CERAMIC MIXTURE BASED ON CLAY WITH ADDITION OF DEIRONING STATIONS RESIDUE
FIELD: construction.SUBSTANCE: invention relates to production of construction materials and can be used for production of heat-insulation, structural heat insulation and structural ceramic construction articles for residential and civil construction. Ceramic mass is produced of mixture containing clay, sand and additive, besides additive is residue of deironing station containing 68.57 % of iron(III) oxide in ratio of total weight of dry residue, clay is clay of Kyshtyrlin deposit milled to specific surface of 2,000 m/g, sand is finely ground sand with specific surface area of 1,400 m/g, in following ratio of components, wt%: said clay 69.5–94.5, sand 5–25, residue of deironing station 0.5–5.5. Technical result is production of ceramic wall articles with low density (1,100–1,600 kg/m) and high strength (15.7–22.5 MPa).EFFECT: wall ceramic articles with low density and high strength.1 cl, 5 tbl
Изобретение относится к производству строительных материалов и может быть использовано для изготовления теплоизоляционных, конструкционно-теплоизоляционных и конструкционных керамических строительных изделий для жилищного и гражданского строительства. Керамическая масса получена из смеси, включающей глину, песок и добавку, причём в качестве добавки она содержит осадок станции обезжелезивания, содержащий 68,57% оксида железа(III) в долевом соотношении от общей массы сухого осадка, в качестве глины - размолотую до удельной поверхности 2000 м/г глину Кыштырлинского месторождения Тюменской области, а в качестве песка - тонкоизмельченный песок с удельной поверхностью 1400 м/г, при следующем соотношении компонентов, мас.%: указанная глина 69,5-94,5, песок 5-25, осадок станции обезжелезивания 0,5-5,5. Техническим результатом изобретения является получение стеновых керамических изделий с пониженной плотностью (1100-1600 кг/м) и высокой прочностью (15,7-22,5 МПа). 5 табл.
CERAMIC MIXTURE BASED ON CLAY WITH ADDITION OF DEIRONING STATIONS RESIDUE
FIELD: construction.SUBSTANCE: invention relates to production of construction materials and can be used for production of heat-insulation, structural heat insulation and structural ceramic construction articles for residential and civil construction. Ceramic mass is produced of mixture containing clay, sand and additive, besides additive is residue of deironing station containing 68.57 % of iron(III) oxide in ratio of total weight of dry residue, clay is clay of Kyshtyrlin deposit milled to specific surface of 2,000 m/g, sand is finely ground sand with specific surface area of 1,400 m/g, in following ratio of components, wt%: said clay 69.5–94.5, sand 5–25, residue of deironing station 0.5–5.5. Technical result is production of ceramic wall articles with low density (1,100–1,600 kg/m) and high strength (15.7–22.5 MPa).EFFECT: wall ceramic articles with low density and high strength.1 cl, 5 tbl
Изобретение относится к производству строительных материалов и может быть использовано для изготовления теплоизоляционных, конструкционно-теплоизоляционных и конструкционных керамических строительных изделий для жилищного и гражданского строительства. Керамическая масса получена из смеси, включающей глину, песок и добавку, причём в качестве добавки она содержит осадок станции обезжелезивания, содержащий 68,57% оксида железа(III) в долевом соотношении от общей массы сухого осадка, в качестве глины - размолотую до удельной поверхности 2000 м/г глину Кыштырлинского месторождения Тюменской области, а в качестве песка - тонкоизмельченный песок с удельной поверхностью 1400 м/г, при следующем соотношении компонентов, мас.%: указанная глина 69,5-94,5, песок 5-25, осадок станции обезжелезивания 0,5-5,5. Техническим результатом изобретения является получение стеновых керамических изделий с пониженной плотностью (1100-1600 кг/м) и высокой прочностью (15,7-22,5 МПа). 5 табл.
CERAMIC MIXTURE BASED ON CLAY WITH ADDITION OF DEIRONING STATIONS RESIDUE
КЕРАМИЧЕСКАЯ МАССА НА ОСНОВЕ ГЛИНЫ С ДОБАВЛЕНИЕМ ОСАДКА СТАНЦИЙ ОБЕЗЖЕЛЕЗИВАНИЯ
MAKSIMOV LEV IGOREVICH (author) / MAKSIMOVA SVETLANA VALENTINOVNA (author) / PESHEVA ANNA VALENTINOVNA (author) / KUDOMANOV MAKSIM VALEREVICH (author) / RADAEV SERGEJ SERGEEVICH (author)
2017-02-14
Patent
Electronic Resource
Russian
IPC:
C04B
Kalk
,
LIME
Application of ural glauconite for groundwater deironing and demanganation
| Taylor & Francis Verlag | 2021
Defluoridation and deironing of ground water using polystyrene beads
| Online Contents | 2013
Characterization of a Water Clearing Treatment Residue and Its Application as Clay Ceramic Addition
| British Library Online Contents | 2014