A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH CEMENT AND A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH MORTAR CONTAINING THE SAME
The present invention relates to an ultra-rapid hardening quicklime and an ultra-rapid hardening quicklime mortar containing the same. The ultra-rapid hardening quicklime according to the present invention is manufactured by mixing an additive and cement. The cement used in the present invention is furnace slag cement and the additive contains gypsum, activated carbon, phosphate, calcium silicate, kaolin, and waste wood powder. A total weight of the additive contains 10-20 parts by weight of the gypsum, 30-40 parts by weight of the activated carbon, 5-10 parts by weight of the phosphate, 5-15 parts by weight of the calcium silicate with respect to 100 parts by weight of the total phosphate, 5-15 parts by weight of the kaolin, and 3-10 parts by weight of the waste wood powder, which are mixed at the above weight ratio. According to the above configuration of the present invention, cement with a contraction reduction function is manufactured by mixing the additive, and thus a setting can be accelerated since moisture is quickly evaporated during setting in the early stage of curing. Moreover, during drying following the setting, drying is delayed by continuous moisture supply, thereby preventing cracks. Finally, required intensity can be obtained for a short-time of period, thereby improving physical characteristics and durability relating to intensity, repairing a damage portion of cultural assets, and easily restoring the cultural assets in their original shapes.
본 발명은 초속경 강회 및 이를 포함하는 초속경 강회 몰탈에 관한 것이다. 본 발명에 따른 초속경 강회는 첨가제와 시멘트를 혼합하여 제조되되, 상기 시멘트는 고로슬래그 시멘트가 사용되고, 상기 첨가제는 석고, 활성탄, 인산염, 규산칼슘, 고령토 및 폐목분을 포함하고, 상기 첨가제 전체 함량 중에서 상기 석고는 10 내지 20 중량부, 상기 활성탄은 30 내지 40 중량부, 상기 인산염은 5 내지 10 중량부, 상기 규산칼슘은 인산염 전체 100 중량부에 대하여 5 내지 15 중량부, 상기 고령토는 5 내지 15 중량부, 상기 폐목분은 3 내지 10 중량부의 중량비율로 혼합된다. 상기한 구성에 의해 본 발명은 첨가제를 혼합하여 수축 절감 성능을 가지는 시멘트를 제조함으로써, 양생 초기 응결시 수분이 급격하게 증발되어 응결속도를 단축할 수 있으며, 응결 후 건조시에는 지속적인 수분 공급에 의해 건조시간을 지연시켜 급격한 건조에 의한 균열을 방지할 수 있고, 단시간에 소요 강도를 얻을 수 있어 강도와 관련한 물리적인 특성과 내구성이 우수하고 문화재의 손상된 부분을 보수하거나 문화재를 원래의 원형대로 용이하게 복원할 수 있다.
A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH CEMENT AND A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH MORTAR CONTAINING THE SAME
The present invention relates to an ultra-rapid hardening quicklime and an ultra-rapid hardening quicklime mortar containing the same. The ultra-rapid hardening quicklime according to the present invention is manufactured by mixing an additive and cement. The cement used in the present invention is furnace slag cement and the additive contains gypsum, activated carbon, phosphate, calcium silicate, kaolin, and waste wood powder. A total weight of the additive contains 10-20 parts by weight of the gypsum, 30-40 parts by weight of the activated carbon, 5-10 parts by weight of the phosphate, 5-15 parts by weight of the calcium silicate with respect to 100 parts by weight of the total phosphate, 5-15 parts by weight of the kaolin, and 3-10 parts by weight of the waste wood powder, which are mixed at the above weight ratio. According to the above configuration of the present invention, cement with a contraction reduction function is manufactured by mixing the additive, and thus a setting can be accelerated since moisture is quickly evaporated during setting in the early stage of curing. Moreover, during drying following the setting, drying is delayed by continuous moisture supply, thereby preventing cracks. Finally, required intensity can be obtained for a short-time of period, thereby improving physical characteristics and durability relating to intensity, repairing a damage portion of cultural assets, and easily restoring the cultural assets in their original shapes.
본 발명은 초속경 강회 및 이를 포함하는 초속경 강회 몰탈에 관한 것이다. 본 발명에 따른 초속경 강회는 첨가제와 시멘트를 혼합하여 제조되되, 상기 시멘트는 고로슬래그 시멘트가 사용되고, 상기 첨가제는 석고, 활성탄, 인산염, 규산칼슘, 고령토 및 폐목분을 포함하고, 상기 첨가제 전체 함량 중에서 상기 석고는 10 내지 20 중량부, 상기 활성탄은 30 내지 40 중량부, 상기 인산염은 5 내지 10 중량부, 상기 규산칼슘은 인산염 전체 100 중량부에 대하여 5 내지 15 중량부, 상기 고령토는 5 내지 15 중량부, 상기 폐목분은 3 내지 10 중량부의 중량비율로 혼합된다. 상기한 구성에 의해 본 발명은 첨가제를 혼합하여 수축 절감 성능을 가지는 시멘트를 제조함으로써, 양생 초기 응결시 수분이 급격하게 증발되어 응결속도를 단축할 수 있으며, 응결 후 건조시에는 지속적인 수분 공급에 의해 건조시간을 지연시켜 급격한 건조에 의한 균열을 방지할 수 있고, 단시간에 소요 강도를 얻을 수 있어 강도와 관련한 물리적인 특성과 내구성이 우수하고 문화재의 손상된 부분을 보수하거나 문화재를 원래의 원형대로 용이하게 복원할 수 있다.
A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH CEMENT AND A ENVIRONMENTAL-FRINDLY ULTRA SUPER EARLY STRENGTH MORTAR CONTAINING THE SAME
초속경 강회 및 이를 포함하는 초속경 강회 몰탈
YANG HAI DONG (author)
2017-08-24
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
European Patent Office | 2017
| European Patent Office | 2023
Ultra early strength binder and Ultra early strength concrete using the same
| European Patent Office | 2019
Super early strength accelerator for portland cement concrete
| European Patent Office | 2015