CONCRETE REPAIRING MORTAR AND MANUFACTURING METHOD THEREOF
The present invention provides a mortar composition for concrete repairing, containing: 15-50 wt% of fluidized bed boiler ash; 10-40 wt% of cement; 2-6 wt% of silica hume; 2-6 wt% of blast furnace slag; 0.1-0.3 wt% of a fluidizing agent; 1-4 wt% of an expansion material; 0.01-0.15 wt% of a thickening agent; and 10-50 wt% of aggregate. The fluidized bed boiler ash is desired to have 9-17% of free-CaO based on the weight of ash because 0.18-0.22 part by weight of water is covered based on the weight of ash in order to lower the free-CaO ratio. If the fluidized bed boiler ash is mixed with the concrete composition, a free-CaO component causes problems such as an abnormal condensation phenomenon of the concrete composition, a slump loss, retarder usage increase, durability degradation, etc. Accordingly, in the present invention, water is sprayed on the fluidized bed ash to react the water with partial CaO, thereby reducing an amount of CaO. Therefore, the present invention reduces the content of the free-CaO included in ash to 9-17% to prevent problems such as the abnormal condensation phenomenon and the durability degradation of the concrete composition.
본 발명의 콘크리트 보수용 모르타르 조성물은 유동층보일러 애시 15~50 중량%; 시멘트 10~40 중량%: 실리카흄 2~6 중량%: 고로슬래그 2~6 중량%: 유동화제 0.1~0.3 중량%; 팽창재 1~4 중량%; 증점제 0.01~0.15 중량%; 골재 10~50 중량%;를 포함한다. 유동층보일러 애시는 Free-Cao의 비율을 낮추기 위해, 애시 중량을 기준으로, 0.18~0.22 중량부의 수분이 도포되어, Free-Cao의 비율이 애시 중량을 기준으로 9 ~ 17%인 것이 바람직하다. 유동층보일러 애시를 콘크리트 조성물에 혼합하게 되면 애시의 Frer-CaO 성분 때문에 콘크리트 조성물의 이상 응결현상, 슬럼프 손실, 진연제 사용량 증가, 내구성 저하 등의 문제가 발생한다. 이에 본 발명에서는 유동층보일러 애시에 물을 분사하여 일부 CaO를 물과 반응시켜 CaO의 량을 줄인다. 이로 인해, 애시 내에 포함된 Free-CaO의 함량을 9~17%로 감소되어 콘크리트 조성물의 이상응결현상과 내구성 저하 등의 문제를 방지한다.
CONCRETE REPAIRING MORTAR AND MANUFACTURING METHOD THEREOF
The present invention provides a mortar composition for concrete repairing, containing: 15-50 wt% of fluidized bed boiler ash; 10-40 wt% of cement; 2-6 wt% of silica hume; 2-6 wt% of blast furnace slag; 0.1-0.3 wt% of a fluidizing agent; 1-4 wt% of an expansion material; 0.01-0.15 wt% of a thickening agent; and 10-50 wt% of aggregate. The fluidized bed boiler ash is desired to have 9-17% of free-CaO based on the weight of ash because 0.18-0.22 part by weight of water is covered based on the weight of ash in order to lower the free-CaO ratio. If the fluidized bed boiler ash is mixed with the concrete composition, a free-CaO component causes problems such as an abnormal condensation phenomenon of the concrete composition, a slump loss, retarder usage increase, durability degradation, etc. Accordingly, in the present invention, water is sprayed on the fluidized bed ash to react the water with partial CaO, thereby reducing an amount of CaO. Therefore, the present invention reduces the content of the free-CaO included in ash to 9-17% to prevent problems such as the abnormal condensation phenomenon and the durability degradation of the concrete composition.
본 발명의 콘크리트 보수용 모르타르 조성물은 유동층보일러 애시 15~50 중량%; 시멘트 10~40 중량%: 실리카흄 2~6 중량%: 고로슬래그 2~6 중량%: 유동화제 0.1~0.3 중량%; 팽창재 1~4 중량%; 증점제 0.01~0.15 중량%; 골재 10~50 중량%;를 포함한다. 유동층보일러 애시는 Free-Cao의 비율을 낮추기 위해, 애시 중량을 기준으로, 0.18~0.22 중량부의 수분이 도포되어, Free-Cao의 비율이 애시 중량을 기준으로 9 ~ 17%인 것이 바람직하다. 유동층보일러 애시를 콘크리트 조성물에 혼합하게 되면 애시의 Frer-CaO 성분 때문에 콘크리트 조성물의 이상 응결현상, 슬럼프 손실, 진연제 사용량 증가, 내구성 저하 등의 문제가 발생한다. 이에 본 발명에서는 유동층보일러 애시에 물을 분사하여 일부 CaO를 물과 반응시켜 CaO의 량을 줄인다. 이로 인해, 애시 내에 포함된 Free-CaO의 함량을 9~17%로 감소되어 콘크리트 조성물의 이상응결현상과 내구성 저하 등의 문제를 방지한다.
CONCRETE REPAIRING MORTAR AND MANUFACTURING METHOD THEREOF
콘크리트 보수용 모르타르 조성물 및 그 제조방법
KANG YONG HAK (author) / LEE CHIN YONG (author)
2018-08-30
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Concrete structure repairing mortar and repairing method
| European Patent Office | 2018
European Patent Office | 2020
| European Patent Office | 2020
MORTAR COMPOSITION AND REPAIRING METHOD FOR CONCRETE STRUCTURE THEREOF
| European Patent Office | 2018