PLASTERING COMPOSITION FOR ARCHITECTURE USING OYSTER SHELL POWDER
The present invention relates to a plastering composition for architecture in which oyster shell powder is mixed with cement instead of sand. Provided is a plastering composition for architecture, which comprises cement in which Portland cement and slug cement are mixed at a weight ratio of 1.1 to 1.2, and oyster shell powder obtained by removing impurities from collected oyster shells, and washing, dehydrating and drying the collected oyster shells, and pulverizing the same to pass through a net of 0.5-1.5 mm, at a weight ratio of 1:1.5-1:3. The plastering composition of the present invention contains a large amount of oyster shell powder, and thus has excellent thermal insulation, and superior thermal and cold protection effects, has high bond strength, has less crack generation due to excellent fine crack resistance and impact resistance, maintains the plastering state for a long period of time due to superior wear resistance, and has less condensation due to excellent resistance to hot and cold repeated actions, thereby preventing the generation of molds. Moreover, the plastering composition of the present invention provides economic efficiency at low production cost, has consumption compared to the weight ratio, i.e. construction area, greatly increased to 1.3-1.5 times as the weight thereof becomes lighter, and can be easily carried.
본 발명은 모래 대신 굴 껍질 분말을 시멘트와 혼합한 건축용 미장 조성물에 관한 것으로, 본 발명에서는 포틀랜드 시멘트와 슬러그 시멘트를 1:1 내지 1:2의 중량비로 혼합한 시멘트와 수거된 굴 껍질을 불순물 제거, 세척, 탈수, 건조 및 살균처리를 한 후 0.5~1.5mm 체를 통과하도록 분쇄하여 얻은 굴 껍질 분말을 1:1.5 내지 1:3의 중량비로 포함하는 건축용 미장 조성물이 제공된다. 본 발명의 미장 조성물은 굴 껍질 분말이 다량 포함됨에 따라 단열성이 우수하여 보온 및 방한효과가 우수하고, 부착강도가 높으며, 내잔갈림성이나 내충격성이 우수하여 크랙의 발생이 적으며, 내마모성이 우수하여 미장상태의 유지가 오래 지속되며, 온냉반복작용에 대한 저항성이 우수하여 결로현상이 적으므로 곰팡이균의 발생을 억제하는 효과가 있다. 또한, 본 발명의 미장 조성물은 낮은 생산비용으로 경제성이 있으며, 중량이 가벼워져 중량 대비 사용량, 즉 시공면적이 1.3~1.5배 이상으로 크게 늘어나고, 운반이 용이하다는 장점이 있다.
PLASTERING COMPOSITION FOR ARCHITECTURE USING OYSTER SHELL POWDER
The present invention relates to a plastering composition for architecture in which oyster shell powder is mixed with cement instead of sand. Provided is a plastering composition for architecture, which comprises cement in which Portland cement and slug cement are mixed at a weight ratio of 1.1 to 1.2, and oyster shell powder obtained by removing impurities from collected oyster shells, and washing, dehydrating and drying the collected oyster shells, and pulverizing the same to pass through a net of 0.5-1.5 mm, at a weight ratio of 1:1.5-1:3. The plastering composition of the present invention contains a large amount of oyster shell powder, and thus has excellent thermal insulation, and superior thermal and cold protection effects, has high bond strength, has less crack generation due to excellent fine crack resistance and impact resistance, maintains the plastering state for a long period of time due to superior wear resistance, and has less condensation due to excellent resistance to hot and cold repeated actions, thereby preventing the generation of molds. Moreover, the plastering composition of the present invention provides economic efficiency at low production cost, has consumption compared to the weight ratio, i.e. construction area, greatly increased to 1.3-1.5 times as the weight thereof becomes lighter, and can be easily carried.
본 발명은 모래 대신 굴 껍질 분말을 시멘트와 혼합한 건축용 미장 조성물에 관한 것으로, 본 발명에서는 포틀랜드 시멘트와 슬러그 시멘트를 1:1 내지 1:2의 중량비로 혼합한 시멘트와 수거된 굴 껍질을 불순물 제거, 세척, 탈수, 건조 및 살균처리를 한 후 0.5~1.5mm 체를 통과하도록 분쇄하여 얻은 굴 껍질 분말을 1:1.5 내지 1:3의 중량비로 포함하는 건축용 미장 조성물이 제공된다. 본 발명의 미장 조성물은 굴 껍질 분말이 다량 포함됨에 따라 단열성이 우수하여 보온 및 방한효과가 우수하고, 부착강도가 높으며, 내잔갈림성이나 내충격성이 우수하여 크랙의 발생이 적으며, 내마모성이 우수하여 미장상태의 유지가 오래 지속되며, 온냉반복작용에 대한 저항성이 우수하여 결로현상이 적으므로 곰팡이균의 발생을 억제하는 효과가 있다. 또한, 본 발명의 미장 조성물은 낮은 생산비용으로 경제성이 있으며, 중량이 가벼워져 중량 대비 사용량, 즉 시공면적이 1.3~1.5배 이상으로 크게 늘어나고, 운반이 용이하다는 장점이 있다.
PLASTERING COMPOSITION FOR ARCHITECTURE USING OYSTER SHELL POWDER
굴 껍질 분말을 이용한 건축용 미장 조성물
KIM DO GYUN (author)
2016-02-24
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Plastering Composition for architecture using oyster shell powder
European Patent Office | 2016
CEMENT COMPOSITION FOR PLASTERING AND MORTAR FOR PLASTERING
| European Patent Office | 2020