RAPID HARDENING ADDITIVE FOR CEMENT, METHOD FOR PRODUCING THE SAME, AND RAPID HARDENING CEMENT COMPOSITION
To provide a rapid hardening additive for cement, capable of securing sufficient working life and capable of imparting an early strength-developing function, and a method for producing the same; and to provide a rapid hardening cement composition.SOLUTION: A rapid hardening additive for cement comprises a calcium aluminate material, the surface of which is treated with water, boric acid, and a gypsum, wherein: the calcium aluminate material, the surface of which is treated with the water, is surface-treated with 0.25 to 2 pts.mass of water based on 100 pts.mass of calcium aluminate material powder; 1.2-1.8 pts.mass of the boric acid is contained in the calcium aluminate material treated with the water based on 100 pts.mass; and the gypsum is contained in the calcium aluminate material treated with the water in a mass ratio of 4:6-6:4.SELECTED DRAWING: None
【課題】 十分な可使時間を確保できるとともに、早期強度発現性を付与することができるセメント用速硬性混和材及びその製造方法、並びに速硬性セメント組成物を提供する。【解決手段】 セメント用速硬性混和材は、表面が水処理されたカルシウムアルミネート材と、ホウ酸と、石膏とを含有し、前記表面が水処理されたカルシウムアルミネート材は、カルシウムアルミネート材粉末１００質量部に対して、０．２５〜２質量部の水で表面処理されており、ホウ酸は、前記水処理されたカルシウムアルミネート材に１００質量部に対して１．２〜１．８質量部含まれ、石膏は、前記水処理されたカルシウムアルミネート材に対して、質量比で４：６〜６：４の割合まれる。【選択図】なし
RAPID HARDENING ADDITIVE FOR CEMENT, METHOD FOR PRODUCING THE SAME, AND RAPID HARDENING CEMENT COMPOSITION
To provide a rapid hardening additive for cement, capable of securing sufficient working life and capable of imparting an early strength-developing function, and a method for producing the same; and to provide a rapid hardening cement composition.SOLUTION: A rapid hardening additive for cement comprises a calcium aluminate material, the surface of which is treated with water, boric acid, and a gypsum, wherein: the calcium aluminate material, the surface of which is treated with the water, is surface-treated with 0.25 to 2 pts.mass of water based on 100 pts.mass of calcium aluminate material powder; 1.2-1.8 pts.mass of the boric acid is contained in the calcium aluminate material treated with the water based on 100 pts.mass; and the gypsum is contained in the calcium aluminate material treated with the water in a mass ratio of 4:6-6:4.SELECTED DRAWING: None
【課題】 十分な可使時間を確保できるとともに、早期強度発現性を付与することができるセメント用速硬性混和材及びその製造方法、並びに速硬性セメント組成物を提供する。【解決手段】 セメント用速硬性混和材は、表面が水処理されたカルシウムアルミネート材と、ホウ酸と、石膏とを含有し、前記表面が水処理されたカルシウムアルミネート材は、カルシウムアルミネート材粉末１００質量部に対して、０．２５〜２質量部の水で表面処理されており、ホウ酸は、前記水処理されたカルシウムアルミネート材に１００質量部に対して１．２〜１．８質量部含まれ、石膏は、前記水処理されたカルシウムアルミネート材に対して、質量比で４：６〜６：４の割合まれる。【選択図】なし
RAPID HARDENING ADDITIVE FOR CEMENT, METHOD FOR PRODUCING THE SAME, AND RAPID HARDENING CEMENT COMPOSITION
セメント用速硬性混和材、その製造方法及び速硬性セメント組成物
ITO KYOKO (author) / KIKUCHI SADATO (author) / HIRANO YUKI (author) / KAMIKOUCHI TAKASHI (author) / KIKO TOMOKO (author) / KANO KAZUHIRO (author)
2020-04-02
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
RAPID-HARDENING ADMIXTURE MATERIAL AND RAPID-HARDENING CEMENT COMPOSITION
| European Patent Office | 2023