に準拠して測定される割裂引張強度に対する気中養生による材齢９１日の上記割裂引張強度の割合が、０．９０以上１．１０以下である当該セメント組成物の硬化体である。【選択図】なし
CEMENT COMPOSITION AND HARDENING BODY THEREOF
セメント組成物及びその硬化体
OKAWA JUNYA (author) / SASAKI HIROTO (author) / SASAKI WATARU (author) / ONDA YOSUKE (author) / TANIGUCHI HIDEAKI (author)
2019-08-08
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
CEMENT COMPOSITION AND METHOD FOR PRODUCING CEMENT HARDENING BODY
| European Patent Office | 2020
MANUFACTURING METHOD OF CEMENT HARDENING BODY USING CEMENT COMPOSITION
| European Patent Office | 2017
CEMENT COMPOSITION AND METHOD FOR PRODUCING CEMENT HARDENING BODY
| European Patent Office | 2021
METHOD FOR PRODUCING HARDENING CEMENT COMPOSITION, HARDENING CEMENT COMPOSITION, AND HARDENED CEMENT
| European Patent Office | 2024
QUICK-HARDENING CEMENT ADMIXTURE AND QUICK-HARDENING CEMENT COMPOSITION
| European Patent Office | 2017