METHOD FOR PRODUCING MAGNESIA-CARBON REFRACTORY
To provide a method for producing a magnesia-carbon refractory in which a magnesia-carbon reaction is further suppressed by further densification of the magnesia-carbon refractory and a damage of a structure is suppressed.SOLUTION: A method for producing a magnesia-carbon refractory comprises: a molding step of kneading and molding a mixture to obtain a molded body; a non-oxidizing atmosphere firing step of firing the molded body at 800-1,500°C in a non-oxidizing atmosphere to obtain a sintered body; and an impregnation step of impregnating the sintered body with coal tar pitch to obtain a magnesia-carbon refractory. The mixture contains a magnesia raw material, a carbon raw material, and a binder. Particle size of 15-35 mass% of the magnesia raw material is less than 0.3 mm and the balance has a particle diameter of 0.3 mm or more. An amount of the added binder is 0.5 mass% or more and less than 3 mass% based on the total content of 100 mass% of the magnesia raw material and the carbon raw material. The viscosity of the coal tar pitch is 0.06 Pa s or less at 180°C.SELECTED DRAWING: None
【課題】 マグネシア・カーボン質耐火物のさらなる緻密化によりマグネシア・カーボン反応をさらに抑制し、組織の損傷を抑制することができるマグネシア・カーボン質耐火物の製造方法を提供すること。【解決手段】 マグネシア・カーボン質耐火物の製造方法は、配合物を混錬、成形して成形体を得る成形工程と、成形体を非酸化雰囲気中８００〜１５００℃で焼成して焼成体を得る非酸化雰囲気焼成工程と、焼成体にコールタールピッチを含浸してマグネシア・カーボン質耐火物を得る含浸工程とを含み、配合物はマグネシア原料とカーボン原料とバインダーとを含み、マグネシア原料の１５〜３５質量％は粒径が０．３ｍｍ未満、残部は粒径が０．３ｍｍ以上であり、バインダーの添加量は、マグネシア原料とカーボン原料の合計含有量１００質量％に対して外掛０．５質量％以上３質量％未満であり、コールタールピッチの１８０℃における粘度が０．０６Ｐａ・ｓ以下である。【選択図】 なし
METHOD FOR PRODUCING MAGNESIA-CARBON REFRACTORY
To provide a method for producing a magnesia-carbon refractory in which a magnesia-carbon reaction is further suppressed by further densification of the magnesia-carbon refractory and a damage of a structure is suppressed.SOLUTION: A method for producing a magnesia-carbon refractory comprises: a molding step of kneading and molding a mixture to obtain a molded body; a non-oxidizing atmosphere firing step of firing the molded body at 800-1,500°C in a non-oxidizing atmosphere to obtain a sintered body; and an impregnation step of impregnating the sintered body with coal tar pitch to obtain a magnesia-carbon refractory. The mixture contains a magnesia raw material, a carbon raw material, and a binder. Particle size of 15-35 mass% of the magnesia raw material is less than 0.3 mm and the balance has a particle diameter of 0.3 mm or more. An amount of the added binder is 0.5 mass% or more and less than 3 mass% based on the total content of 100 mass% of the magnesia raw material and the carbon raw material. The viscosity of the coal tar pitch is 0.06 Pa s or less at 180°C.SELECTED DRAWING: None
【課題】 マグネシア・カーボン質耐火物のさらなる緻密化によりマグネシア・カーボン反応をさらに抑制し、組織の損傷を抑制することができるマグネシア・カーボン質耐火物の製造方法を提供すること。【解決手段】 マグネシア・カーボン質耐火物の製造方法は、配合物を混錬、成形して成形体を得る成形工程と、成形体を非酸化雰囲気中８００〜１５００℃で焼成して焼成体を得る非酸化雰囲気焼成工程と、焼成体にコールタールピッチを含浸してマグネシア・カーボン質耐火物を得る含浸工程とを含み、配合物はマグネシア原料とカーボン原料とバインダーとを含み、マグネシア原料の１５〜３５質量％は粒径が０．３ｍｍ未満、残部は粒径が０．３ｍｍ以上であり、バインダーの添加量は、マグネシア原料とカーボン原料の合計含有量１００質量％に対して外掛０．５質量％以上３質量％未満であり、コールタールピッチの１８０℃における粘度が０．０６Ｐａ・ｓ以下である。【選択図】 なし
METHOD FOR PRODUCING MAGNESIA-CARBON REFRACTORY
マグネシア・カーボン質耐火物の製造方法
KAKIHARA MASAYOSHI (author) / IIDA ATSUHISA (author) / SHIMADA TAKESHI (author)
2021-05-06
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
MAGNESIA CARBON REFRACTORY COMPOSITION AND METHOD FOR PRODUCING MAGNESIA CARBON BRICK
| European Patent Office | 2020
MAGNESIA-CARBON REFRACTORY AND PRODUCTION METHOD OF MAGNESIA-CARBON REFRACTORY
| European Patent Office | 2018
| European Patent Office | 2015