CERAMIC MIXTURE FOR MAKING FACING TILES
FIELD: ceramic industry.SUBSTANCE: invention relates to compositions of ceramic mixtures, which can primarily be used for production of facing tiles. Ceramic mixture for making facing tiles contains, wt%: kaolin 70.0-73.5; scrap tile 0.1-1.0; Phosphorite 3.0-4.0; feldspar 11.0-13.0; silica sand 11.0-13.0. Components are dosed in required amounts, crushed to powdered state (not more than 2 % of residue on mesh 0056), ceramic mixture with moisture content of 9-13 %, from which facing tiles are formed using semidry method (under pressure 35-40 MPa). Articles are annealed at temperature of 1300-1310 °C.EFFECT: technical result of the invention is improvement in strength of tiles.1 cl, 1 tbl
Изобретение относится к составам керамических масс, которые могут быть использованы преимущественно для изготовления облицовочной плитки. Керамическая масса для изготовления облицовочной плитки включает, мас. %: каолин 70,0-73,5; плиточный бой 0,1-1,0; фосфорит 3,0-4,0; полевой шпат 11,0-13,0; кварцевый песок 11,0-13,0. Компоненты дозируют в требуемых количествах, размалывают до порошкообразного состояния (остаток не более 2% на сите 0056), готовят керамическую массу с влажностью 9-13%, из которой полусухим способом формуют (под давлением 35-40 МПа) облицовочные плитки. Изделия обжигают при температуре 1300-1310°C. Технический результат изобретения - повышение прочности плитки. 1 табл.
CERAMIC MIXTURE FOR MAKING FACING TILES
FIELD: ceramic industry.SUBSTANCE: invention relates to compositions of ceramic mixtures, which can primarily be used for production of facing tiles. Ceramic mixture for making facing tiles contains, wt%: kaolin 70.0-73.5; scrap tile 0.1-1.0; Phosphorite 3.0-4.0; feldspar 11.0-13.0; silica sand 11.0-13.0. Components are dosed in required amounts, crushed to powdered state (not more than 2 % of residue on mesh 0056), ceramic mixture with moisture content of 9-13 %, from which facing tiles are formed using semidry method (under pressure 35-40 MPa). Articles are annealed at temperature of 1300-1310 °C.EFFECT: technical result of the invention is improvement in strength of tiles.1 cl, 1 tbl
Изобретение относится к составам керамических масс, которые могут быть использованы преимущественно для изготовления облицовочной плитки. Керамическая масса для изготовления облицовочной плитки включает, мас. %: каолин 70,0-73,5; плиточный бой 0,1-1,0; фосфорит 3,0-4,0; полевой шпат 11,0-13,0; кварцевый песок 11,0-13,0. Компоненты дозируют в требуемых количествах, размалывают до порошкообразного состояния (остаток не более 2% на сите 0056), готовят керамическую массу с влажностью 9-13%, из которой полусухим способом формуют (под давлением 35-40 МПа) облицовочные плитки. Изделия обжигают при температуре 1300-1310°C. Технический результат изобретения - повышение прочности плитки. 1 табл.
CERAMIC MIXTURE FOR MAKING FACING TILES
КЕРАМИЧЕСКАЯ МАССА ДЛЯ ИЗГОТОВЛЕНИЯ ОБЛИЦОВОЧНОЙ ПЛИТКИ