MANUFACTURING METHOD OF LIGHT WEIGHT GEOPOLYMER BY USING SLAG FROM WASTE SPENT CATALYST AND SILICON SLUDGE
The present invention relates to a method for manufacturing an environmentally friendly inorganic lightweight bubble geopolymer for replacing lightweight bubble concrete using existing cement and, more specifically, to a method for manufacturing an economical lightweight bubble geopolymer without generating a large amount of CO_2 by using only 100% of waste catalyst slag, which is waste generated in industries, without using conventional blast furnace slag or metakaolin-based products, and also using silicon sludge generated from a semiconductor wafer process as a foaming agent for lightening. The present invention provides a method for manufacturing a lightweight bubble geopolymer comprising a step of mixing, hardening, and curing waste catalyst slag including silica (SiO_2), alumina (Al_2O_3), and a calcia (CaO), silicon sludge, and an alkaline activator solution, wherein the mixed alkaline activator solution has a concentration of 5-15 M and a content ratio of water to the total weight of the waste catalyst slag and the silicon sludge is 0.20 to 0.32.
기존의 시멘트를 이용한 경량 기포 콘크리트를 대체하기 위한 친환경 무기계 경량 기포 지오폴리머의 제조에 관한 것으로서 기존의 고로슬래그나 메타카올린과 제품을 사용하지 않고 산업체에서 발생되는 폐기물인 폐촉매 슬래그만을 100% 사용하고 경량화를 위한 발포제 역시 반도체 웨이퍼 공정에서 발생되는 실리콘 슬러지를 사용함으로써, 대량의 CO가 발생하지 않고 경제적인 경량 기포 지오폴리머를 제조할 수 있는 방법이 개시된다. 본 발명은 실리카(SiO), 알루미나(AlO) 및 칼시아(CaO)를 포함하는 폐촉매 슬래그, 실리콘 슬러지 및 알칼리 활성화제 용액을 혼합, 경화 및 양생하는 단계를 포함하여 경량 기포 지오폴리머를 제조하는 방법으로, 상기 혼합되는 알칼리 활성화제 용액은, 농도가 5~15M이고, 상기 폐촉매 슬래그 및 상기 실리콘 슬러지 총 중량에 대한 물 함량비가 0.20~0.32인 것을 특징으로 하는 경량 기포 지오폴리머 제조방법을 제공한다.
MANUFACTURING METHOD OF LIGHT WEIGHT GEOPOLYMER BY USING SLAG FROM WASTE SPENT CATALYST AND SILICON SLUDGE
The present invention relates to a method for manufacturing an environmentally friendly inorganic lightweight bubble geopolymer for replacing lightweight bubble concrete using existing cement and, more specifically, to a method for manufacturing an economical lightweight bubble geopolymer without generating a large amount of CO_2 by using only 100% of waste catalyst slag, which is waste generated in industries, without using conventional blast furnace slag or metakaolin-based products, and also using silicon sludge generated from a semiconductor wafer process as a foaming agent for lightening. The present invention provides a method for manufacturing a lightweight bubble geopolymer comprising a step of mixing, hardening, and curing waste catalyst slag including silica (SiO_2), alumina (Al_2O_3), and a calcia (CaO), silicon sludge, and an alkaline activator solution, wherein the mixed alkaline activator solution has a concentration of 5-15 M and a content ratio of water to the total weight of the waste catalyst slag and the silicon sludge is 0.20 to 0.32.
기존의 시멘트를 이용한 경량 기포 콘크리트를 대체하기 위한 친환경 무기계 경량 기포 지오폴리머의 제조에 관한 것으로서 기존의 고로슬래그나 메타카올린과 제품을 사용하지 않고 산업체에서 발생되는 폐기물인 폐촉매 슬래그만을 100% 사용하고 경량화를 위한 발포제 역시 반도체 웨이퍼 공정에서 발생되는 실리콘 슬러지를 사용함으로써, 대량의 CO가 발생하지 않고 경제적인 경량 기포 지오폴리머를 제조할 수 있는 방법이 개시된다. 본 발명은 실리카(SiO), 알루미나(AlO) 및 칼시아(CaO)를 포함하는 폐촉매 슬래그, 실리콘 슬러지 및 알칼리 활성화제 용액을 혼합, 경화 및 양생하는 단계를 포함하여 경량 기포 지오폴리머를 제조하는 방법으로, 상기 혼합되는 알칼리 활성화제 용액은, 농도가 5~15M이고, 상기 폐촉매 슬래그 및 상기 실리콘 슬러지 총 중량에 대한 물 함량비가 0.20~0.32인 것을 특징으로 하는 경량 기포 지오폴리머 제조방법을 제공한다.
MANUFACTURING METHOD OF LIGHT WEIGHT GEOPOLYMER BY USING SLAG FROM WASTE SPENT CATALYST AND SILICON SLUDGE
폐촉매 슬래그와 실리콘 슬러지를 이용한 경량 기포 지오폴리머 제조방법
KIM YOO TAEK (author) / LEE KI GANG (author) / KANG SEUNG GU (author) / KIM KANG DUK (author) / LEE YU NA (author)
2017-09-20
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
European Patent Office | 2018
MANUFACTURING METHOD OF GEOPOLYMER HAVING HIGH STRENGTH BY USING SLAG FROM WASTE SPENT CATALYST
| European Patent Office | 2015
MANUFACTURING METHOD OF GEOPOLYMER HAVING HIGH STRENGTH BY USING SLAG FROM WASTE SPENT CATALYST
European Patent Office | 2016
| European Patent Office | 2016