CEMENT COMPOSITIONS, METHOD FOR MANUFACTURING CEMENT COMPOSITION, MORTAR COMPOSITION, AND CONCRETE COMPOSITION
To provide a cement composition that contains more than 5 mass% of limestone, capable of improving compressive strength of hardened bodies of not only a concrete composition but also a mortar composition, and exhibiting sufficiently low heat of hydration.SOLUTION: A cement composition includes a cement clinker, gypsum, and limestone. The limestone content is more than 5 mass% and 15 mass% or less. The cement composition has a Blaine specific surface area of 3,500 cm2/g or more and 4,000 cm2/g or less. In a particle size distribution of the cement composition, Rc calculated by the formula Rc=R35.1/(R10.9-R35.1) is 0.27 or more and 0.40 or less. The content of SO3 in the cement clinker is 0.3 mass% or more and 1.5 mass% or less. The degree of semi-hydration of gypsum is 25 mass% or more and 90 mass% or less. The apparent viscosity of the mortar composition containing the cement composition at a shear rate of 1 s-1 is 1 Pa_s or more and 8 Pa_s or less.SELECTED DRAWING: None
【課題】本開示は、５質量％を超える含有量の石灰石を含みながら、コンクリート組成物だけでなくモルタル組成物の硬化体の圧縮強さを改善でき、しかも十分に低い水和熱を示すセメント組成物に関する。【解決手段】セメントクリンカ、石膏、及び石灰石を含む、セメント組成物。石灰石の含有量が５質量％を超えて１５質量％以下である。セメント組成物が３５００ｃｍ２以上４０００ｃｍ２／ｇ以下のブレーン比表面積を有する。セメント組成物の粒度分布において、式：Ｒｃ＝Ｒ３５．１／（Ｒ１０．９－Ｒ３５．１）によって算出されるＲｃが０．２７以上０．４０以下である。セメントクリンカにおいてＳＯ３の含有量が０．３質量％以上１．５質量％以下である。石膏の半水化率が２５質量％以上９０質量％以下である。セメント組成物を含むモルタル組成物のせん断速度１ｓ－１における見かけ粘度が１Ｐａ・ｓ以上８Ｐａ・ｓ以下である。【選択図】なし
CEMENT COMPOSITIONS, METHOD FOR MANUFACTURING CEMENT COMPOSITION, MORTAR COMPOSITION, AND CONCRETE COMPOSITION
To provide a cement composition that contains more than 5 mass% of limestone, capable of improving compressive strength of hardened bodies of not only a concrete composition but also a mortar composition, and exhibiting sufficiently low heat of hydration.SOLUTION: A cement composition includes a cement clinker, gypsum, and limestone. The limestone content is more than 5 mass% and 15 mass% or less. The cement composition has a Blaine specific surface area of 3,500 cm2/g or more and 4,000 cm2/g or less. In a particle size distribution of the cement composition, Rc calculated by the formula Rc=R35.1/(R10.9-R35.1) is 0.27 or more and 0.40 or less. The content of SO3 in the cement clinker is 0.3 mass% or more and 1.5 mass% or less. The degree of semi-hydration of gypsum is 25 mass% or more and 90 mass% or less. The apparent viscosity of the mortar composition containing the cement composition at a shear rate of 1 s-1 is 1 Pa_s or more and 8 Pa_s or less.SELECTED DRAWING: None
【課題】本開示は、５質量％を超える含有量の石灰石を含みながら、コンクリート組成物だけでなくモルタル組成物の硬化体の圧縮強さを改善でき、しかも十分に低い水和熱を示すセメント組成物に関する。【解決手段】セメントクリンカ、石膏、及び石灰石を含む、セメント組成物。石灰石の含有量が５質量％を超えて１５質量％以下である。セメント組成物が３５００ｃｍ２以上４０００ｃｍ２／ｇ以下のブレーン比表面積を有する。セメント組成物の粒度分布において、式：Ｒｃ＝Ｒ３５．１／（Ｒ１０．９－Ｒ３５．１）によって算出されるＲｃが０．２７以上０．４０以下である。セメントクリンカにおいてＳＯ３の含有量が０．３質量％以上１．５質量％以下である。石膏の半水化率が２５質量％以上９０質量％以下である。セメント組成物を含むモルタル組成物のせん断速度１ｓ－１における見かけ粘度が１Ｐａ・ｓ以上８Ｐａ・ｓ以下である。【選択図】なし
CEMENT COMPOSITIONS, METHOD FOR MANUFACTURING CEMENT COMPOSITION, MORTAR COMPOSITION, AND CONCRETE COMPOSITION
セメント組成物、セメント組成物の製造方法、モルタル組成物、及びコンクリート組成物
GOTO TAKU (author) / YAMASHITA MAKIO (author) / OSAKI MASAFUMI (author)
2024-10-15
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2021
POLYMER CEMENT COMPOSITION, POLYMER CEMENT MORTAR COMPOSITION AND POLYMER CEMENT CONCRETE STRUCTURE
| European Patent Office | 2016
CEMENT COMPOSITION, CEMENT PASTE, CEMENT MORTAR AND CONCRETE MATERIAL
| European Patent Office | 2019
ULTRARAPID HARDENING CEMENT COMPOSITION, MORTAR COMPOSITION, AND CONCRETE COMPOSITION
| European Patent Office | 2019