DURABILITY-IMPROVED ULTRA-QUICK-HARDENING CEMENT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
The present invention relates to an ultra-rapid hardening cement concrete composition with improved durability, and a pavement maintenance and repair method using the same. According to the present invention, the ultra-rapid hardening cement concrete composition comprises: 5 to 45 weight percent of an ultra-rapid hardening coupling agent; 15 to 75 weight percent of fine aggregates; 15 to 70 weight percent of coarse aggregates; 1 to 25 weight percent of a performance modifier; and 4 to 30 weight percent of water. The ultra-rapid hardening agent comprises: 5 to 79 weight percent of earl-strength Portland cement; 10 to 50 weight percent of calcium or magnesium sulfonate aluminate; 2 to 35 weight percent of blast furnace slag powder with a particle size of 3,000 to 9,000 cm^2/g; 1 to 30 weight percent of tricalcium aluminate; 1 to 30 weight percent of peat or turf; 1 to 20 weight percent of gypsum; 1 to 10 weight percent of kaolin; 1 to 10 weight percent of nitric kalmite; 1 to 10 weight percent of lithium carbonate; 1 to 10 weight percent of clinoptilolite; 0.5 to 5 weight percent of a deforming agent; and 0.5 to 5 weight percent of a water reducing agent. According to the present invention, the ultra-rapid hardening cement concrete composition promotes the densification of an inner tissue to form dense concrete, thereby providing an effect of improving strength and durability, in particular, waterproofness and corrosion of the concrete. Moreover, wear resistance is excellent to improve scaling resistance, thereby providing an effect of preventing deterioration of a surface of pavement. Moreover, provided are effects of preventing surface crack and expansion breakage caused by drying shrinkage, and providing a self-crack curing effect, which absorbs water and discharges the water again to fill a crack while existing inside the cured concrete in a reduced volume state.
본 발명은 내구성이 개선된 초속경성 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 유지 보수 공법에 관한 것이다. 이는 초속경성 결합재 5~45중량%, 잔골재 15~75중량%, 굵은골재 15~70중량%, 성능 개질제 1~25중량% 및 물 4~30 중량%를 포함하며, 상기 초속경성 결합재는 조강 포틀랜드 시멘트 5~79중량%, 칼슘 또는 마그네슘 설포알루미네이트 10~50중량%, 분말도가 3,000~9,000㎠/g인 고로슬래그 분말 2~35중량%, 트리칼슘알루미네이트 1~30중량%, 이토 또는 토탄 1~30중량%, 석고 1~20중량%, 카올린 1~10중량%, 아초산 칼마이트 1~10중량, 리튬카보네이트 1~10 중량%, 클리노프틸로라이트(clinoptilolite) 1~10중량%, 소포제 0.5~5중량% 및 감수제 0.5~5중량%를 포함한다. 본 발명에 따른 초속경성 시멘트 콘크리트 조성물은 내부 조직의 치밀화를 촉진하여 밀실한 콘크리트를 만들 수 있어 콘크리트의 강도 및 내구성, 특히 방수성, 내식성을 개선할 수 있으며, 내마모성이 우수하여 스케일링 저항성을 개선함으로 포장체 표면의 열화를 방지할 수 있는 효과를 가진다. 또한, 건조수축에 의한 표면균열 및 팽창파괴현상을 방지하는 효과를 발휘할 수 있는 효과를 얻을 수 있다. 또한, 굳은 콘크리트 내부에서 체적이 줄어든 상태로 존재하는 하다가 다시 물을 흡수하고 수분을 방출하면서 균열을 메우는 균열 자기 치유 효과를 얻을 수 있다.
