ZIRCONIA CALCINATED BODY AND ZIRCONIA SINTERED BODY, AND LAMINATE
To provide a zirconia sintered body having suppressed irregular shrinkage deformation.SOLUTION: A zirconia calcinated body is formed by burning a laminate comprising a plurality of zirconia layers containing zirconia and a stabilizer for suppressing a phase transition of zirconia and having different compositions, wherein: when a test piece is prepared by molding the resulting zirconia calcinated body to a rectangular solid shape with dimension of width 50 mm×height 10 mm×depth 5 mm, the test piece having a surface as a bottom surface with dimension of width 50 mm×depth 5 mm, a border surface formed by the plurality of zirconia layers is in parallel to the bottom surface; when the test piece is burned at 1,500°C for 2 hours and is placed with a bottom surface deformed into a concave surface facing down out of two bottom surfaces, (maximum intervals between a bottom surface deformed into the concave surface and a ground surface)/(distance between grand parts in a width direction)×100 is 0.15 or less; and 0-0.3 mass% of aluminum oxide is contained based on the total mass of the zirconia and the stabilizer.SELECTED DRAWING: None
【課題】いびつな収縮変形を抑制したジルコニア焼結体を提供すること。【解決手段】ジルコニア及びジルコニアの相転移を抑制する安定化剤を含有し、組成が異なる複数のジルコニア層からなる積層体を焼成してなるジルコニア仮焼体であって、ジルコニア仮焼体を幅５０ｍｍ×高さ１０ｍｍ×奥行き５ｍｍの寸法の直方体形状に成形したものを試験片とし、試験片において、幅５０ｍｍ×奥行き５ｍｍとなる面を底面としたとき、複数のジルコニア層によって形成される境界面が底面と平行になっており、試験片を１５００℃で２時間焼成し、２つの底面のうち、凹面に変形した底面を下にして載置したとき、（凹面に変形した底面と接地面との最大間隔）／（幅方向における接地部分間の距離）×１００が０．１５以下であり、ジルコニア及び安定化剤の合計質量に対して酸化アルミニウムを０質量％〜０．３質量％含有する。【選択図】なし
ZIRCONIA CALCINATED BODY AND ZIRCONIA SINTERED BODY, AND LAMINATE
To provide a zirconia sintered body having suppressed irregular shrinkage deformation.SOLUTION: A zirconia calcinated body is formed by burning a laminate comprising a plurality of zirconia layers containing zirconia and a stabilizer for suppressing a phase transition of zirconia and having different compositions, wherein: when a test piece is prepared by molding the resulting zirconia calcinated body to a rectangular solid shape with dimension of width 50 mm×height 10 mm×depth 5 mm, the test piece having a surface as a bottom surface with dimension of width 50 mm×depth 5 mm, a border surface formed by the plurality of zirconia layers is in parallel to the bottom surface; when the test piece is burned at 1,500°C for 2 hours and is placed with a bottom surface deformed into a concave surface facing down out of two bottom surfaces, (maximum intervals between a bottom surface deformed into the concave surface and a ground surface)/(distance between grand parts in a width direction)×100 is 0.15 or less; and 0-0.3 mass% of aluminum oxide is contained based on the total mass of the zirconia and the stabilizer.SELECTED DRAWING: None
【課題】いびつな収縮変形を抑制したジルコニア焼結体を提供すること。【解決手段】ジルコニア及びジルコニアの相転移を抑制する安定化剤を含有し、組成が異なる複数のジルコニア層からなる積層体を焼成してなるジルコニア仮焼体であって、ジルコニア仮焼体を幅５０ｍｍ×高さ１０ｍｍ×奥行き５ｍｍの寸法の直方体形状に成形したものを試験片とし、試験片において、幅５０ｍｍ×奥行き５ｍｍとなる面を底面としたとき、複数のジルコニア層によって形成される境界面が底面と平行になっており、試験片を１５００℃で２時間焼成し、２つの底面のうち、凹面に変形した底面を下にして載置したとき、（凹面に変形した底面と接地面との最大間隔）／（幅方向における接地部分間の距離）×１００が０．１５以下であり、ジルコニア及び安定化剤の合計質量に対して酸化アルミニウムを０質量％〜０．３質量％含有する。【選択図】なし
ZIRCONIA CALCINATED BODY AND ZIRCONIA SINTERED BODY, AND LAMINATE
ジルコニア仮焼体及びジルコニア焼結体並びに積層体
YAMADA YOSHIHISA (author) / MATSUMOTO ATSUSHI (author) / ITO TSUGUHISA (author)
2020-05-21
Patent
Electronic Resource
Japanese
ZIRCONIA-CALCINATED BODY CAPABLE OF PRODUCING FLUORESCENT ZIRCONIA-SINTERED BODY
| European Patent Office | 2021
| European Patent Office | 2016
ZIRCONIA CALCINATED BODY AND MANUFACTURING METHOD THEREFOR
| European Patent Office | 2018