Manufacturing method of the aluminum titanate ceramics
The present invention relates to a method for manufacturing aluminum titanate (Al_2TiO_5) ceramics, which comprises the following steps of: mixing a mixed powder, which includes 50 to 55 parts by weight of Al_2O_3 powder, 40 to 45 parts by weight of TiO_2 powder, 3 to 5 parts by weight of SiO_2 powder, and 1 to 5 parts by weight of Fe_2O_3 powder, and ZrO_2 powder by a ratio of 92 : 8; wet kneading the mixture mixed in the previous step in a kneader to form wet slurry; drying the wet slurry acquired in the previous step to acquire dry powder; molding the dry powder acquired in the previous step in a predetermined shape; and sintering the molded material molded in the previous step. According to the present invention, a process is simplified through improvement of a manufacturing process, thereby reducing manufacturing costs and providing aluminum titanate (Al_2TiO_5) ceramics with remarkably increased thermal and mechanical stability through a proper blend of SiO_2 and ZrO_2.
본 발명은 알루미늄 티타네이트(AlTiO) 세라믹스 제조방법에 관한 것으로서, AlO분말 50 내지 55 중량부와 TiO분말 40 내지 45 중량부에 SiO분말 3 내지 5중량부 및 FeO분말 1 내지 5중량부가 첨가된 혼합분말과 ZrO분말을 92:8의 비율로 혼합하는 단계 및 상기 단계에서 혼합된 혼합물을 혼련기에서 습식 혼련하여 습식 슬러리를 형성하는 단계 및 상기 단계에서 수득한 습식 슬러리를 건조시켜 건조분말을 수득하는 단계 및 상기 단계에서 수득한 건조분말을 일정한 형상으로 성형하는 단계 및 상기 단계에서 성형된 성형물을 소성하는 단계를 포함하여 이루어진다. 상기와 같은 본 발명에 의하면, 제조공정의 개선을 통해 공정이 단순화됨에 따라 제조원가가 절감됨과 아울러, SiO및 ZrO의 적정 배합을 통해 열적ㆍ기계적 안정성이 현저하게 향상된 알루미늄 티타네이트(AlTiO) 세라믹스를 제공할 수 있게 된다.
Manufacturing method of the aluminum titanate ceramics
The present invention relates to a method for manufacturing aluminum titanate (Al_2TiO_5) ceramics, which comprises the following steps of: mixing a mixed powder, which includes 50 to 55 parts by weight of Al_2O_3 powder, 40 to 45 parts by weight of TiO_2 powder, 3 to 5 parts by weight of SiO_2 powder, and 1 to 5 parts by weight of Fe_2O_3 powder, and ZrO_2 powder by a ratio of 92 : 8; wet kneading the mixture mixed in the previous step in a kneader to form wet slurry; drying the wet slurry acquired in the previous step to acquire dry powder; molding the dry powder acquired in the previous step in a predetermined shape; and sintering the molded material molded in the previous step. According to the present invention, a process is simplified through improvement of a manufacturing process, thereby reducing manufacturing costs and providing aluminum titanate (Al_2TiO_5) ceramics with remarkably increased thermal and mechanical stability through a proper blend of SiO_2 and ZrO_2.
본 발명은 알루미늄 티타네이트(AlTiO) 세라믹스 제조방법에 관한 것으로서, AlO분말 50 내지 55 중량부와 TiO분말 40 내지 45 중량부에 SiO분말 3 내지 5중량부 및 FeO분말 1 내지 5중량부가 첨가된 혼합분말과 ZrO분말을 92:8의 비율로 혼합하는 단계 및 상기 단계에서 혼합된 혼합물을 혼련기에서 습식 혼련하여 습식 슬러리를 형성하는 단계 및 상기 단계에서 수득한 습식 슬러리를 건조시켜 건조분말을 수득하는 단계 및 상기 단계에서 수득한 건조분말을 일정한 형상으로 성형하는 단계 및 상기 단계에서 성형된 성형물을 소성하는 단계를 포함하여 이루어진다. 상기와 같은 본 발명에 의하면, 제조공정의 개선을 통해 공정이 단순화됨에 따라 제조원가가 절감됨과 아울러, SiO및 ZrO의 적정 배합을 통해 열적ㆍ기계적 안정성이 현저하게 향상된 알루미늄 티타네이트(AlTiO) 세라믹스를 제공할 수 있게 된다.
Manufacturing method of the aluminum titanate ceramics
알루미늄 티타네이트 세라믹스 제조방법
CHA TAE MIN (author)
2020-07-02
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Low thermal expansion aluminum titanate-zirconium tin titanate ceramics
| European Patent Office | 2017
LOW THERMAL EXPANSION ALUMINUM TITANATE -ZIRCONIUM TIN TITANATE CERAMICS
| European Patent Office | 2016
LOW THERMAL EXPANSION ALUMINUM TITANATE - ZIRCONIUM TIN TITANATE CERAMICS
| European Patent Office | 2016
Low thermal expansion aluminum titanate zirconium tin titanate ceramics
| European Patent Office | 2016