Black Alumina Sintered Body And Manufacturing Method Thereof
The present invention relates to black alumina that can replace Japanese alumina raw materials and black alumina which have high unit prices due to Japan's export regulations and instead uses domestic alumina raw materials for preparing same or better black alumina, so that the black alumina can replace conventional Japanese alumina raw materials or black alumina. In a method for preparing black alumina according to the present invention, a ratio of alumina to additives and sintering temperature for densification are established to ensure black color and low reflectivity while maintaining the excellent mechanical properties of conventional alumina. According to the present invention, liquid sintering occurs due to additives during a sintering process. Accordingly, the material can be densified at a temperature lower than 1600 ℃ or the alumina sintering temperature for conventional solid-state sintering, thereby bringing economic advantages and black color and low reflectivity are ensured to allow the black alumina to be used in a photo process.
본 발명의 블랙 알루미나는 일본의 수출규제로 인한 높은 단가를 가지는 일본산 알루미나 원료 및 블랙 알루미나를 대체하여 국내산 알루미나 원료를 사용하여 동일하거나 더 우수한 블랙 알루미나를 제조하였으므로 종래의 일본산 알루미나 원료 또는 블랙 알루미나를 대체할 수 있는 효과가 있다. 본 발명의 블랙알루미나 제조방법은 종래의 알루미나가 가지는 우수한 기계적 특성을 유지하면서도 블랙색상을 가져 낮은 반사율을 가질 수 있도록 알루미나와 첨가제 간의 비율 및 치밀화를 위한 소결온도 확립한 것이다. 본 발명은 소결과정 중 첨가제로 인하여 액상소결이 진행된다. 따라서 종래의 고상소결에 의한 알루미나 소결온도인 1600℃보다 낮은 온도에서 소재의 치밀화가 가능하므로 경제적인 이점을 있을 뿐 아니라 블랙색상의 낮은 반사율을 보여 포토(Photo) 공정에 사용 가능한 장점이 있다.
Black Alumina Sintered Body And Manufacturing Method Thereof
The present invention relates to black alumina that can replace Japanese alumina raw materials and black alumina which have high unit prices due to Japan's export regulations and instead uses domestic alumina raw materials for preparing same or better black alumina, so that the black alumina can replace conventional Japanese alumina raw materials or black alumina. In a method for preparing black alumina according to the present invention, a ratio of alumina to additives and sintering temperature for densification are established to ensure black color and low reflectivity while maintaining the excellent mechanical properties of conventional alumina. According to the present invention, liquid sintering occurs due to additives during a sintering process. Accordingly, the material can be densified at a temperature lower than 1600 ℃ or the alumina sintering temperature for conventional solid-state sintering, thereby bringing economic advantages and black color and low reflectivity are ensured to allow the black alumina to be used in a photo process.
본 발명의 블랙 알루미나는 일본의 수출규제로 인한 높은 단가를 가지는 일본산 알루미나 원료 및 블랙 알루미나를 대체하여 국내산 알루미나 원료를 사용하여 동일하거나 더 우수한 블랙 알루미나를 제조하였으므로 종래의 일본산 알루미나 원료 또는 블랙 알루미나를 대체할 수 있는 효과가 있다. 본 발명의 블랙알루미나 제조방법은 종래의 알루미나가 가지는 우수한 기계적 특성을 유지하면서도 블랙색상을 가져 낮은 반사율을 가질 수 있도록 알루미나와 첨가제 간의 비율 및 치밀화를 위한 소결온도 확립한 것이다. 본 발명은 소결과정 중 첨가제로 인하여 액상소결이 진행된다. 따라서 종래의 고상소결에 의한 알루미나 소결온도인 1600℃보다 낮은 온도에서 소재의 치밀화가 가능하므로 경제적인 이점을 있을 뿐 아니라 블랙색상의 낮은 반사율을 보여 포토(Photo) 공정에 사용 가능한 장점이 있다.
Black Alumina Sintered Body And Manufacturing Method Thereof
블랙 알루미나 소결체 및 이의 제조방법
LEE SANG JIN (author) / KONG HEON (author) / OH BOK HYUN (author) / PARK SANG JIN (author) / AHN YOO KYOUNG (author) / LEE JONG KEUN (author)
2023-06-01
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Black Alumina Sintered Body And Manufacturing Method Thereof
European Patent Office | 2024
Method for manufacturing alumina sintered body and alumina sintered body
| European Patent Office | 2017
METHOD FOR MANUFACTURING ALUMINA SINTERED BODY AND ALUMINA SINTERED BODY
| European Patent Office | 2016
METHOD FOR MANUFACTURING ALUMINA SINTERED BODY AND ALUMINA SINTERED BODY
| European Patent Office | 2016