Manufacturing method for production temperature-reducing warm-mix modified asphalt mixture using reactive chemical modified-additives and modified asphalt mixture thereof
The present invention relates to a method of manufacturing production temperature reduction type reformed asphalt mixture by using reactive chemical reformed additives and a reformed asphalt mixture thereof. The method includes: a step (S1) of heating straight asphalt in an oven at a 95-105°C for 55-60 minutes, and then, measuring the asphalt in a beaker; a step (S2) of putting the measured beaker in a beaker-shaped mantle heater, and then, putting the mantle heater in a stirrer, and then, stirring the asphalt at 1800-2100 rpm; a step (S3) of making a straight asphalt mixture by adding a selected reactive chemical reformed additive; and a step (S4) of stirring the manufactured asphalt mixture, and then, cooling the mixture for 2.5-3.5 hours.
본 발명은 반응성 화학 개질첨가제를 사용한 생산온도저감형 개질아스팔트 혼합물 제조방법 및 그 개질아스팔트 혼합물에 관한 것으로 아스팔트 내 존재하는 아스팔텐의 수산화기와 반응이 가능하고, 중온 이상에서 유동성을 가지는 물질을 도입하여 생산온도저감 효과와 개질 효과를 부여하도록 하기 위하여, 침입도가 60∼80인 스트레이트 아스팔트를 95∼105℃의 내부온도를 갖는 오븐에서 55∼60분 동안 가열 후, 비커에 계량하는 단계(S1); 상기 S1단계를 통해 스트레이트 아스팔트가 계량된 비커를 비커형 맨틀히터에 넣고, 상기 맨틀히터를 교반기에 넣은 다음, 상기 교반기로 140∼150℃의 내부온도 상에서 1800∼2100rpm으로 교반하는 단계(S2); 상기 S2단계를 통해 교반된 스트레이트 아스팔트에 도데실-테트라데실 글리시딜 에테르(DTGE : Dodecyl and tetradecyl glycidyl ether), 폴리에틸렌 지 말레익 무수물(PE-g-MA : Polyethylene-g-maleic anhydride), 폴리프로필렌 지 말레익 무수물(PP-g-MA : Polypropylene-g-maleic anhydride)중 어느 하나 이상으로 선택된 반응성 화학 개질 첨가제를 투입하여 스트레이트 아스팔트 혼합물을 제조하는 단계(S3); 상기 S3단계를 통해 제조된 스트레이트 아스팔트 혼합물을 15∼20분 교반한 후 15∼25℃의 상온에서 2.5∼3.5시간 동안 냉각하는 단계(S4);를 포함하여 이루어지며, 상기 S3단계에서, 상기 스트레이트 아스팔트 100 중량부를 기준으로 도데실-테트라데실 글리시딜 에테르(DTGE : Dodecyl and tetradecyl glycidyl ether), 폴리에틸렌 지 말레익 무수물(PE-g-MA : Polyethylene-g-maleic anhydride), 폴리프로필렌 지 말레익 무수물(PP-g-MA : Polypropylene-g-maleic anhydride)중 어느 하나 이상으로 선택된 반응성 화학 개질 첨가제 1∼2 중량부를 투입하여 혼합되도록 구성하고, 상기 S3단계에서, 상기 스트레이트 아스팔트 100 중량부를 기준으로 스타이렌-부타디엔 고무(SBS), 스타디엔-에틸렌-부틸렌 블록 공중합 고무(SEBS), 폐타이어 고무(CRM), 이소프렌(IR), 염소고무(CR) 중 적어도 어느 하나 이상으로 선택된 고무폴리머 6∼7 중량부를 투입하여 혼합되도록 구성하며, 상기 고무폴리머는 스트레이트 아스팔트와의 혼화성, 작업성을 고려하여 평균입도가 0.3∼1.0㎜의 미세분말 형태로 형성되는 것을 특징으로 한다.
Manufacturing method for production temperature-reducing warm-mix modified asphalt mixture using reactive chemical modified-additives and modified asphalt mixture thereof
The present invention relates to a method of manufacturing production temperature reduction type reformed asphalt mixture by using reactive chemical reformed additives and a reformed asphalt mixture thereof. The method includes: a step (S1) of heating straight asphalt in an oven at a 95-105°C for 55-60 minutes, and then, measuring the asphalt in a beaker; a step (S2) of putting the measured beaker in a beaker-shaped mantle heater, and then, putting the mantle heater in a stirrer, and then, stirring the asphalt at 1800-2100 rpm; a step (S3) of making a straight asphalt mixture by adding a selected reactive chemical reformed additive; and a step (S4) of stirring the manufactured asphalt mixture, and then, cooling the mixture for 2.5-3.5 hours.
