Easy sintering yellow alumina containing magnesium oxide and iron oxide and the manufacturing method of the same
The present invention relates to a yellow easy sintering alumina containing magnesium oxide and iron oxide and a method for manufacturing the same and, more particularly, to a method for manufacturing yellow easy sintering alumina containing magnesium oxide and iron oxide including: a step of producing a mixture by mixing alumina powder, magnesium salt, and iron oxide powder in a wet process; a step of calcining the mixture; a step of grinding the calcined mixture in a wet process; a step of forming the ground mixture; and a step of sintering the formed mixture. The magnesium salt is put in for 0.01 to 0.1 wt% of magnesium oxide and the amount of the iron oxide added is at least 0.3 wt% and less than 2 wt% with respect to 100 wt% of the alumina powder. According to the present invention, the diversity of the yellow color of the alumina is enriched, inter-color concentration adjustment is facilitated, and the probability of commercial use of the alumina as a dental material is increased.
본 발명은 산화마그네슘과 산화철을 함유한 노랑계열 색상의 이소결성 알루미나 및 그 제조방법에 관한 것으로서, 보다 상세하게는 알루미나 분말과 마그네슘 염과 산화철 분말을 습식공정으로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 하소하는 단계; 상기 하소된 혼합물을 습식공정으로 분쇄하는 단계; 상기 분쇄된 혼합물을 성형하는 단계; 및 상기 성형된 혼합물을 소결하는 단계;를 포함하여 구성되며, 상기 알루미나 분말을 100중량퍼센트로 하였을 때, 마그네슘 염을 산화 마그네슘 0.01 ~ 0.1 중량퍼센트가 되도록 투입하며, 산화철 0.3 이상 2 미만의 중량퍼센트를 첨가하는 것을 특징으로 하는 산화마그네슘과 산화철을 함유한 노랑계열 색상의 이소결성 알루미나의 제조방법을 제공한다. 이상과 같은 본 발명에 따르면, 알루미나의 노랑계열 색상의 다양성을 풍부히하고 색상간 농도 조절을 용이하게 하여 치과 재료로서의 알루미나의 상용화 가능성을 높이도록 하는 작용효과가 기대된다.
Easy sintering yellow alumina containing magnesium oxide and iron oxide and the manufacturing method of the same
The present invention relates to a yellow easy sintering alumina containing magnesium oxide and iron oxide and a method for manufacturing the same and, more particularly, to a method for manufacturing yellow easy sintering alumina containing magnesium oxide and iron oxide including: a step of producing a mixture by mixing alumina powder, magnesium salt, and iron oxide powder in a wet process; a step of calcining the mixture; a step of grinding the calcined mixture in a wet process; a step of forming the ground mixture; and a step of sintering the formed mixture. The magnesium salt is put in for 0.01 to 0.1 wt% of magnesium oxide and the amount of the iron oxide added is at least 0.3 wt% and less than 2 wt% with respect to 100 wt% of the alumina powder. According to the present invention, the diversity of the yellow color of the alumina is enriched, inter-color concentration adjustment is facilitated, and the probability of commercial use of the alumina as a dental material is increased.
본 발명은 산화마그네슘과 산화철을 함유한 노랑계열 색상의 이소결성 알루미나 및 그 제조방법에 관한 것으로서, 보다 상세하게는 알루미나 분말과 마그네슘 염과 산화철 분말을 습식공정으로 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 하소하는 단계; 상기 하소된 혼합물을 습식공정으로 분쇄하는 단계; 상기 분쇄된 혼합물을 성형하는 단계; 및 상기 성형된 혼합물을 소결하는 단계;를 포함하여 구성되며, 상기 알루미나 분말을 100중량퍼센트로 하였을 때, 마그네슘 염을 산화 마그네슘 0.01 ~ 0.1 중량퍼센트가 되도록 투입하며, 산화철 0.3 이상 2 미만의 중량퍼센트를 첨가하는 것을 특징으로 하는 산화마그네슘과 산화철을 함유한 노랑계열 색상의 이소결성 알루미나의 제조방법을 제공한다. 이상과 같은 본 발명에 따르면, 알루미나의 노랑계열 색상의 다양성을 풍부히하고 색상간 농도 조절을 용이하게 하여 치과 재료로서의 알루미나의 상용화 가능성을 높이도록 하는 작용효과가 기대된다.
Easy sintering yellow alumina containing magnesium oxide and iron oxide and the manufacturing method of the same
산화마그네슘과 산화철을 함유한 노랑계열 색상의 이소결성 알루미나 및 그 제조방법
HWANG JONG HEE (author) / LIM TEA YOUNG (author) / LEE MI JAE (author) / KIM JIN HO (author) / JEAN DAE WOO (author) / AHN YOUNG KWAN (author) / CHOI GWANG PYO (author) / SEONG KYUNG PIL (author) / PARK SUNG HYUN (author) / LEE SUNG OH (author)
2017-01-25
Patent
Electronic Resource
Korean
European Patent Office | 2017