DRY ADHESIVE CEMENT-BASED MIXTURE
FIELD: construction.SUBSTANCE: invention relates to dry adhesive cement-based mixture used as tile glue to perform facing work of outer fronts and internal walls of buildings with ceramic tiles. Mixture contains Portland cement, quartz sand, a plasticizer, polymer and a mineral additive and additionally contains as mineral additive synthesized aluminosilicates obtained by sedimentation from liquid glass with silica modulus 2.8 introduction of 15 % solution of technical aluminium sulphate Al(SO)with subsequent washing with distilled water of obtained sediment and drying at temperature t = 5±105 °C during 24 hours with subsequent grinding into particles sized 5.208-5.704 µm, as polymer additive-Neolith p 4400, as plasticizer Kratasol LFM in the following proportions, wt%: Portland cement M400 53.07-60.05, silica sand, in fractions, mm: 0.630-0.315 23.54-26.67, 0.315-0.14 5.89-6.67, synthesized aluminosilicates with sizes 5.208-5.704 µm 6.05-15.92, additive Kratasol LFM 0.28-0.79, additive Neolith p 4400 0.28-0.79.EFFECT: technical result is higher adhesion strength and compression strength, reduced slipping down of tiles.1 cl, 7 tbl
Изобретение относится к сухой клеевой смеси на цементной основе, применяемой в качестве плиточного клея для выполнения облицовки наружных фасадов и внутренних стен зданий керамической плиткой. Смесь содержит портландцемент, песок кварцевый, пластификатор, полимерную и минеральную добавку и . дополнительно содержит в качестве минеральной добавки синтезированные алюмосиликаты, полученные осаждением из жидкого стекла с силикатным модулем 2,8 введением 15%-ного раствора технического сульфата алюминия Al(SO)с последующим промыванием дистиллированной водой полученного осадка и его высушиванием при температуре t=105±5°С в течение 24 ч с последующим измельчением до размера частиц 5,208-5,704 мкм, а в качестве полимерной добавки - Neolith Р 4400, в качестве пластификатора Кратасол ПФМ при следующем соотношении компонентов, масс. %: портландцемент М400 53,07-60,05, песок кварцевый, фракций, мм: 0,630-0,315 23,54-26,67, 0,315-0,14 5,89-6,67, синтезированные алюмосиликаты размером 5,208-5,704 мкм 6,05-15,92, добавка Кратасол ПФМ 0,28-0,79, добавка Neolith Р 4400 0,28-0,79. Технический результат - повышение адгезионной прочности и прочности при сжатии, уменьшение сползания плитки. 7 табл.
DRY ADHESIVE CEMENT-BASED MIXTURE
FIELD: construction.SUBSTANCE: invention relates to dry adhesive cement-based mixture used as tile glue to perform facing work of outer fronts and internal walls of buildings with ceramic tiles. Mixture contains Portland cement, quartz sand, a plasticizer, polymer and a mineral additive and additionally contains as mineral additive synthesized aluminosilicates obtained by sedimentation from liquid glass with silica modulus 2.8 introduction of 15 % solution of technical aluminium sulphate Al(SO)with subsequent washing with distilled water of obtained sediment and drying at temperature t = 5±105 °C during 24 hours with subsequent grinding into particles sized 5.208-5.704 µm, as polymer additive-Neolith p 4400, as plasticizer Kratasol LFM in the following proportions, wt%: Portland cement M400 53.07-60.05, silica sand, in fractions, mm: 0.630-0.315 23.54-26.67, 0.315-0.14 5.89-6.67, synthesized aluminosilicates with sizes 5.208-5.704 µm 6.05-15.92, additive Kratasol LFM 0.28-0.79, additive Neolith p 4400 0.28-0.79.EFFECT: technical result is higher adhesion strength and compression strength, reduced slipping down of tiles.1 cl, 7 tbl
Изобретение относится к сухой клеевой смеси на цементной основе, применяемой в качестве плиточного клея для выполнения облицовки наружных фасадов и внутренних стен зданий керамической плиткой. Смесь содержит портландцемент, песок кварцевый, пластификатор, полимерную и минеральную добавку и . дополнительно содержит в качестве минеральной добавки синтезированные алюмосиликаты, полученные осаждением из жидкого стекла с силикатным модулем 2,8 введением 15%-ного раствора технического сульфата алюминия Al(SO)с последующим промыванием дистиллированной водой полученного осадка и его высушиванием при температуре t=105±5°С в течение 24 ч с последующим измельчением до размера частиц 5,208-5,704 мкм, а в качестве полимерной добавки - Neolith Р 4400, в качестве пластификатора Кратасол ПФМ при следующем соотношении компонентов, масс. %: портландцемент М400 53,07-60,05, песок кварцевый, фракций, мм: 0,630-0,315 23,54-26,67, 0,315-0,14 5,89-6,67, синтезированные алюмосиликаты размером 5,208-5,704 мкм 6,05-15,92, добавка Кратасол ПФМ 0,28-0,79, добавка Neolith Р 4400 0,28-0,79. Технический результат - повышение адгезионной прочности и прочности при сжатии, уменьшение сползания плитки. 7 табл.
DRY ADHESIVE CEMENT-BASED MIXTURE
СУХАЯ КЛЕЕВАЯ СМЕСЬ НА ЦЕМЕНТНОЙ ОСНОВЕ