The present invention comprises: step 1 of making collected clay into clay lumps with moisture content of 20-40%; step 2 of mixing the clay lumps, obtained in the step 1, with finely chopped vegetable fiber and bast fiber, adding fish glue or glue to the mixture, and knead the mixture to be equally mixed; step 3 of inputting the clay lumps, obtained in the step 2, into a drawer, drawing the clay lumps into a flat clay panel and cutting the panel by the specified standard unit; step 4 of pressing the clay panel, obtained in the step 3, with a press by heating the compressing surface of the press to a temperature of 400-500°C, heating the clay panel for 1-3 minutes, and pressing the clay panel until the thickness of the panel is reduced by 5-10%, taking the clay panel from the press, inputting the clay panel into a dryer and drying the clay panel for 2-3 minutes at room temperature; step 5 of immersing a woven member, made by weaving the vegetable fiber in a mesh net form, in glue, extracting the woven member from the glue, unfolding the woven member, and covering the woven member on the clay panel obtained in the step 4 to cover the overall surface of the clay panel; and step 6 of pressing the clay panel, obtained in the step 5, by heating the compressing surface of the press to a temperature of 400-500°C, heating the clay panel for 10-30 seconds, and pressing the clay panel until the thickness of the panel is reduced by 40-50%, taking the clay panel from the press, inputting the clay panel into the dryer and drying the clay panel for 1-2 minutes.
본 발명은 채취한 진흙을 함수율 20 ~ 40% 상태의 진흙덩어리로 만드는 단계 1; 상기 단계 1의 진흙 덩어리에 잘게 조각낸 식물성 섬유나 인피섬유를 혼합하고 부레풀이나 아교를 첨가하여 골고루 섞이도록 반죽하는 단계 2; 상기 단계 2의 진흙 덩어리를 인발기에 넣어 평평한 진흙 패널로 인발하여 특정된 규격단위로 재단하는 단계 3; 상기 단계 3의 진흙 패널을 프레스로 압착하되, 프레스 압착면의 온도를 400 ~ 500℃로 승온시킨 후 1 ~ 3분 동안 진흙 패널을 가열하면서 진흙 패널의 두께가 5 ~ 10% 줄어 들게 가압한 후 꺼내어 진흙 패널을 건조기에 집어넣고 상온에서 2 ~ 3분간 건조하는 단계 4; 상기 단계 4의 진흙패널 위에 진흙패널 전체를 덮을 수 있도록 식물성 섬유를 메시망 형태로 직조된 직조부재를 아교에 함침시켜 꺼내어 펴서 덮는 단계 5; 상기 단계 5의 진흙패널을 압착하되 프레스 압착면의 온도를 400 ~ 500℃로 승온시킨 후 진흙패널을 10 ~ 30초 동안 가열하면서 진흙패널의 두께가 40 ~ 50% 줄어들게 가압한 후 꺼내어 진흙패널을 건조기에 집어넣고 1 ~ 2분간 건조하는 단계 6;를 포함하여 이루어진 것을 특징으로 하는 진흙보드 제조방법에 관한 것이다.
The present invention comprises: step 1 of making collected clay into clay lumps with moisture content of 20-40%; step 2 of mixing the clay lumps, obtained in the step 1, with finely chopped vegetable fiber and bast fiber, adding fish glue or glue to the mixture, and knead the mixture to be equally mixed; step 3 of inputting the clay lumps, obtained in the step 2, into a drawer, drawing the clay lumps into a flat clay panel and cutting the panel by the specified standard unit; step 4 of pressing the clay panel, obtained in the step 3, with a press by heating the compressing surface of the press to a temperature of 400-500°C, heating the clay panel for 1-3 minutes, and pressing the clay panel until the thickness of the panel is reduced by 5-10%, taking the clay panel from the press, inputting the clay panel into a dryer and drying the clay panel for 2-3 minutes at room temperature; step 5 of immersing a woven member, made by weaving the vegetable fiber in a mesh net form, in glue, extracting the woven member from the glue, unfolding the woven member, and covering the woven member on the clay panel obtained in the step 4 to cover the overall surface of the clay panel; and step 6 of pressing the clay panel, obtained in the step 5, by heating the compressing surface of the press to a temperature of 400-500°C, heating the clay panel for 10-30 seconds, and pressing the clay panel until the thickness of the panel is reduced by 40-50%, taking the clay panel from the press, inputting the clay panel into the dryer and drying the clay panel for 1-2 minutes.
본 발명은 채취한 진흙을 함수율 20 ~ 40% 상태의 진흙덩어리로 만드는 단계 1; 상기 단계 1의 진흙 덩어리에 잘게 조각낸 식물성 섬유나 인피섬유를 혼합하고 부레풀이나 아교를 첨가하여 골고루 섞이도록 반죽하는 단계 2; 상기 단계 2의 진흙 덩어리를 인발기에 넣어 평평한 진흙 패널로 인발하여 특정된 규격단위로 재단하는 단계 3; 상기 단계 3의 진흙 패널을 프레스로 압착하되, 프레스 압착면의 온도를 400 ~ 500℃로 승온시킨 후 1 ~ 3분 동안 진흙 패널을 가열하면서 진흙 패널의 두께가 5 ~ 10% 줄어 들게 가압한 후 꺼내어 진흙 패널을 건조기에 집어넣고 상온에서 2 ~ 3분간 건조하는 단계 4; 상기 단계 4의 진흙패널 위에 진흙패널 전체를 덮을 수 있도록 식물성 섬유를 메시망 형태로 직조된 직조부재를 아교에 함침시켜 꺼내어 펴서 덮는 단계 5; 상기 단계 5의 진흙패널을 압착하되 프레스 압착면의 온도를 400 ~ 500℃로 승온시킨 후 진흙패널을 10 ~ 30초 동안 가열하면서 진흙패널의 두께가 40 ~ 50% 줄어들게 가압한 후 꺼내어 진흙패널을 건조기에 집어넣고 1 ~ 2분간 건조하는 단계 6;를 포함하여 이루어진 것을 특징으로 하는 진흙보드 제조방법에 관한 것이다.
MAKING METHOD OF MUDDY BOARD
진흙보드 제조방법
GIM YONG HYEON (author)
2015-12-24
Patent
Electronic Resource
Korean
| British Library Conference Proceedings | 1995
| Wiley | 2003
MUDDY WATER DIFFUSION RESTRAINT DEVICE AND MUDDY WATER DIFFUSION RESTRAINT METHOD
| European Patent Office | 2015
MUDDY WATER DIFFUSION SUPPRESSION DEVICE AND MUDDY WATER DIFFUSION SUPPRESSION METHOD
| European Patent Office | 2015