본 발명은 반응성 화학 개질첨가제를 사용한 생산온도저감형 개질아스팔트 혼합물 제조방법 및 그 개질아스팔트 혼합물에 관한 것으로 아스팔트 내 존재하는 아스팔텐의 수산화기와 반응이 가능하고, 중온 이상에서 유동성을 가지는 물질을 도입하여 생산온도저감 효과와 개질 효과를 부여하도록 하기 위하여, 침입도가 60∼80인 스트레이트 아스팔트를 95∼105℃의 내부온도를 갖는 오븐에서 55∼60분 동안 가열 후, 비커에 계량하는 단계(S1); 상기 S1단계를 통해 스트레이트 아스팔트가 계량된 비커를 비커형 맨틀히터에 넣고, 상기 맨틀히터를 교반기에 넣은 다음, 상기 교반기로 140∼150℃의 내부온도 상에서 1800∼2100rpm으로 교반하는 단계(S2); 상기 S2단계를 통해 교반된 스트레이트 아스팔트에 도데실-테트라데실 글리시딜 에테르(DTGE : Dodecyl and tetradecyl glycidyl ether), 폴리에틸렌 지 말레익 무수물(PE-g-MA : Polyethylene-g-maleic anhydride), 폴리프로필렌 지 말레익 무수물(PP-g-MA : Polypropylene-g-maleic anhydride)중 어느 하나 이상으로 선택된 반응성 화학 개질 첨가제를 투입하여 스트레이트 아스팔트 혼합물을 제조하는 단계(S3); 상기 S3단계를 통해 제조된 스트레이트 아스팔트 혼합물을 15∼20분 교반한 후 15∼25℃의 상온에서 2.5∼3.5시간 동안 냉각하는 단계(S4);를 포함하여 이루어지며, 상기 S3단계에서, 상기 스트레이트 아스팔트 100 중량부를 기준으로 도데실-테트라데실 글리시딜 에테르(DTGE : Dodecyl and tetradecyl glycidyl ether), 폴리에틸렌 지 말레익 무수물(PE-g-MA : Polyethylene-g-maleic anhydride), 폴리프로필렌 지 말레익 무수물(PP-g-MA : Polypropylene-g-maleic anhydride)중 어느 하나 이상으로 선택된 반응성 화학 개질 첨가제 1∼2 중량부를 투입하여 혼합되도록 구성하고, 상기 S3단계에서, 상기 스트레이트 아스팔트 100 중량부를 기준으로 스타이렌-부타디엔 고무(SBS), 스타디엔-에틸렌-부틸렌 블록 공중합 고무(SEBS), 폐타이어 고무(CRM), 이소프렌(IR), 염소고무(CR) 중 적어도 어느 하나 이상으로 선택된 고무폴리머 6∼7 중량부를 투입하여 혼합되도록 구성하며, 상기 고무폴리머는 스트레이트 아스팔트와의 혼화성, 작업성을 고려하여 평균입도가 0.3∼1.0㎜의 미세분말 형태로 형성되는 것을 특징으로 한다.
Manufacturing method for production temperature-reducing warm-mix modified asphalt mixture using reactive chemical modified-additives and modified asphalt mixture thereof
반응성 화학 개질첨가제를 사용한 생산온도저감형 개질아스팔트 혼합물 제조방법 및 그 개질아스팔트 혼합물
JO YOUNG JIN (author) / KIM MYUNG HA (author) / KIM MIN GYEONG (author) / KIM YOUNG GEUN (author) / JUN SOO YONG (author) / KIM JAE YEON (author) / NOH YOUNG JIN (author) / CHOI BYUNG WOOK (author) / YOON SEUNG JUN (author)
2018-10-23
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2018
MODIFIED ASPHALT COMPOSITION, MODIFIED ASPHALT MIXTURE AND PRODUCTION METHODS THEREOF
| European Patent Office | 2019
MODIFIED ASPHALT COMPOSITION AND MODIFIED ASPHALT MIXTURE
| European Patent Office | 2017