POROUS CERAMIC STRUCTURE AND MANUFACTURING METHOD OF POROUS CERAMIC STRUCTURE
To provide a porous ceramic structure having low pressure loss and high catalyst performance.SOLUTION: In the porous ceramic structure, the content of Fe in the case of containing Fe is, in Fe2O3 conversion, 0.1 mass% or larger and 3.0 mass% or smaller, and the content of Mn in the case of containing Mn is, in Mn2O3 conversion, 0.1 mass% or larger and 3.0 mass% or smaller. The content of Co when Fe or Mn and Co are contained is, in Co3O4 conversion, 0.1 mass% or larger and 3.0 mass% or smaller, and the content of Co in the case of not containing Fe and Mn but containing Co is, in Co3O4 conversion, 0.2 mass% or larger and 6.0 mass% or smaller. A content of Ce is, in CeO2 conversion, 0.1 mass% or larger and 10 mass% or smaller. A ratio of Fe/Mn/Co is 0.8 or larger and 9.5 or smaller. The content of metal oxide particles 2 is 0.3 mass% or larger and 8.0 mass% or smaller.SELECTED DRAWING: Figure 7
【課題】圧力損失が低く、高い触媒能を有する多孔質セラミック構造体を提供する。【解決手段】多孔質セラミック構造体において、Ｆｅが含まれる場合のＦｅの含有率は、Ｆｅ２Ｏ３換算で０．１質量％以上かつ３．０質量％以下であり、Ｍｎが含まれる場合のＭｎの含有率は、Ｍｎ２Ｏ３換算で０．１質量％以上かつ３．０質量％以下である。ＦｅまたはＭｎと共にＣｏが含まれる場合のＣｏの含有率は、Ｃｏ３Ｏ４換算で０．１質量％以上かつ３．０質量％以下であり、ＦｅおよびＭｎは含まれずＣｏが含まれる場合のＣｏの含有率は、Ｃｏ３Ｏ４換算で０．２質量％以上かつ６．０質量％以下である。Ｃｅの含有率は、ＣｅＯ２換算で０．１質量％以上かつ１０質量％以下である。Ｆｅ・Ｍｎ・Ｃｏ割合は、０．８以上かつ９．５以下である。金属酸化物粒子２の含有率は、０．３質量％以上かつ８．０質量％以下である。【選択図】図７
POROUS CERAMIC STRUCTURE AND MANUFACTURING METHOD OF POROUS CERAMIC STRUCTURE
To provide a porous ceramic structure having low pressure loss and high catalyst performance.SOLUTION: In the porous ceramic structure, the content of Fe in the case of containing Fe is, in Fe2O3 conversion, 0.1 mass% or larger and 3.0 mass% or smaller, and the content of Mn in the case of containing Mn is, in Mn2O3 conversion, 0.1 mass% or larger and 3.0 mass% or smaller. The content of Co when Fe or Mn and Co are contained is, in Co3O4 conversion, 0.1 mass% or larger and 3.0 mass% or smaller, and the content of Co in the case of not containing Fe and Mn but containing Co is, in Co3O4 conversion, 0.2 mass% or larger and 6.0 mass% or smaller. A content of Ce is, in CeO2 conversion, 0.1 mass% or larger and 10 mass% or smaller. A ratio of Fe/Mn/Co is 0.8 or larger and 9.5 or smaller. The content of metal oxide particles 2 is 0.3 mass% or larger and 8.0 mass% or smaller.SELECTED DRAWING: Figure 7
【課題】圧力損失が低く、高い触媒能を有する多孔質セラミック構造体を提供する。【解決手段】多孔質セラミック構造体において、Ｆｅが含まれる場合のＦｅの含有率は、Ｆｅ２Ｏ３換算で０．１質量％以上かつ３．０質量％以下であり、Ｍｎが含まれる場合のＭｎの含有率は、Ｍｎ２Ｏ３換算で０．１質量％以上かつ３．０質量％以下である。ＦｅまたはＭｎと共にＣｏが含まれる場合のＣｏの含有率は、Ｃｏ３Ｏ４換算で０．１質量％以上かつ３．０質量％以下であり、ＦｅおよびＭｎは含まれずＣｏが含まれる場合のＣｏの含有率は、Ｃｏ３Ｏ４換算で０．２質量％以上かつ６．０質量％以下である。Ｃｅの含有率は、ＣｅＯ２換算で０．１質量％以上かつ１０質量％以下である。Ｆｅ・Ｍｎ・Ｃｏ割合は、０．８以上かつ９．５以下である。金属酸化物粒子２の含有率は、０．３質量％以上かつ８．０質量％以下である。【選択図】図７
POROUS CERAMIC STRUCTURE AND MANUFACTURING METHOD OF POROUS CERAMIC STRUCTURE
多孔質セラミック構造体および多孔質セラミック構造体の製造方法
IZUMI YUNIE (author) / HIDAKA KENICHI (author) / MIURA AKIHIRO (author)
2021-10-07
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
B01J
Chemische oder physikalische Verfahren, z.B. Katalyse oder Kolloidchemie
,
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY
/
F01N
GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL
,
Schalldämpfer oder Auspuffvorrichtungen für Gase von Kraft- und Arbeitsmaschinen oder von Kraftmaschinen allgemein
POROUS CERAMIC STRUCTURE AND MANUFACTURING METHOD OF POROUS CERAMIC STRUCTURE
| European Patent Office | 2021