MANUFACTURING METHOD OF HYDRAULICALLY CURED OBJECT AND HYDRAULICALLY CURED OBJECT
To provide a manufacturing method of a hydraulically cured object which is excellent in salt penetration resistance and has a small shrinkage while using steam curing.SOLUTION: A manufacturing method of a hydraulically cured object comprises: a mixing step of mixing one or more Portland cements as a normal Portland cement or a high-early-strength Portland cement, metakaolin, silica fume, water, a chemical admixture and a fine aggregate to obtain a fresh hydraulic composition; and a curing step of performing steam curing for one hour or longer at a temperature of 40°C to 70°C to obtain the hydraulically cured object. In the mixing step, 70 to 95 pts.mass of the Portland cement, 3 to 20 pts.mass of the metakaolin and 2 to 15 pts.mass of the silica fume are used when the total use amount of the Portland cement, the metakaolin and the silica fume is 100 pts.mass.SELECTED DRAWING: Figure 1
【課題】蒸気養生を用いつつも、塩分浸透抵抗性に優れ、且つ収縮が小さい水硬性硬化体を製造する方法を提供する。【解決手段】この方法は、普通ポルトランドセメント又は早強ポルトランドセメントの１種以上のポルトランドセメント、メタカオリン、シリカフューム、水、化学混和剤、及び細骨材を混合して、フレッシュな水硬性組成物を得る混合工程と、フレッシュな水硬性組成物に対して４０℃～７０℃の温度で１時間以上の蒸気養生を行って水硬性硬化体を得る硬化工程とを有する。混合工程では、ポルトランドセメント、メタカオリン、シリカフュームの合計使用量を１００質量部とすると、７０質量部～９５質量部のポルトランドセメントと、３質量部～２０質量部のメタカオリンと、２質量部～１５質量部のシリカフュームが使用される。【選択図】図１
MANUFACTURING METHOD OF HYDRAULICALLY CURED OBJECT AND HYDRAULICALLY CURED OBJECT
To provide a manufacturing method of a hydraulically cured object which is excellent in salt penetration resistance and has a small shrinkage while using steam curing.SOLUTION: A manufacturing method of a hydraulically cured object comprises: a mixing step of mixing one or more Portland cements as a normal Portland cement or a high-early-strength Portland cement, metakaolin, silica fume, water, a chemical admixture and a fine aggregate to obtain a fresh hydraulic composition; and a curing step of performing steam curing for one hour or longer at a temperature of 40°C to 70°C to obtain the hydraulically cured object. In the mixing step, 70 to 95 pts.mass of the Portland cement, 3 to 20 pts.mass of the metakaolin and 2 to 15 pts.mass of the silica fume are used when the total use amount of the Portland cement, the metakaolin and the silica fume is 100 pts.mass.SELECTED DRAWING: Figure 1
【課題】蒸気養生を用いつつも、塩分浸透抵抗性に優れ、且つ収縮が小さい水硬性硬化体を製造する方法を提供する。【解決手段】この方法は、普通ポルトランドセメント又は早強ポルトランドセメントの１種以上のポルトランドセメント、メタカオリン、シリカフューム、水、化学混和剤、及び細骨材を混合して、フレッシュな水硬性組成物を得る混合工程と、フレッシュな水硬性組成物に対して４０℃～７０℃の温度で１時間以上の蒸気養生を行って水硬性硬化体を得る硬化工程とを有する。混合工程では、ポルトランドセメント、メタカオリン、シリカフュームの合計使用量を１００質量部とすると、７０質量部～９５質量部のポルトランドセメントと、３質量部～２０質量部のメタカオリンと、２質量部～１５質量部のシリカフュームが使用される。【選択図】図１
MANUFACTURING METHOD OF HYDRAULICALLY CURED OBJECT AND HYDRAULICALLY CURED OBJECT
水硬性硬化体の製造方法、水硬性硬化体
KURONO JOTARO (author) / YASUDA EIKI (author) / TATEIWA HANAE (author) / KONO KATSUYA (author)
2023-04-11
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME