Hoeryeong glaze and method for preparing of hoeryeong glaze white porcelain using the same
Disclosed are Hoeryeong glaze and a manufacturing method of Hoeryeong white porcelain using the same. The manufacturing method of Hoeryeong white porcelain uses Hoeryeong glaze which imparts an exclusive color to porcelain and does not crack after being applied to the porcelain, and thus can maintain the cleanliness and exclusivity of white porcelain. The manufacturing method of Hoeryeong white porcelain using the Hoeryeong glaze comprises the following steps: forming a body in a predetermined shape using white clay as base clay, and firstly firing the formed body in a Korean traditional firewood kiln at a temperature of 800-900 deg. C; depositing first sediment after mixing water and ash obtained by burning a raw material which contains a great quantity of siliceous ingredients and is selected from a group consisting of bean pods, straw, bamboo, thatch, and chaff, depositing second sediment after mixing water and feldspar-containing soil or powdered feldspar, depositing third sediment after mixing water and ash obtained by burning pine, and mixing 30-45 wt% of the first sediment, 25-35 wt% of the second sediment, and 25-40 wt% of the third sediment to manufacture Hoeryeong glaze separately from the step of firstly firing the white clay body; soaking the firstly fired white clay body in the Hoeryeong glaze to apply the Hoeryeong glaze to the firstly fired white clay body; and secondly firing the white clay body coated with the Hoeryeong glaze in a Korean traditional firewood kiln at a temperature of 1,300 deg. C or higher for at least two hours.
자기(瓷器)의 색감을 고급스럽게 하고, 도포 후 균열이 발생하지 않는 회령 유약을 사용함으로써, 백자의 청결함 및 고급스러움을 유지할 수 있는 회령 유약 및 이를 이용한 회유백자의 제조방법이 개시된다. 상기 회령 유약을 이용한 회유백자의 제조방법은, 태토인 백자토를 이용하여 일정한 형상으로 성형한 소지를 800 내지 900 ℃ 온도의 전통장작가마에서 초벌구이 하는 단계; 상기 백자토 소지를 초벌구이 하는 것과는 별개로, 30 내지 45 중량%의 규산질 성분이 다량 함유되어 있는 콩깍지, 지푸라기, 대나무, 억새풀 및 왕겨로 이루어진 군으로부터 선택되는 원료를 태운 재를 물과 혼합시킨 후 침전된 앙금, 25 내지 35 중량%의 장석 성분이 포함된 흙 또는 분말 형태의 장석을 물과 혼합시킨 후 침전된 앙금 및 25 내지 40 중량%의 소나무를 태운 재를 물과 혼합시킨 후 침전된 앙금을 혼합하여 회령 유약을 제조하는 단계; 상기 초벌구이 된 백자토 소지를 상기 유약에 침지시켜, 상기 초벌구이 된 백자토 소지에 유약을 도포하는 단계; 및 상기 유약이 도포된 백자토 소지를 1,300 ℃ 이상의 온도에서 2 시간 이상 동안 전통장작가마에서 환원 소성으로 재벌구이 하는 단계를 포함한다.
Hoeryeong glaze and method for preparing of hoeryeong glaze white porcelain using the same
Disclosed are Hoeryeong glaze and a manufacturing method of Hoeryeong white porcelain using the same. The manufacturing method of Hoeryeong white porcelain uses Hoeryeong glaze which imparts an exclusive color to porcelain and does not crack after being applied to the porcelain, and thus can maintain the cleanliness and exclusivity of white porcelain. The manufacturing method of Hoeryeong white porcelain using the Hoeryeong glaze comprises the following steps: forming a body in a predetermined shape using white clay as base clay, and firstly firing the formed body in a Korean traditional firewood kiln at a temperature of 800-900 deg. C; depositing first sediment after mixing water and ash obtained by burning a raw material which contains a great quantity of siliceous ingredients and is selected from a group consisting of bean pods, straw, bamboo, thatch, and chaff, depositing second sediment after mixing water and feldspar-containing soil or powdered feldspar, depositing third sediment after mixing water and ash obtained by burning pine, and mixing 30-45 wt% of the first sediment, 25-35 wt% of the second sediment, and 25-40 wt% of the third sediment to manufacture Hoeryeong glaze separately from the step of firstly firing the white clay body; soaking the firstly fired white clay body in the Hoeryeong glaze to apply the Hoeryeong glaze to the firstly fired white clay body; and secondly firing the white clay body coated with the Hoeryeong glaze in a Korean traditional firewood kiln at a temperature of 1,300 deg. C or higher for at least two hours.
자기(瓷器)의 색감을 고급스럽게 하고, 도포 후 균열이 발생하지 않는 회령 유약을 사용함으로써, 백자의 청결함 및 고급스러움을 유지할 수 있는 회령 유약 및 이를 이용한 회유백자의 제조방법이 개시된다. 상기 회령 유약을 이용한 회유백자의 제조방법은, 태토인 백자토를 이용하여 일정한 형상으로 성형한 소지를 800 내지 900 ℃ 온도의 전통장작가마에서 초벌구이 하는 단계; 상기 백자토 소지를 초벌구이 하는 것과는 별개로, 30 내지 45 중량%의 규산질 성분이 다량 함유되어 있는 콩깍지, 지푸라기, 대나무, 억새풀 및 왕겨로 이루어진 군으로부터 선택되는 원료를 태운 재를 물과 혼합시킨 후 침전된 앙금, 25 내지 35 중량%의 장석 성분이 포함된 흙 또는 분말 형태의 장석을 물과 혼합시킨 후 침전된 앙금 및 25 내지 40 중량%의 소나무를 태운 재를 물과 혼합시킨 후 침전된 앙금을 혼합하여 회령 유약을 제조하는 단계; 상기 초벌구이 된 백자토 소지를 상기 유약에 침지시켜, 상기 초벌구이 된 백자토 소지에 유약을 도포하는 단계; 및 상기 유약이 도포된 백자토 소지를 1,300 ℃ 이상의 온도에서 2 시간 이상 동안 전통장작가마에서 환원 소성으로 재벌구이 하는 단계를 포함한다.
Hoeryeong glaze and method for preparing of hoeryeong glaze white porcelain using the same
회령 유약 및 이를 이용한 회유백자의 제조방법
KIM YOUNG SIK (author)
2016-11-09
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
White porcelain glaze and method for preparing ceramic product by using white porcelain glaze
| European Patent Office | 2023
Glaze material for Jun red glaze and process for preparing Jun porcelain from glaze material
| European Patent Office | 2015
| European Patent Office | 2024