The Bottom Gas Bubbling MgO Refractory composition to Relieve Thermal Stress and the product manufacturing Method
Provided are a bottom-blown magnesia carbon refractory composition for relieving thermal stress and a method for manufacturing the same. A composition for a bottom-blown magnesia carbon refractory of the present invention comprises: a main raw material including 75-85 wt% of an electro-melting magnesia clinker and 15-25 wt% of flaky graphite. The composition for a bottom-blown magnesia carbon refractory further comprises: 0.5-3.0 parts by weight of a coal-based pitch; 0.5-5.0 parts by weight of a novolac-based phenol powder binder; 0.5-5.0 parts by weight of a Frit having a melting temperature of 750-950°C; and 1.0-5.0 parts by weight of aluminum powder, based on 100 parts by weight of the main raw material, wherein the electro-melting magnesia clinker comprises 10-25 wt% of an electro-melting magnesia clinker having a particle size of 3-5 mm, and 25-35 wt% of an electro-melting magnesia clinker having a particle size less than or equal to 1 mm.
열응력 해소를 위한 저취 마그네시아 카본질 내화물 조성물 및 그 제조 방법이 제공된다. 본 발명의 저취 마그네시아 카본질 내화물용 조성물은, 중량%로, 전융 마그네시아 클린커 75~85%와 인상 흑연 15~25 중량%를 포함하여 조성되는 주원료와, 상기 주원료 100중량부에 대하여, 석탄계 피치 0.5~3.0 중량부; 노블락계 페놀 분말 바인더 0.5~5.0 중량부; 750~950℃의 용융온도를 가지는 Frit 0.5~5.0 중량부; 및 알루미늄 분말 1.0~5.0 중량부를 첨가하여 이루어지고, 상기 전융 마그네시아 클린커는 그 자체 중량%로, 입도가 3~5mm인 전융 마그네시아 클린커 10~25%와 입도가 1mm 이하인 전융 마그네시아 클린커 25~35%를 포함하여 조성됨을 특징으로 한다.
The Bottom Gas Bubbling MgO Refractory composition to Relieve Thermal Stress and the product manufacturing Method
Provided are a bottom-blown magnesia carbon refractory composition for relieving thermal stress and a method for manufacturing the same. A composition for a bottom-blown magnesia carbon refractory of the present invention comprises: a main raw material including 75-85 wt% of an electro-melting magnesia clinker and 15-25 wt% of flaky graphite. The composition for a bottom-blown magnesia carbon refractory further comprises: 0.5-3.0 parts by weight of a coal-based pitch; 0.5-5.0 parts by weight of a novolac-based phenol powder binder; 0.5-5.0 parts by weight of a Frit having a melting temperature of 750-950°C; and 1.0-5.0 parts by weight of aluminum powder, based on 100 parts by weight of the main raw material, wherein the electro-melting magnesia clinker comprises 10-25 wt% of an electro-melting magnesia clinker having a particle size of 3-5 mm, and 25-35 wt% of an electro-melting magnesia clinker having a particle size less than or equal to 1 mm.
열응력 해소를 위한 저취 마그네시아 카본질 내화물 조성물 및 그 제조 방법이 제공된다. 본 발명의 저취 마그네시아 카본질 내화물용 조성물은, 중량%로, 전융 마그네시아 클린커 75~85%와 인상 흑연 15~25 중량%를 포함하여 조성되는 주원료와, 상기 주원료 100중량부에 대하여, 석탄계 피치 0.5~3.0 중량부; 노블락계 페놀 분말 바인더 0.5~5.0 중량부; 750~950℃의 용융온도를 가지는 Frit 0.5~5.0 중량부; 및 알루미늄 분말 1.0~5.0 중량부를 첨가하여 이루어지고, 상기 전융 마그네시아 클린커는 그 자체 중량%로, 입도가 3~5mm인 전융 마그네시아 클린커 10~25%와 입도가 1mm 이하인 전융 마그네시아 클린커 25~35%를 포함하여 조성됨을 특징으로 한다.
The Bottom Gas Bubbling MgO Refractory composition to Relieve Thermal Stress and the product manufacturing Method
열응력 해소를 위한 저취 마그네시아 카본질 내화물 조성물 및 내화물 제조 방법
HEO JOON (author) / BAE IN KYUNG (author) / KIM BONG JIK (author)
2020-03-10
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
European Patent Office | 2020
Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
| European Patent Office | 2019
Thermal Shock Resistant Composition for Bottom Gas Bubbling Refractory
European Patent Office | 2019
Measures to Relieve the Stress of Water
| British Library Conference Proceedings | 2013