ALUMINOUS CEMENT COMPOSITION FOR SALT-SHIELDING MORTAR
To provide an aluminous cement composition for a salt-shielding mortar, having small initial-state length change along with hardening and capable of forming a mortar hardened body having salt-shielding property after hardening.SOLUTION: The invention provides an aluminous cement composition for a salt-shielding mortar involving an aluminous cement and a gypsum hemihydrate, wherein the aluminous cement composition for the salt-shielding mortar is characterized by that the aluminous cement includes 55-75 mass% of CA, 5-8 mass% of C12A7, 10-28 mass% of C4AF, and 2-6 mass% of C2AS, Blaine specific surface area of the aluminous cement is 2000-4000 cm2/g, Blaine specific surface area of the gypsum hemihydrate is 3000-6000 cm2/g, the content of the gypsum hemihydrate is 10-24 pts.mass per 100 pts.mass of the aluminous cement.SELECTED DRAWING: None
【課題】硬化に伴う初期の長さ変化量が小さく、硬化後において遮塩性を有するモルタル硬化体を形成することが可能な遮塩性モルタル用アルミナセメント組成物を提供すること。【解決手段】アルミナセメント及び半水石膏を含む遮塩性モルタル用アルミナセメント組成物であって、上記アルミナセメントが、ＣＡを５５質量％〜７５質量％、Ｃ１２Ａ７を５質量％〜８質量％、Ｃ４ＡＦを１０質量％〜２８質量％、及びＣ２ＡＳを２質量％〜６質量％含み、上記アルミナセメントのブレーン比表面積が、２０００ｃｍ２／ｇ〜４０００ｃｍ２／ｇであり、上記半水石膏のブレーン比表面積が、３０００ｃｍ２／ｇ〜６０００ｃｍ２／ｇであり、上記半水石膏の含有量が、上記アルミナセメント１００質量部に対して、１０量部〜２４質量部である、遮塩性モルタル用アルミナセメント組成物を提供する。【選択図】なし
ALUMINOUS CEMENT COMPOSITION FOR SALT-SHIELDING MORTAR
To provide an aluminous cement composition for a salt-shielding mortar, having small initial-state length change along with hardening and capable of forming a mortar hardened body having salt-shielding property after hardening.SOLUTION: The invention provides an aluminous cement composition for a salt-shielding mortar involving an aluminous cement and a gypsum hemihydrate, wherein the aluminous cement composition for the salt-shielding mortar is characterized by that the aluminous cement includes 55-75 mass% of CA, 5-8 mass% of C12A7, 10-28 mass% of C4AF, and 2-6 mass% of C2AS, Blaine specific surface area of the aluminous cement is 2000-4000 cm2/g, Blaine specific surface area of the gypsum hemihydrate is 3000-6000 cm2/g, the content of the gypsum hemihydrate is 10-24 pts.mass per 100 pts.mass of the aluminous cement.SELECTED DRAWING: None
【課題】硬化に伴う初期の長さ変化量が小さく、硬化後において遮塩性を有するモルタル硬化体を形成することが可能な遮塩性モルタル用アルミナセメント組成物を提供すること。【解決手段】アルミナセメント及び半水石膏を含む遮塩性モルタル用アルミナセメント組成物であって、上記アルミナセメントが、ＣＡを５５質量％〜７５質量％、Ｃ１２Ａ７を５質量％〜８質量％、Ｃ４ＡＦを１０質量％〜２８質量％、及びＣ２ＡＳを２質量％〜６質量％含み、上記アルミナセメントのブレーン比表面積が、２０００ｃｍ２／ｇ〜４０００ｃｍ２／ｇであり、上記半水石膏のブレーン比表面積が、３０００ｃｍ２／ｇ〜６０００ｃｍ２／ｇであり、上記半水石膏の含有量が、上記アルミナセメント１００質量部に対して、１０量部〜２４質量部である、遮塩性モルタル用アルミナセメント組成物を提供する。【選択図】なし
ALUMINOUS CEMENT COMPOSITION FOR SALT-SHIELDING MORTAR
遮塩性モルタル用アルミナセメント組成物