The present invention relates to a concrete composition for a PHC pile having the ultra high strength of compressive strength of 120 MPa or more and an ultra high strength PHC pile manufactured by using the same. In particular, the present invention relates to a technique which enhances manufacturing efficiency of PHC pile products by switching an material mixing order and applying a high strength additive including a solidification accelerating agent such as alpha-hemihydrate gypsum and alumina, and an admixture or the like improving dispersibility and viscosity, reduces a failure rate and shortens delivery lead time. According to the present invention, the concrete composition for the ultra high strength PHC pile is composed by including 110-170 kg/m^3 of water; 500-850 kg/m^3 of a bonding agent; 400-750 kg/m^3 of fine aggregate; and 900-1,400 kg/m^3 of coarse aggregate, wherein the bonding agent is composed of 65-90 wt% of cement and 10-35 wt% of a high strength admixture, and the cement is composed of 1-55 wt% of type 1 ordinary cement and 45-99 wt% of type 3 Portland cement, and the high strength additive is composed by including 40-55 wt% of calcium oxide (CaO, quicklime), 15-25 wt% of sulfur trioxide (SO_3), 5-10 wt% of alumina (Al_2O_3), and 5-10 wt% of alpha-hemihydrate gypsum (α-CaSO_4·1/2H_2O), and polycarboxylate-based high performance water reducing agent including amine-based surfactant and methylcellulose-based viscosity agent is added to the bonding agent by 1.5-2.5 wt% thereof.
본 발명은 압축강도 120MPa 이상의 초고강도가 발현되는 PHC 파일용 콘크리트 조성물 및 이를 이용하여 제조한 초고강도 PHC 파일에 관한 것으로서, 더욱 상세하게는 재료 혼합 순서의 변경, 알파반수석고, 알루미나 등 응결 촉진 성분을 포함하는 고강도 혼합재, 분산성 및 점성을 향상시키는 혼화제 등의 적용으로 PHC 파일 제품의 생산 효율을 높이고, 불량률을 낮추며, 출하기간을 단축시킬 수 있도록 한 기술에 관한 것이다. 본 발명은 『물 110~170㎏/㎥; 결합재 500~850㎏/㎥; 잔골재 400~750㎏/㎥; 및 굵은골재 900~1,400㎏/㎥; 를 포함하여 조성되고, 상기 결합재는 시멘트 65~90wt% 및 고강도 혼합재 10~35wt%로 조성되고, 상기 시멘트는 1종보통시멘트 1~55wt% 및 3종조강시멘트 45~99wt%로 조성되고, 상기 고강도 혼합재는 산화칼슘(CaO, 생석회) 40~55wt%, 삼산화황(SO) 15~25wt%, 알루미나(AlO) 5~10wt% 및 알파반수석고(α-CaSO·1/2HO) 5~10wt%를 포함하여 조성되며, 아민계 계면활성제 및 메틸-셀룰로오스계 증점제를 포함하는 폴리카르복실레이트계 고성능감수제가 상기 결합재의 1.5~2.5wt% 첨가된 것을 특징으로 하는 초고강도 PHC 파일용 콘크리트 조성물』을 제공한다.
The present invention relates to a concrete composition for a PHC pile having the ultra high strength of compressive strength of 120 MPa or more and an ultra high strength PHC pile manufactured by using the same. In particular, the present invention relates to a technique which enhances manufacturing efficiency of PHC pile products by switching an material mixing order and applying a high strength additive including a solidification accelerating agent such as alpha-hemihydrate gypsum and alumina, and an admixture or the like improving dispersibility and viscosity, reduces a failure rate and shortens delivery lead time. According to the present invention, the concrete composition for the ultra high strength PHC pile is composed by including 110-170 kg/m^3 of water; 500-850 kg/m^3 of a bonding agent; 400-750 kg/m^3 of fine aggregate; and 900-1,400 kg/m^3 of coarse aggregate, wherein the bonding agent is composed of 65-90 wt% of cement and 10-35 wt% of a high strength admixture, and the cement is composed of 1-55 wt% of type 1 ordinary cement and 45-99 wt% of type 3 Portland cement, and the high strength additive is composed by including 40-55 wt% of calcium oxide (CaO, quicklime), 15-25 wt% of sulfur trioxide (SO_3), 5-10 wt% of alumina (Al_2O_3), and 5-10 wt% of alpha-hemihydrate gypsum (α-CaSO_4·1/2H_2O), and polycarboxylate-based high performance water reducing agent including amine-based surfactant and methylcellulose-based viscosity agent is added to the bonding agent by 1.5-2.5 wt% thereof.
본 발명은 압축강도 120MPa 이상의 초고강도가 발현되는 PHC 파일용 콘크리트 조성물 및 이를 이용하여 제조한 초고강도 PHC 파일에 관한 것으로서, 더욱 상세하게는 재료 혼합 순서의 변경, 알파반수석고, 알루미나 등 응결 촉진 성분을 포함하는 고강도 혼합재, 분산성 및 점성을 향상시키는 혼화제 등의 적용으로 PHC 파일 제품의 생산 효율을 높이고, 불량률을 낮추며, 출하기간을 단축시킬 수 있도록 한 기술에 관한 것이다. 본 발명은 『물 110~170㎏/㎥; 결합재 500~850㎏/㎥; 잔골재 400~750㎏/㎥; 및 굵은골재 900~1,400㎏/㎥; 를 포함하여 조성되고, 상기 결합재는 시멘트 65~90wt% 및 고강도 혼합재 10~35wt%로 조성되고, 상기 시멘트는 1종보통시멘트 1~55wt% 및 3종조강시멘트 45~99wt%로 조성되고, 상기 고강도 혼합재는 산화칼슘(CaO, 생석회) 40~55wt%, 삼산화황(SO) 15~25wt%, 알루미나(AlO) 5~10wt% 및 알파반수석고(α-CaSO·1/2HO) 5~10wt%를 포함하여 조성되며, 아민계 계면활성제 및 메틸-셀룰로오스계 증점제를 포함하는 폴리카르복실레이트계 고성능감수제가 상기 결합재의 1.5~2.5wt% 첨가된 것을 특징으로 하는 초고강도 PHC 파일용 콘크리트 조성물』을 제공한다.
ULTRA HIGH STRENGTH PHC PILE
초고강도 ＰＨＣ 파일
YOUM HONG SUB (author)
2016-04-20
Patent
Electronic Resource
Korean
| European Patent Office | 2022
ULTRA HIGH STRENGTH PHC PILE USING ULTRA RAPID HARDING CEMENT
| European Patent Office | 2016
ULTRA-HIGH STRENGTH CONCRETE PILE PRODUCTION METHOD AND VIBRATOR
| European Patent Office | 2024