MgAl2O4 Spinel Forming Method of MgAl2O4 Spinel
The present invention provides a method for producing a MgAl_2O_4 spinel molded body, comprising the steps of: adding a monomer based organic material besides dispersant in a procedure of dispersing MgAl_2O_4 nanoparticles to make stable slurry without condensation and sedimentation of particles in accordance with hydration of the MgAl_2O_4 particles; and molding the solution using complex technology of filter pressing and gel casting, which is a unique molding scheme, thereby providing a very uniform molded body having no locally irregular distribution of pores which is inevitable in obtaining transparent MgAl_2O_4 ceramic. The present invention enables the added monomer to be absorbed on surfaces of the nanoparticles and to play a role of disturbing particle sedimentation and increases stability of the MgAl_2O_4 slurry together with the dispersant giving electrostatic repulsion force. The increased stability of the slurry and the combination of the filter pressing and the gel casting molding method makes it possible to produce the very regular MgAl_2O_4 molded body inevitable in producing the ceramic.
본 발명은 MgAl2O4 나노분체의 분산 단계에서 분산제 외에 모노머 류의 유기물을 추가로 첨가하여 MgAl2O4 입자의 수화에 따른 입자들의 응집 및 침강이 거의 없는 안정한 슬러리을 만들고, 이 용액을 본 발명의 독특한 성형법인의 복합기술로 성형하여, 투명한 MgAl2O4 세라믹을 얻는데 필수적인 국부적으로 기공들의 불균일 분포가 없는 매우 균일한 성형체를 제공하는 것을 요지로 한다. 본 발명에서 첨가하는 모노머는 나노입자 표면에 흡착하여 기하학적으로 입자 침강을 방해하는 역할을 하며, 정전기적 반발력을 부여하는 분산제와 더불어 MgAl2O4 슬러리의 안정성을 배가시킨다. 이러한 슬러리의 배가된 안정성과성형법의 조합은 투명 세라믹 제조에 필수적인 매우 균일한 MgAl2O4 성형체 제작을 가능하게 한다.
MgAl2O4 Spinel Forming Method of MgAl2O4 Spinel
The present invention provides a method for producing a MgAl_2O_4 spinel molded body, comprising the steps of: adding a monomer based organic material besides dispersant in a procedure of dispersing MgAl_2O_4 nanoparticles to make stable slurry without condensation and sedimentation of particles in accordance with hydration of the MgAl_2O_4 particles; and molding the solution using complex technology of filter pressing and gel casting, which is a unique molding scheme, thereby providing a very uniform molded body having no locally irregular distribution of pores which is inevitable in obtaining transparent MgAl_2O_4 ceramic. The present invention enables the added monomer to be absorbed on surfaces of the nanoparticles and to play a role of disturbing particle sedimentation and increases stability of the MgAl_2O_4 slurry together with the dispersant giving electrostatic repulsion force. The increased stability of the slurry and the combination of the filter pressing and the gel casting molding method makes it possible to produce the very regular MgAl_2O_4 molded body inevitable in producing the ceramic.
본 발명은 MgAl2O4 나노분체의 분산 단계에서 분산제 외에 모노머 류의 유기물을 추가로 첨가하여 MgAl2O4 입자의 수화에 따른 입자들의 응집 및 침강이 거의 없는 안정한 슬러리을 만들고, 이 용액을 본 발명의 독특한 성형법인의 복합기술로 성형하여, 투명한 MgAl2O4 세라믹을 얻는데 필수적인 국부적으로 기공들의 불균일 분포가 없는 매우 균일한 성형체를 제공하는 것을 요지로 한다. 본 발명에서 첨가하는 모노머는 나노입자 표면에 흡착하여 기하학적으로 입자 침강을 방해하는 역할을 하며, 정전기적 반발력을 부여하는 분산제와 더불어 MgAl2O4 슬러리의 안정성을 배가시킨다. 이러한 슬러리의 배가된 안정성과성형법의 조합은 투명 세라믹 제조에 필수적인 매우 균일한 MgAl2O4 성형체 제작을 가능하게 한다.
MgAl2O4 Spinel Forming Method of MgAl2O4 Spinel
MgAl2O4 Spinel 성형체의 제조방법
JANG CHEOL WOO (author) / HAM SUNG WON (author)
2017-05-26
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Crack-healing in spinel (MgAl2O4) ceramic
| British Library Online Contents | 2015
Construction of hierarchical MgAl2O4 spinel as catalytic supports
| British Library Online Contents | 2015
Container coated with MgAl2O4 spinel coating and corundum
| European Patent Office | 2024
CONTAINER COATED WITH A MGAL2O4 SPINEL AND CORUNDUM COATING
| European Patent Office | 2025