ZIRCONIUM OXIDE-BASED METHOD FOR PRODUCING POROUS BIOACTIVE CERAMICS
FIELD: medicine.SUBSTANCE: invention relates to medicine, in particular to traumatology, orthopaedics, regenerative medicine, dentistry and maxillofacial surgery, and can be used for recovery of bone tissue structure and function. Zirconium dioxide is mixed with chemically resistant glass of XC-2 №29 mark and magnesium oxide, which is used as a stabilizing component, preventing transition of zirconium dioxide of tetragonal structure in monoclinous one while heating. Then, a mixture of ammonium phosphate twice-substituted (NH)HPOand calcium carbonate CaCOis added. Initial mixture contains the following component ratio, wt.%: 72-73 of ZrO, 4-5 of MgO, 6-8 of (NH)HPO, 7-9 of CaCOand 8-8,5 of XC-2 №29 glass. Mixture is grated on vibrating mill, then 90% of particles have size less than 50 mcm, then it is pressed in mold under pressure of 100 mPas/cmand annealed in a muffle furnace at temperature of 1,300 °C. As a result, zirconium oxide-based porous bioactive ceramics is produced, in which pores is lined inside with a biologically active layer-particles of calcium phosphates with compression strength of not lower than 100 mPas.EFFECT: method provides for simultaneous production of bioinertial matrix with bioactive coating in a single step.1 cl, 7 ex
Изобретение относится к медицине, в частности к травматологии, ортопедии, регенеративной медицине, стоматологии и челюстно-лицевой хирургии, и может быть использовано для восстановления структуры и функции костной ткани. Диоксид циркония смешивают с химически стойким стеклом марки ХС-2 №29 и оксидом магния, который используют в качестве стабилизирующего компонента, препятствующего переходу диоксида циркония из тетрагональной структуры в моноклинную при нагревании. Затем добавляют смесь аммония фосфорнокислого 2-х замещенного (NH)HPOи кальция углекислого CaCO. При этом исходная смесь содержит компоненты в следующем соотношении, мас. %: 72-73 ZrO, 4-5 MgO, 6-8 (NH)HPO, 7-9 CaCOи 8-8,5 стекло марки ХС-2 №29. Смесь истирают на вибромельнице, после чего 90% частиц имеют размер менее 50 мкм, далее прессуют в пресс-форме под давлением 100 МПа/сми прокаливают в муфельной печи при температуре 1300°С. В результате получают пористую биоактивную керамику на основе оксида циркония, в которой поры выстланы изнутри биоактивным слоем - частицами фосфатов кальция с прочностью на сжатие не ниже 100 МПа. Способ обеспечивает одновременное получение биоинертной матрицы с биоактивным покрытием в одну стадию. 7 пр.
ZIRCONIUM OXIDE-BASED METHOD FOR PRODUCING POROUS BIOACTIVE CERAMICS
FIELD: medicine.SUBSTANCE: invention relates to medicine, in particular to traumatology, orthopaedics, regenerative medicine, dentistry and maxillofacial surgery, and can be used for recovery of bone tissue structure and function. Zirconium dioxide is mixed with chemically resistant glass of XC-2 №29 mark and magnesium oxide, which is used as a stabilizing component, preventing transition of zirconium dioxide of tetragonal structure in monoclinous one while heating. Then, a mixture of ammonium phosphate twice-substituted (NH)HPOand calcium carbonate CaCOis added. Initial mixture contains the following component ratio, wt.%: 72-73 of ZrO, 4-5 of MgO, 6-8 of (NH)HPO, 7-9 of CaCOand 8-8,5 of XC-2 №29 glass. Mixture is grated on vibrating mill, then 90% of particles have size less than 50 mcm, then it is pressed in mold under pressure of 100 mPas/cmand annealed in a muffle furnace at temperature of 1,300 °C. As a result, zirconium oxide-based porous bioactive ceramics is produced, in which pores is lined inside with a biologically active layer-particles of calcium phosphates with compression strength of not lower than 100 mPas.EFFECT: method provides for simultaneous production of bioinertial matrix with bioactive coating in a single step.1 cl, 7 ex
Изобретение относится к медицине, в частности к травматологии, ортопедии, регенеративной медицине, стоматологии и челюстно-лицевой хирургии, и может быть использовано для восстановления структуры и функции костной ткани. Диоксид циркония смешивают с химически стойким стеклом марки ХС-2 №29 и оксидом магния, который используют в качестве стабилизирующего компонента, препятствующего переходу диоксида циркония из тетрагональной структуры в моноклинную при нагревании. Затем добавляют смесь аммония фосфорнокислого 2-х замещенного (NH)HPOи кальция углекислого CaCO. При этом исходная смесь содержит компоненты в следующем соотношении, мас. %: 72-73 ZrO, 4-5 MgO, 6-8 (NH)HPO, 7-9 CaCOи 8-8,5 стекло марки ХС-2 №29. Смесь истирают на вибромельнице, после чего 90% частиц имеют размер менее 50 мкм, далее прессуют в пресс-форме под давлением 100 МПа/сми прокаливают в муфельной печи при температуре 1300°С. В результате получают пористую биоактивную керамику на основе оксида циркония, в которой поры выстланы изнутри биоактивным слоем - частицами фосфатов кальция с прочностью на сжатие не ниже 100 МПа. Способ обеспечивает одновременное получение биоинертной матрицы с биоактивным покрытием в одну стадию. 7 пр.
ZIRCONIUM OXIDE-BASED METHOD FOR PRODUCING POROUS BIOACTIVE CERAMICS
СПОСОБ ПОЛУЧЕНИЯ ПОРИСТОЙ БИОАКТИВНОЙ КЕРАМИКИ НА ОСНОВЕ ОКСИДА ЦИРКОНИЯ
MEDKOV MIKHAIL AZAREVICH (author) / GRISHSHENKO DINA NIKOLAEVNA (author)
2016-08-27
Patent
Electronic Resource
Russian
METHOD FOR PRODUCING BIOACTIVE CERAMICS BASED ON ZIRCONIUM DIOXIDE
| European Patent Office | 2022
Zirconium oxide-based porous body and method for producing zirconium oxide-based porous body
| European Patent Office | 2023
METHOD OF PRODUCING BIOCOMPATIBLE POROUS ZIRCONIUM DIOXIDE CERAMICS FOR ENDOPROSTHESIS REPLACEMENT
| European Patent Office | 2021
POROUS CERAMICS AND METHOD FOR PRODUCING POROUS CERAMICS
| European Patent Office | 2022