DURABILITY-IMPROVED ULTRA-QUICK-HARDENING CEMENT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
The present invention relates to an ultra-rapid hardening cement concrete composition with improved durability, and a pavement maintenance and repair method using the same. According to the present invention, the ultra-rapid hardening cement concrete composition comprises: 5 to 45 weight percent of an ultra-rapid hardening coupling agent; 15 to 75 weight percent of fine aggregates; 15 to 70 weight percent of coarse aggregates; 1 to 25 weight percent of a performance modifier; and 4 to 30 weight percent of water. The ultra-rapid hardening agent comprises: 5 to 79 weight percent of earl-strength Portland cement; 10 to 50 weight percent of calcium or magnesium sulfonate aluminate; 2 to 35 weight percent of blast furnace slag powder with a particle size of 3,000 to 9,000 cm^2/g; 1 to 30 weight percent of tricalcium aluminate; 1 to 30 weight percent of peat or turf; 1 to 20 weight percent of gypsum; 1 to 10 weight percent of kaolin; 1 to 10 weight percent of nitric kalmite; 1 to 10 weight percent of lithium carbonate; 1 to 10 weight percent of clinoptilolite; 0.5 to 5 weight percent of a deforming agent; and 0.5 to 5 weight percent of a water reducing agent. According to the present invention, the ultra-rapid hardening cement concrete composition promotes the densification of an inner tissue to form dense concrete, thereby providing an effect of improving strength and durability, in particular, waterproofness and corrosion of the concrete. Moreover, wear resistance is excellent to improve scaling resistance, thereby providing an effect of preventing deterioration of a surface of pavement. Moreover, provided are effects of preventing surface crack and expansion breakage caused by drying shrinkage, and providing a self-crack curing effect, which absorbs water and discharges the water again to fill a crack while existing inside the cured concrete in a reduced volume state.
본 발명은 내구성이 개선된 초속경성 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 유지 보수 공법에 관한 것이다. 이는 초속경성 결합재 5~45중량%, 잔골재 15~75중량%, 굵은골재 15~70중량%, 성능 개질제 1~25중량% 및 물 4~30 중량%를 포함하며, 상기 초속경성 결합재는 조강 포틀랜드 시멘트 5~79중량%, 칼슘 또는 마그네슘 설포알루미네이트 10~50중량%, 분말도가 3,000~9,000㎠/g인 고로슬래그 분말 2~35중량%, 트리칼슘알루미네이트 1~30중량%, 이토 또는 토탄 1~30중량%, 석고 1~20중량%, 카올린 1~10중량%, 아초산 칼마이트 1~10중량, 리튬카보네이트 1~10 중량%, 클리노프틸로라이트(clinoptilolite) 1~10중량%, 소포제 0.5~5중량% 및 감수제 0.5~5중량%를 포함한다. 본 발명에 따른 초속경성 시멘트 콘크리트 조성물은 내부 조직의 치밀화를 촉진하여 밀실한 콘크리트를 만들 수 있어 콘크리트의 강도 및 내구성, 특히 방수성, 내식성을 개선할 수 있으며, 내마모성이 우수하여 스케일링 저항성을 개선함으로 포장체 표면의 열화를 방지할 수 있는 효과를 가진다. 또한, 건조수축에 의한 표면균열 및 팽창파괴현상을 방지하는 효과를 발휘할 수 있는 효과를 얻을 수 있다. 또한, 굳은 콘크리트 내부에서 체적이 줄어든 상태로 존재하는 하다가 다시 물을 흡수하고 수분을 방출하면서 균열을 메우는 균열 자기 치유 효과를 얻을 수 있다.
DURABILITY-IMPROVED ULTRA-QUICK-HARDENING CEMENT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
내구성이 개선된 초속경성 시멘트 콘크리트 조성물 및 이를 이용한 도로 포장 유지 보수 공법
KANG IN DONG (author)
2018-08-02
Patent
Electronic Resource
Korean
| European Patent Office | 2018
QUICK-HARDENING CEMENT CONCRETE COMPOSITION AND REPAIRING METHOD FOR ROAD PAVEMENT THEREWITH
| European Patent Office | 2018
| European Patent Office | 2019
| European Patent Office | 2019
| European Patent Office | 2021