The present invention relates to silicon carbide (SiC) ceramics with improved machinability, which are formed by sintering a mixture of SiC powder, a sintering binder, and a sintering aid, wherein the sintering aid is Al_2TiO_5 acting in an amorphous phase, and the mixture is sintered at a temperature ranging from 1700 to 1900 deg. C. According to the present invention, the SiC ceramics having an excellent sintered state and improved machinability can be provided by performing a sintering process after adding Al_2TiO_5 in process of compounding raw materials. In addition, since mixing Al_2TiO_5 improves the sinterability of the SiC ceramics of the present invention, the sintering process is performed without pressurization at a relatively low temperature when compared to an existing sintering process, thereby reducing production costs. Moreover, since the silicon carbide ceramics of the present invention have improved machinability and may be processed by machining such as drilling, etc., the silicon carbide ceramics can be processed in various shapes and applied to various fields.
본 발명은 기계 가공성이 향상된 탄화규소 세라믹에 관한 것으로, SiC 분말과 소결용 바인더 및 소결조제를 혼합하여 소결된 것으로서, 상기 소결조제가 AlTiO이며, 1700~1900℃의 온도 범위에서 소결되어 상기 AlTiO가 비정질 상태의 소결조제로서 작용한 것을 특징으로 한다. 본 발명은 원료 합성 과정에서 AlTiO를 첨가한 뒤에 소결공정을 수행함으로써, 소결 상태가 뛰어나고 기계가공성이 향상된 SiC 세라믹을 제공할 수 있는 효과가 있다. 또한, 본 발명의 SiC 세라믹은 AlTiO를 혼합하여 소결성을 높임으로써, 종래의 소결 공정에 비하여 낮은 온도에서 무가압으로 소결공정을 수행하여 제조되기 때문에 낮은 제조 비용으로 제조할 수 있는 효과가 있다. 나아가 본 발명에 의한 탄화규소 세라믹은 기계 가공성이 향상되어 드릴링 등의 가공을 통해서 가공이 가능하므로, 탄화규소 세라믹을 다양한 형상으로 가공하여 다양한 분야에 적용할 수 있는 뛰어난 효과가 있다.
The present invention relates to silicon carbide (SiC) ceramics with improved machinability, which are formed by sintering a mixture of SiC powder, a sintering binder, and a sintering aid, wherein the sintering aid is Al_2TiO_5 acting in an amorphous phase, and the mixture is sintered at a temperature ranging from 1700 to 1900 deg. C. According to the present invention, the SiC ceramics having an excellent sintered state and improved machinability can be provided by performing a sintering process after adding Al_2TiO_5 in process of compounding raw materials. In addition, since mixing Al_2TiO_5 improves the sinterability of the SiC ceramics of the present invention, the sintering process is performed without pressurization at a relatively low temperature when compared to an existing sintering process, thereby reducing production costs. Moreover, since the silicon carbide ceramics of the present invention have improved machinability and may be processed by machining such as drilling, etc., the silicon carbide ceramics can be processed in various shapes and applied to various fields.
본 발명은 기계 가공성이 향상된 탄화규소 세라믹에 관한 것으로, SiC 분말과 소결용 바인더 및 소결조제를 혼합하여 소결된 것으로서, 상기 소결조제가 AlTiO이며, 1700~1900℃의 온도 범위에서 소결되어 상기 AlTiO가 비정질 상태의 소결조제로서 작용한 것을 특징으로 한다. 본 발명은 원료 합성 과정에서 AlTiO를 첨가한 뒤에 소결공정을 수행함으로써, 소결 상태가 뛰어나고 기계가공성이 향상된 SiC 세라믹을 제공할 수 있는 효과가 있다. 또한, 본 발명의 SiC 세라믹은 AlTiO를 혼합하여 소결성을 높임으로써, 종래의 소결 공정에 비하여 낮은 온도에서 무가압으로 소결공정을 수행하여 제조되기 때문에 낮은 제조 비용으로 제조할 수 있는 효과가 있다. 나아가 본 발명에 의한 탄화규소 세라믹은 기계 가공성이 향상되어 드릴링 등의 가공을 통해서 가공이 가능하므로, 탄화규소 세라믹을 다양한 형상으로 가공하여 다양한 분야에 적용할 수 있는 뛰어난 효과가 있다.
MACHINABLE SIC CERAMICS
기계 가공성이 향상된 탄화규소 세라믹
KIM IL SOO (author)
2015-10-14
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Machinable calcium pyrophosphate glass-ceramics
| British Library Online Contents | 2001
Study of Machinable Dental Glass Ceramics
| British Library Online Contents | 2009
Graded Machinable Ceramics: Concept and Practice
| British Library Online Contents | 2003
Low Melting Temperature Machinable Glass Ceramics
| British Library Online Contents | 2003
Machinable glass ceramics containing calcium pyrophosphate crystal
| British Library Online Contents | 2004