Surface reinforcement and repair method of waterway concrete structures
The present invention relates to a method for reinforcing and repairing the surface of a waterway concrete structures. The method comprises: a construction pretreatment step of removing foreign substances and attachments attached to the surfaces of concrete and a concrete structure, washing the same, and spraying a rust remover on the surfaces of the washed concrete and concrete structure; a sphere reinforcement application step of applying a sphere reinforcement to the surfaces of the concrete and the concrete structure; a repair mortar construction step of applying super-velocity repair mortar while maintaining the surface temperature of the concrete and the concrete structure at 23 to 35℃, and curing the same for 6 hours; a penetration waterproofing agent application step of applying a penetration waterproofing agent to the surface of the super-velocity repair mortar that has been cured, but mixing 4.1Kg of the penetration waterproofing agent per 1 liter of water, applying the mixture, and drying the mixture for a period of time; a mortar and panel member construction step of applying mixed mortar, in which cement, sand, and water are mixed at a ratio of 1:3:1 by weight, to the surface of the penetration waterproofing agent to have a thickness of 2 to 4 cm, and compressing a repair panel formed as 2.3 tons of a galvanized panel against the surfaces of the concrete and the concrete structure before curing the mixed mortar; and a finishing step of applying modified silicone to the circumferential surface of the repair panel and the construction site of an anchor bolt. Therefore, the time and cost required for reinforcement and repair of the concrete structure can be significantly reduced.
본 발명은 콘크리트 및 콘크리트 구조물의 표면에 부착된 이물질 및 부착물을 제거한 후, 세척하고, 세척된 상기 콘크리트 및 콘크리트 구조물의 표면에 녹 제거제를 분사하는 시공 전처리 단계; 상기 콘크리트 및 콘크리트 구조물의 표면에 구체 강화제를 도포하는 구체 강화제 도포 단계; 상기 콘크리트 및 콘크리트 구조물의 표면 온도를 23℃ ~ 35℃로 유지시키면서 초속경 보수몰탈을 도포한 후, 6시간 동안 양생시키는 보수몰탈 시공단계; 침투 방수제를 양생이 완료된 초속경 보수몰탈의 표면으로 도포하되, 물 1ℓ당 상기 침투 방수제 4.1Kg 을 혼합하여 도포한 다음, 일정 시간 동안 건조시키는 침투 방수제 도포단계; 시멘트, 모래 및 물이 각각 중량비로 1:3:1의 비율로 혼합된 혼합몰탈을 상기 침투 방수제의 표면으로 2cm ~ 4cm의 두께를 이루도록 도포하고, 상기 혼합몰탈의 양생이 이루어지기 전, 상기 콘크리트 및 콘크리트 구조물의 표면으로 2.3t의 아연도금패널로 이루어지는 보수패널을 압착시키는 몰탈 및 패널부재 시공단계; 및 변성 실리콘을 상기 보수패널의 둘레면과 앙카볼트의 시공 부위에 도포하는 마감단계;를 포함하는 것을 특징으로 한다.
Surface reinforcement and repair method of waterway concrete structures
The present invention relates to a method for reinforcing and repairing the surface of a waterway concrete structures. The method comprises: a construction pretreatment step of removing foreign substances and attachments attached to the surfaces of concrete and a concrete structure, washing the same, and spraying a rust remover on the surfaces of the washed concrete and concrete structure; a sphere reinforcement application step of applying a sphere reinforcement to the surfaces of the concrete and the concrete structure; a repair mortar construction step of applying super-velocity repair mortar while maintaining the surface temperature of the concrete and the concrete structure at 23 to 35℃, and curing the same for 6 hours; a penetration waterproofing agent application step of applying a penetration waterproofing agent to the surface of the super-velocity repair mortar that has been cured, but mixing 4.1Kg of the penetration waterproofing agent per 1 liter of water, applying the mixture, and drying the mixture for a period of time; a mortar and panel member construction step of applying mixed mortar, in which cement, sand, and water are mixed at a ratio of 1:3:1 by weight, to the surface of the penetration waterproofing agent to have a thickness of 2 to 4 cm, and compressing a repair panel formed as 2.3 tons of a galvanized panel against the surfaces of the concrete and the concrete structure before curing the mixed mortar; and a finishing step of applying modified silicone to the circumferential surface of the repair panel and the construction site of an anchor bolt. Therefore, the time and cost required for reinforcement and repair of the concrete structure can be significantly reduced.
본 발명은 콘크리트 및 콘크리트 구조물의 표면에 부착된 이물질 및 부착물을 제거한 후, 세척하고, 세척된 상기 콘크리트 및 콘크리트 구조물의 표면에 녹 제거제를 분사하는 시공 전처리 단계; 상기 콘크리트 및 콘크리트 구조물의 표면에 구체 강화제를 도포하는 구체 강화제 도포 단계; 상기 콘크리트 및 콘크리트 구조물의 표면 온도를 23℃ ~ 35℃로 유지시키면서 초속경 보수몰탈을 도포한 후, 6시간 동안 양생시키는 보수몰탈 시공단계; 침투 방수제를 양생이 완료된 초속경 보수몰탈의 표면으로 도포하되, 물 1ℓ당 상기 침투 방수제 4.1Kg 을 혼합하여 도포한 다음, 일정 시간 동안 건조시키는 침투 방수제 도포단계; 시멘트, 모래 및 물이 각각 중량비로 1:3:1의 비율로 혼합된 혼합몰탈을 상기 침투 방수제의 표면으로 2cm ~ 4cm의 두께를 이루도록 도포하고, 상기 혼합몰탈의 양생이 이루어지기 전, 상기 콘크리트 및 콘크리트 구조물의 표면으로 2.3t의 아연도금패널로 이루어지는 보수패널을 압착시키는 몰탈 및 패널부재 시공단계; 및 변성 실리콘을 상기 보수패널의 둘레면과 앙카볼트의 시공 부위에 도포하는 마감단계;를 포함하는 것을 특징으로 한다.
Surface reinforcement and repair method of waterway concrete structures
수로용 콘크리트 구조물의 표면 보강 및 보수 방법
NA YOUNG SU (author) / KIM YU JEONG (author)
2021-08-09
Patent
Electronic Resource