ENVIRONMENTALLY FRIENDLY POLYMER MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITHOUT PORTLAND CEMENT AND METHOD FOR REPAIRING CONCRETE STRUCTURE USING THE SAME
The present invention provides an eco-friendly polymer mortar composition for repairing a concrete structure without Portland concrete and a method for repairing a concrete structure using the same, which largely lowers manufacturing costs by using blast furnace slag, has rapid curing speed, enhances initial strength and long term strength, and minimizes generation of hexavalent chromium (Cr^6+), a harmful substance, by excluding Portland concrete. The eco-friendly polymer mortar composition for repairing a concrete structure without Portland concrete contains: 49-55 wt% of blast furnace slag cement; 0.05-0.2 wt% of fiber; 0.2-1.5 wt% of polymer; 0.02-0.1 wt% of a thickener; 0.05-0.2 wt% of a foaming agent; and 40-50 wt% of fine aggregate wherein the blast furnace cement contains the blast furnace as a maximum constituent with respect to weight and also contains hauyne, lime and anhydrous gypsum to be able to generate ettringite (3CaO·Al_2O_3·3CaSO_4·32H_2O) through hydration.
본 발명은 콘크리트 구조물 보수용 친환경 무시멘트 폴리머 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수방법으로서, 고로슬래그 사용으로 제조원가를 크게 낮추면서도 경화가 빠르고 초기 강도 및 장기 강도가 높으며, 포틀랜드 시멘트를 배제하여 유해물질인 6가 크롬(Cr)의 발생을 극소화한 것이다. 이러한 본 발명의 콘크리트 구조물 보수용 친환경 무시멘트 폴리머 모르타르 조성물은, 고로슬래그 시멘트 49~55중량%, 섬유 0.05~0.2중량%, 폴리머 0.2~1.5중량%, 증점제 0.02~0.1중량%, 기포제 0.05~0.2중량% 및 잔골재 40~50중량%를 포함하되, 상기 고로슬래그 시멘트는 중량 기준으로 고로슬래그를 최대 성분으로 포함하고, 수화반응을 통하여 에트린자이트(3CaO·AlO·3CaSO·32HO)를 생성할 수 있도록 아우인, 석회, 무수석고를 더 포함하는 것을 특징으로 한다.
ENVIRONMENTALLY FRIENDLY POLYMER MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITHOUT PORTLAND CEMENT AND METHOD FOR REPAIRING CONCRETE STRUCTURE USING THE SAME
The present invention provides an eco-friendly polymer mortar composition for repairing a concrete structure without Portland concrete and a method for repairing a concrete structure using the same, which largely lowers manufacturing costs by using blast furnace slag, has rapid curing speed, enhances initial strength and long term strength, and minimizes generation of hexavalent chromium (Cr^6+), a harmful substance, by excluding Portland concrete. The eco-friendly polymer mortar composition for repairing a concrete structure without Portland concrete contains: 49-55 wt% of blast furnace slag cement; 0.05-0.2 wt% of fiber; 0.2-1.5 wt% of polymer; 0.02-0.1 wt% of a thickener; 0.05-0.2 wt% of a foaming agent; and 40-50 wt% of fine aggregate wherein the blast furnace cement contains the blast furnace as a maximum constituent with respect to weight and also contains hauyne, lime and anhydrous gypsum to be able to generate ettringite (3CaO·Al_2O_3·3CaSO_4·32H_2O) through hydration.
본 발명은 콘크리트 구조물 보수용 친환경 무시멘트 폴리머 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수방법으로서, 고로슬래그 사용으로 제조원가를 크게 낮추면서도 경화가 빠르고 초기 강도 및 장기 강도가 높으며, 포틀랜드 시멘트를 배제하여 유해물질인 6가 크롬(Cr)의 발생을 극소화한 것이다. 이러한 본 발명의 콘크리트 구조물 보수용 친환경 무시멘트 폴리머 모르타르 조성물은, 고로슬래그 시멘트 49~55중량%, 섬유 0.05~0.2중량%, 폴리머 0.2~1.5중량%, 증점제 0.02~0.1중량%, 기포제 0.05~0.2중량% 및 잔골재 40~50중량%를 포함하되, 상기 고로슬래그 시멘트는 중량 기준으로 고로슬래그를 최대 성분으로 포함하고, 수화반응을 통하여 에트린자이트(3CaO·AlO·3CaSO·32HO)를 생성할 수 있도록 아우인, 석회, 무수석고를 더 포함하는 것을 특징으로 한다.
ENVIRONMENTALLY FRIENDLY POLYMER MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITHOUT PORTLAND CEMENT AND METHOD FOR REPAIRING CONCRETE STRUCTURE USING THE SAME
콘크리트 구조물 보수용 친환경 무시멘트 폴리머 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수방법
PAIK TAI YOON (author) / PAIK NAM JOON (author)
2019-01-29
Patent
Electronic Resource
Korean
| European Patent Office | 2018
European Patent Office | 2021
| European Patent Office | 2018
| European Patent Office | 2018