SINTERED ZIRCON MATERIAL FOR FORMING BLOCK
To provide a zircon refractory object formed by using a fusion draw process used for forming glass, and to provide a method for forming the same.SOLUTION: A refractory object may include a zircon body that may include an AlO-containing component of about 0.1 wt.% or more and about 5.5 wt.% or less with respect to a total weight of the zircon body. The zircon body may further include an SiOcomponent of 25 wt.% or more and 35 wt.% or less with respect to the total weight of the zircon body.SELECTED DRAWING: Figure 1
【課題】ガラスの成形に用いられるフュージョンドロープロセスを用いたジルコン耐火物及びその形成方法を提供する。【解決手段】耐火物はジルコン本体を含んでもよく、このジルコン本体は、ジルコン本体の総重量に対して約０．１重量％以上かつ約５．５重量％以下のＡｌ２Ｏ３含有成分を含んでもよい。このジルコン本体は、ジルコン本体の総重量に対して約２５重量％以上かつ約３５重量％以下のＳｉＯ２成分をさらに含んでもよい。【選択図】図１
SINTERED ZIRCON MATERIAL FOR FORMING BLOCK
To provide a zircon refractory object formed by using a fusion draw process used for forming glass, and to provide a method for forming the same.SOLUTION: A refractory object may include a zircon body that may include an AlO-containing component of about 0.1 wt.% or more and about 5.5 wt.% or less with respect to a total weight of the zircon body. The zircon body may further include an SiOcomponent of 25 wt.% or more and 35 wt.% or less with respect to the total weight of the zircon body.SELECTED DRAWING: Figure 1
【課題】ガラスの成形に用いられるフュージョンドロープロセスを用いたジルコン耐火物及びその形成方法を提供する。【解決手段】耐火物はジルコン本体を含んでもよく、このジルコン本体は、ジルコン本体の総重量に対して約０．１重量％以上かつ約５．５重量％以下のＡｌ２Ｏ３含有成分を含んでもよい。このジルコン本体は、ジルコン本体の総重量に対して約２５重量％以上かつ約３５重量％以下のＳｉＯ２成分をさらに含んでもよい。【選択図】図１
SINTERED ZIRCON MATERIAL FOR FORMING BLOCK
ブロック形成用焼結ジルコン材料