The present invention relates to a crack reduction type rapid hardening cement concrete composition including a functional binding material, and to a road pavement repairing method using the same, capable of improving workability and constructability of concrete by using a binding material, improving toughness and bonding strength of the concrete, preventing shrinkage cracks by reducing shrinkage, and improving durability. In addition, the cement concrete composition including a functional binding material, and the road pavement repairing method using the same can accelerate hydration and densification of internal tissues in order to dense concrete, thus, can improve strength, durability, in particular, waterproofness, and corrosion resistance of the concrete, can prevent a surface crack and an expansion destruction phenomenon due to dry shrinkage, and can satisfy all of watertightness, adhesiveness, durability, and crack resistance which are required for pavement. In particular, the binding material in the present invention includes an inorganic latent heat material and an organic latent heat material by considering the characteristics of a latent heat material. Here, the inorganic latent heat material has an advantage of generally having high latent heat and thermal conductivity, but has a disadvantage of generating a phase separation phenomenon while the organic latent heat material has an advantage of generating less phase separation phenomenon than the inorganic latent heat material and thus, having a long service life, but has a disadvantage of having an expensive price. However, the provided concrete and a placing method thereof apply an optimum eutectic mixture to the concrete composition according to a proper composition ratio of an organic material and an inorganic material, thus, can shorten curing time of concrete and minimize the number of internal defects in a concrete structure, thereby having excellent durability and strength. In addition, the composition is composed of: 100 parts by weight of water; 800-1,250 parts by weight of fine aggregate; 700-840 parts by weight of coarse aggregate; 70-150 parts by weight of a latex synthetic polymer; 5-12 parts by weight of lithium carbonate; and 1-5 parts by weight of anhydrous citric acid.

본 발명은 기능성 결합재를 함유하는 균열 저감형 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로포장 보수공법에 관한 것으로서, 상기 결합재를 사용함으로써 콘크리트의 작업성 및 시공성을 향상시킬 수 있고, 콘크리트의 인성 및 부착강도를 개선하며, 수축을 저감시켜 수축 균열을 방지하고 내구성을 개선시킨다. 또한, 수화 및 내부 조직의 치밀화를 촉진하여 밀실한 콘크리트를 만들 수 있어 콘크리트의 강도 및 내구성, 특히 방수성, 내식성을 개선할 수 있고, 건조수축에 의한 표면균열 및 팽창파괴현상을 방지하며, 포장에 요구되는 제반 특성, 즉 수밀성, 부착성, 내구성 및 균열 저항성 등을 모두 만족할 수 있다. 특히 본 발명에서는 잠열재의 특성을 고려하여 무기계 잠열재와 유기계 잠열재를 결합재에 포함하는데, 무기계 잠열재는 일반적으로 잠열과 열전도도가 높다는 장점이 있으나 상분리 현상이 발생하며 단점을 가지고 있고 이에 반해 유기계 잠열재는 무기잠열재에 비해 상분리현상이 적어 그 수명이 길다는 장점이 있으나, 가격면에서는 비싸다는 단점이 있지만, 본 발명에서는 유기계 소재나 무기계 소재를 적절한 조성비에 따라 최적의 공융혼합물을 콘트리트 조성물에 적용하여 콘트리트의 양생시간을 단축시키고 콘크리트 구조물의 내부결함을 최소화시켜 내구성 및 강도기 우수한 콘크리트 및 이의 타설방법을 제공한다.